The objective of this experiment was to study some possibilities to simplify freezing, thawing and transfer procedure of one-step straw method comparing with the conventional methods using bovine embryos. The previous work are also designed to investigate the thawing effect by development stage and its quality using the embryos. Results obtained were summarized as follows: 1. A total of 87 embryos from 14 donor cows were frozen-thawed and an average of frozen embryo/donor was 6.2. 2. The survival rates of morula stage(65.4%) were higher than those of blastocyst stage(57.l%) and vice versa in rate of morphological recovery (80% vs 95.4%). However. no significant difference was denoted between them. 3. In difference between the groups of good quality and poor quality. good quality was resulted in a significantly higher embryo survival rate(75%) and recovery rates(95%) than poor quality(P<0.0l). 4. In effects of non-permeable sugar dilution in added to l.0M glycerol. higher survival rates were orderd in sucrose. lactose, raffinose and xylose. But lactose-raffinose, sucrose-trehalose and xylose in added to 2.OM glycerol. 5. The highest survival rates were obtained by direct plunge into the liquid nitrogen with 3.OM concentration both of glycerol and trehalose. 6. The survival rates in vitro condition of one-step and direct plunge methods(75%-87.5%) were significantly higher than those of multiple steps (21.4-52.6%) in in vitro (P<0.0l). However, the results of single-step were critical in comparing to other steps of final pregnant conformation.

공란우 89두와 수라우 94두를 사용하여 호르몬 투여에 대한 난소반응, glycerol의 평형과 제거방법에 따른 융해란자의 형태적 정상성과 동결 융해란의 이식후 임신율과 쌍태유기율을 조사하였다. 1. 호르몬처리에 대한 난소반응 :1) 과배란 처리후 배란된 난자수는 A.B.C군에서 각각 8.3, 7.8, 9.5개로서 C군이 전체 평균의 8.3개보다 증가되었다. 2) 난자의 회수율은 42.1%, 두당회수된 난자수는 3.5개였으며, 회수란자중 정상발육한 상실

지표에 노출된 암석은 지속적으로 풍화를 받게 되고 이러한 영향으로 암석의 공학적 안정성이 약해 지게 된다. 특히 풍화가 진행되면서 암석의 표면은 풍화에 의해서 변화를 일으키고 이러한 표면 변화는 암석 으로 구성된 지반의 공학적 안전성에 영향을 미치게 된다. 또한, 풍화를 받은 암석에서 생성되는 화학종은 주 변환경에 직접적인 영향을 미치거나 구조물에 영향을 미치게 된다. 광산지역과 같이 암석이 노출된 지역에서 는 풍화에 의해 생성된 화학종이 주변 자연환경에 심각한 영향을 미치기도 한다. 본 연구에서는 이러한 관점 에서 동결/융해 실험을 활용한 풍화가속 실험을 이미 풍화를 받은 암석과 신선한 암석을 대상으로 실시하고 각 암석의 표면 변화를 다초점 레이저 현미경으로 관찰하고 IC/ICP-MS를 활용하여 화학종 생성에 대한 분 석을 실시하였다. 풍화가 진행됨에 따라 표면의 거칠기는 완화되는 것을 확인하였고 주변환경에 영향을 미칠 수 있는 화학종은 풍화를 받는동안 양이 증가하는 것을 확인하였다. 본 연구 결과는 암석이 노출된 지역에서 의 공학적/환경학적 안전성을 평가하는 기초 자료로 활용될 수 있을 것이다.

국내 철근콘크리트 구조물의 경우 제작 시기를 고려했을 때 노후화가 상당히 진행된 경우가 많다. 이에 대한 안전검토 및 내진성능평가를 위해서는 노후화된 재료의 특성을 고려하여 평가하여야 한다. 그 중 동결융해에 관한 실제 거동에서 유사한 거동을 분석하기 위하여 실제 구조물의 형태에 가깝게 제작하여 평가를 진행 할 필요가 있다. 이에 본 연구에서는 300×450×2240mm의 보를 제작하였다. 동결융해된 보는 KS F 2456 및 ASTM C 666에서 제시하고 있는 동결융해 시험법을 따라 - 18℃~4℃를 1Cycle로 선정하여 300Cycle의 동결융해를 진행하였다. 두 시편 모두 4점 휨 실험(4Point Bending Test)으로 실험하였다.

