The purpose of this paper was to investigate the effect of a high-energy milling (HEM) process on the particle morphology and the correlation between a thermal treatment and tetragonal/monoclinic nanostructured zirconia powders obtained by a precipitation process. To eliminate chloride residue ions from hydrous zirconia, a modified washing method was used. It was found that the used washing method was effective in removing the chloride from the precipitated gel. In order to investigate the effect of a pre-milling process on the particle morphology of the precipitate, dried Zr(OH)4 was milled using a HEM machine with distilled water. The particle size of the Zr(OH)4 powder exposed to HEM reduced to 100~150 nm, whereas that of fresh Zr(OH)4 powder without a pre-milling process had a large and irregular size of 100 nm~1.5 μm. Additionally, modified heat treatment process was proposed to achieve nano-sized zirconia having a pure monoclinic phase. It was evident that two-step calcining process was effective in perfectly eliminating the tetragonal phase, having a small average particle of ~100 nm with good uniformity compared to the sample calcined by a single-step process, showing a large average particle size of ~300 nm with an irregular particle shape and a broad particle size distribution. The modified method is considered to be a promising process for nano-sized zirconia having a fully monoclinic phase.

Processing and properties of high power piezoelectric transformer (PT) fabricated by PIM with nano-sized piezoelectric powders are demonstrated. The high power characteristics of a PMed dome-shaped PT were examined by the lighting test for a 55watt PL lamp. The 55watt PL lamp was successfully driven by the PIMed PT with sustaining efficiency higher than 98%. The transformer with ring/dot area ratio of 2.1 exhibited the maximum properties in terms of output power, efficiency and temperature stability.