PURPOSES: The objective of this study is to evaluate the properties of high-performance concrete and compare them with the properties of ternary blended cement (OPC 60% : BFS 30% : FA 10%) as applied to all-in-one bridge decks. High-performance concrete modified with styrene-butadiene latex (SB latex) was evaluated for strength development and durability through its compressive strength and chloride ion diffusion coefficient. METHODS: The compressive strength test was conducted according to KS F 2405, and the average value of the three specimens was used as the result at each stage. The chloride ion diffusion test was performed at 28 days, 56 days, and 365 days according to NT BUILLD 492. The chloride ion penetration test was conducted according to ASTM C 1202. RESULTS: For the compressive strength of the high-performance concrete, the blast furnace slag 40% replacement (BFS40) mixture had the most similar results to those of the ternary blended cement. The BFS40 mixture exhibited a lower compressive strength at 3 days than the latex modified concrete (LMC) mixture used for the bridge deck pavement, whereas it exhibited a 3.7-9.8% higher compressive strength at 7 days. In addition, the BFS40 mixture had the lowest diffusion coefficient, which was 49.1~59.0% lower than that of the LMC mixture. Mixing with latex tended to decrease in charge passed compared to Plain which is only used ternary blended cement, and showed excellent watertighness (rated “very low”), which is lower than 1,000 coulombs in all mixtures with latex. CONCLUSIONS : The BFS40 mixture exhibited excellent compressive strength, chloride ion permeability resistance, and the lowest chloride ion diffusion coefficient although it included a small amount of latex, which makes it more expensive than the current LMC mixture. It is believed that it is possible to secure excellent economic efficiency and durability by using lesser latex than that in the LMC mixture and using a mixture of the blast furnace slag instead.

본 연구는 초고성능 콘크리트의 성능을 보다 향상시키기 위해 현재 콘크리트 보강에 사용하는 섬유들을 조합한 복합 섬유를 제작하여 복합섬유 혼입 초고성능 콘크리트의 강도 특성을 분석하였다. 복합섬유 4종과 단일섬유 3종을 각각 혼입하여 유동성과 압축, 휨강도 실험을 진행하였다. 복합섬유와 단일섬유 혼입 시험체 모두 유동성 평가를 만족하였으며, 단일섬유가 조금 더 우수한 성능을 나타내었다. 강도 평가결과 파라아라미드 섬유와 강섬유를 조합한 복합섬유 2종이 가장 우수한 결과를 나타내었으며, 복합섬유 직경 차이에 따라 압축 및 휨강도 보강효과가 다르게 나타난 것을 확인할 수 있었다. 압축강도 감소를 최소화하며 휨강도를 증가시킨 결과를 통해, 복합섬유는 단일섬유 간의 단점을 서로 보완할 수 있을 것으로 판단되며, 본 연구를 통해 차후 콘크리트의 다양한 재료적 특성을 보강하는 복합섬유도 충분히 제작 가능할 것으로 판단된다.

It is a well known that concrete is strong for compression and weak for tension. For reinforcing the weakness and improving the performance about concrete, various methods are used. Fiber reinforced concrete that is one of them has been investigated in this study. The function of fiber in concrete is to improve the stress strain relation and toughness, crack control. It’s applied from normal strength concrete to ultra-high performance concrete. But it is essential to disperse fiber uniformly and to prevent aggregation of fiber in concrete, in order that fiber reinforced concrete show the sufficient performance. The various properties of fiber affect the essential properties, for instance, length and diameter of fiber, source, etc. So, this study evaluated the ultra-high performance concrete with mixed in composite fiber.

최근 온실가스 감축을 위해 시멘트 클링커를 대체하여 고로슬래그 미분말을 다량 치환한 하이볼륨 슬래그 시멘트에 대한 연구 활 발히 진행되고 있다. 하지만, 수화열 및 내구성 등 다양한 장점에도 불구하고 초기 재령에서의 낮은 강도 발현 등의 문제점으로 인해 실제 현장 의 적용에 한계점을 가지고 있다. 본 연구는 이러한 점을 극복하고자 GGBFS 혼입률에 따른 페이스트의 압축강도, 수화열 등의 특성을 분석하 였다. GGBS 분말도에 따른 4종류와 치환율 35%, 50%, 65%, 80% 4수준으로 하여 총 16개의 배합에 대해 실험을 수행하였다. 실험결과 낮은 물-바인더 비에 의한 고성능 하이볼륨 슬래그 시멘트 페이스트 배합은 초기 재령에서의 낮은 압축강도의 한계점을 극복할 수 있을 것으로 판단된 다. 또한 GGBS의 분말도는 고성능 하이볼륨 슬래그 시멘트 페이스트의 초기 재령에서의 압축강도 증진에는 효과가 있지만, 28일 이후의 장기 강도에는 큰 영향이 없는 것으로 나타났다.