In the aerospace field, Carbon/Cork composites have been used for rocket propulsion systems as a light weight structural component with a high bending stiffness and high thermal insulation properties. For the fabrication of a carbon composite with a heat insulation cork part, the bonding properties between them are very important to determine the service life of the Carbon/Cork composite structure. In this study, the changes in the interfacial adhesion and mechanical properties of Carbon/Cork composites under accelerated aging conditions were investigated. The accelerated aging experiments were performed with different temperatures and humidity conditions. The properties of the aged Carbon/Cork composites were evaluated mainly with the interfacial strength. Finally, the lifetime prediction of the Carbon/Cork composites was performed with the long-term property data under accelerated conditions.

보리(Hordeum vulgare)의 유묘이 14 co2 를 10분 및 30분간 처리한 후 잎을 채취하여 아미노산, 당, 인산염 및 유기산과 같은 수용성 대사물질을 분석하였다. 배양기간에 따른 label 정도는 비슷하였으나 종류와 양에 있어서는 차이가 있었다. 10분 처리시에는 아미노산 분획보다 중성분회(당, 인산염에스퇴르 및 유기산)에서 label 양이 4.5배 증가하였으나 30분 처리시에는 1.7배로 감소하였다. 당분획에 있어서는 처리 시간이 길어짐에 따라 label 양이 약간 증가 하였으나 아미노산 분획에 있어서는 양과 질적으로 label 양이 현저히 증가하였다. 탄소 동화율은 10분에서 30분으로 길어질수록 현저히 감소하였다(0.125대 0.034와 0.042 mole CO2 /mg 엽록소/분).