Generally, reinforced concrete structures are exposed to complex deterioration. It is necessary to investigate the effect of decreasing the strength of reinforced concrete structures subjected to aging more frequently. Therefore, this study aims to analyze the resistance to freezing and thawing during complex deterioration. After the beam specimens were prepared, the freezing and thawing tests were carried out and the strength of the specimens subjected to freezing and thawing decreased as a result of 4 - point bending test.

The purpose of this study is to investigate the freeze - thaw behavior of FRP reinforced concrete structures. Under the same conditions, two FRP reinforced beam specimens were made, and one speciemen was subjected to freezing and thawing. Then a four-point bending experiment was conducted. As a result, it was analyzed that the load values of reinforced specimens after freezing and thawing appear less at the same displacement in displacement-load behavior.

Concrete structures are exposed to complex degradation environments depending on their environmental characteristics. The concrete members of bridges are exposed to water and salt by rivers and oceans, and there is always a possibility of freezing and thawing damage in the upper and lower part of the bridge due to the continuous heat and heavy snow in summer and winter. In this study, a freeze-thaw test method which indirectly evaluates the strength reduction of concrete according to the repeated cycle of freezing and thawing was proposed, and the strength reduction rate was measured by using the concrete specimen. As a result, the concrete strength was reduced by 20% in freeze-thaw test method. In the future, it can be used as a basic data of the study on strength of each cycles.

본 연구에서는 동결융해 작용을 받는 콘크리트의 내구성을 현장에서 평가하기 위한 일환으로 표면 거칠기 값과 이미지 분석을 대 상으로 상대동탄성계수와의 관계를 분석하였다. 배합은 물-시멘트비에 따라 40%, 50%, 60% 및 70% 총 4배합으로 수행하였으며 동해를 조기에 발현시키기 위하여 AE제를 사용하지 않았다. 실험은 물-시멘트비에 따라 상대동탄성계수 및 압축강도 등의 기본 물성 시험과 표면 거칠기 측정, 화상 이미지 및 SEM 이미지 분석을 수행하였다. 표면 거칠기 시험 결과 물-시멘트비에 상관없이 전반적으로 싸이클이 증가함에 따라 표면거칠기 값이 증가하는 경향을 보였으며 상대적으로 조밀한 40% 및 50%의 경우 상대동탄성계수가 60% 이하인 시점까지 서서히 증가하는 경향을 보였으나, 60% 및 70%의 경우 파괴 시점에서만 표면 거칠기 값이 증가하였다. 또한, 표면부 화상 이미지 분석에서도 물-시멘트비 40% 및 50%의 경우 동결융해 싸이클이 진행되는 과정에서 표면부터 서서히 열화가 진행되는 과정을 확인할 수 있었으나 60% 및 70%의 경우 표면 부의 변화가 미미하다 파괴 시점에서 균열 등의 손상을 확인할 수 있었다. 따라서, 상대적으로 수밀하지 않은 시험체의 경우 화상 이미지나 표면 거칠기 등의 인자로 동결융해의 열화 정도를 판별하기에는 일부 제한이 있을 것으로 판단되며 상대적으로 수밀한 W/C 40% 및 50%의 경우 표면 거칠기 및 표면부 화상 이미지로 동해의 열화 진행 정도를 판단할 수 있었으며 향후 현장에서 표면 거칠기 및 이미지 분석을 적용할 수 있을 것으로 판단된다.

The purpose of this study is to evaluate the tensile strength of GFRP and BFRP Rebar after exposure to environmental factors of deterioration (alkali, freezing -thawing) in order to present that as basic data for the application of FRP Rebar as concrete reinforcement. As a result, in the exposure of an alkali environment, the deterioration of fiber-resin was accelerated as the temperature increased, and it was found that there was an insignificant effect on freezing-thawing.

In this study, To evaluate the durability of concrete by freezing-thawing, relative dynamic modulus of elasticity and surface roughness were measured. The results showed that the surface roughness can be used to understand the damage tendency of freezing-thawing and the durability of concrete.

In this study, To evaluate the durability of concrete by freezing-thawing, relative dynamic modulus of elasticity and surface roughness were measured. The results showed that the surface roughness can be used to understand the damage tendency of freezing-thawing and the durability of concrete.