Recent earthquake of incidence is increasing. The purpose of this study was to investigate the strain characteristics of bare frame with non-seismic details. The experimental investigation consisted of a cyclic load tests on 1/3-scale models of one story-one bay bare reinforced concrete frame.

This research investigated the effects of adding micro fibers on the direct tensile behavior of ultra-high-performance hybrid-fiber-reinforced concrete (UHPHFRC) at high strain rates. Macro fiber was long smooth fiber (LS, Df=0.3mm, Lf=30mm) and micro fiber was short smooth fiber (SS, Df=0.2mm, Lf=13mm). The volume content of macro fibers was 1.0% and the volume content of micro fibers varied between 0.0 and 1.0%. The addition of micro fibers clearly increased the tensile strength of UHPHFRCs even at high strain rates.

To evaluate the stress-strain relationship of HVFA(High Volume Fly Ash) concrete, experiments were performed according to the ratio of fly ash usage and concrete compressive strength. Test results were shown that elasticity modulus of HVFAC was influenced by compressive strength, elasticity modulus and fly ash usage ratio. And the existing equation of stress-strain relationship had a large difference. So, new equation of stress-strain relationship for HVFAC was proposed, and the proposed results had a good correlation with test results

A strain compatibility method is based on the strain compatibility approach proposed by AISC (American Institute of Steel Construction, Inc.). The strain compatibility method assumes a linear strain of all the members. After that, set up the equilibrium equations of the state of stress in each component for calculating the location of the neutral axis of the cross-section in the presence. In this study, the reinforced concrete simple beam is analyzed by strain compatibility method for calculating the neutral axis and the bending moment. And then, a variation of neutral axis of the reinforced concrete simple beam is measured.

콘크리트 공시편의 외부보강을 위해서 강판과 FRP 자켓을 이용하였다. 기존의 강판 또는 FRP 자켓 보강기법은 보강재와 콘크리트 사이에 접착제를 이용하여 시공하므로 콘크리트와 보강재가 합성거동 하게 된다. 그러나 본 연구에서 사용한 강판 보강기법은 외부압착에 의한 기법으로 강판과 콘크리트가 합성거동을 하지 않는다. 본 연구에서는 비합성거동과 합성거동을 하는 보강된 콘크리트 시편의 압축 변형률의 측정과 이를 보정하는 기법을 제시하였다. 비합성거동의 강판보강 콘크리트 시편의 압축변형률 측정은 강판의 표면에서 변형률을 측정하여 표시할 수 없으며, 시편에 설치하여 측정하는 compressometer를 사용할 수도 없었다. 따라서 시편의 상하단에 두꺼운 판을 설치하여 두 판사이의 변형을 측정한 후. 이를 압축변형률로 변환하였다. 합성거동을 하는 FRP 보강의 경우는 FRP 튜브 표면에서 측정되는 수직방향의 변형률을 콘크리트의 압축변형률로 사용이 가능하다. 그러나 튜브 표면의 수직변형률은 시편의 부풀음에 의한 인장변형률이 포함되어 있기 때문에 콘크리트의 압축변형률을 추정하기 위해서는 이를 보정하여야 한다. 보정된 압축변형률은 콘크리트 내부에서 측정한 변형률과 기존의 콘크리트 연속체 모델과 비교하였을 때, 만족한 결과를 보였다. 보정 전의 응력-변형률 곡선은 콘크리트의 연성거동 및 에너지 소산능력을 보정 전에 비해 낮게 평가할 위험성이 있다.