Silica is used in shell materials to minimize oxidation and aggregation of nanoparticles. Particularly, porous silica has gained attention because of its performance in adsorption, catalysis, and medical applications. In this study, to investigate the effect of the density of the silica coating layer on the color of the pigment, we arbitrarily change the structure of a silica layer using an etchant. We use NaOH or NH4OH to etch the silica coating layer. First, we synthesize α-FeOOH for a length of 400 nm and coat it with TEOS to fabricate particles with a 50 nm coating layer. The coating thickness is then adjusted to 30–40 nm by etching the silica layer for 5 h. Four different shapes of α-FeOOH with different colors are measured using UV–vis light. From the color changes of the four different shapes of α-FeOOH features during coating or etching, the L* value is observed to increase and brighten the overall color, and the b* value increases to impart a clear yellow color to the pigment. The brightest yellow color was that coated with silica; if the sample is etched with NaOH or NH4OH, the b* value can be controlled to study the yellow colors.

본 연구에서는 역삼투막의 내오염성을 향상시키기 위해 실란 커플링제로 표 면 개질하여 steric hinderance를 일으키고 에폭시 코팅으로 친수성을 향상시키고자 하였다. 상용 역삼투막을 UV로 식각하여 표면을 활성화한 후 말단기가 다 른 실란 커플링제를 sol-gel 공법으로 표면 개질하고 에폭시를 이용하여 코팅하였다. 그 결과, 친수성 및 내오염성이 향상된 것을 확인하였고, FT-IR, SEM, XPS 를 통해 막의 특성을 분석하였다.

PCB 제조에서 photoresist와 Copper Clad Laminate(CCL)의 구리표면과의 부착력을 항상시 키기 위하여 사용되는 soft etching제를 제조하기 위하여 과산화수소 사용을 배제하고, 유기산과 유기과 산화물을 이용하여 산의 종류, 농도, 에칭시간 등에 따른 구리표면의 에칭속도, 표면 조도, 및 오염도 등 을 조사하였다. 또한 에칭 후의 표면의 얼룩을 제거하기 위한 안정제의 최적 배합 및 농도도 확립하였 다. 본 연구 결과 유기산의 종류 중에서는 아세트산이 초기 구리 에칭속도가 가장 빨랐으며, 농도가 0.04 M이었을 때 0.4 μm/min이였다. 유기과산화물인 APS의 농도는 높을수록 에칭속도가 가장 빨랐으나, 표면 오염이 심각하였다. 안정제 용액의 조성도 표면 오염도에 큰 영향을 주었다. 결과적 0.04 M 아세 트산, 0.1M APS에 4 g/L의 안정제(ST-1)를 첨가한 에칭액의 경우 0.37 μm/min의 에칭속도와 표면 오염이 전혀 없으며, 표면 조도도 가장 우수하였다. 즉, CCL과 photoresist와 접착력을 향상시킬 수 있 을 것으로 판단된다.

This essay examines Rembrandt van Rijn(1606-1669)'s landscape etchings, focusing on their characteristic rendition of humans in a minuscule and shady form to embody the theme of rural life. Unlike conventional landscape paintings which foreground shepherds or farmers to convey peace and tranquility of idyllic atmosphere, Rembrandt's etchings of the same theme cover the humans and other objects with a dense hatching, rendering them nearly invisible. The mainstream view maintains that the painter intended to emphasize rural life itself by placing little distinction between humans and surrounding landscapes. This interpretation draws on the painter's personal history that he stayed for convalescence in the suburbs of Amsterdam in the late 1630s. Admitting the validity of the biographical approach as such, this study enacts a different angle to read the Rembrandt etchings in the social contexts. It pays attention to the fact that the Dutches of the mid-Seventeenth Century found in countrysides an emotional as well as physical resting place isolated from ever expanding cities. The trend among upper-classes was to purchase lands in rural areas where they built private resorts. Lower-middle classes, the largest segment of the population, couldn't afford such a luxury, but they sought the grace of nature in literature, meditations, and paintings. Therefore, there was a great demand for the landscape paintings portraying idyllic sceneries. Rembrandt's landscape etchings were conceived of to meet the demands of the paintings market. Yet they were not just consumer-oriented commodities. A great religious meditator himself, Rembrandt induced the potential viewer to have three phases of artistic experience or spiritual awakening. First, the viewer distances herself from the landscape portrayed on an etching work, but she finds it hard to locate the main motifs. Next, a long hard gaze enables the viewer to see the motifs of lovers, shepherds, and saints, but shortly afterwards she wonders why their shapes are masked by thick hatching lines. Finally, the viewer comes to understand what the style signifies: the humans are part of nature, a mere creation of God. This study concludes that Rembrandt invited his contemporaries, who longed for rural life, to his landscape etchings where he encapsulated his message that the true meaning of natural life is the life of religious devotion.

본 연구는 인쇄회로기판(PCB) 제조 시 에칭공정에서 발생되는 구리이온(Cu+2)을 고농도로 함유한 황산 폐에칭액을 NF 막분리법을 사용하여 에칭액 회수와 구리이온 처리를 효율적으로 수행하기 위한 NF 막여과 공정의 운전 조건을 설정하기 위한 기본 자료를 확보하는데 있다. 이를 위해 미국 Koch사의 SelRO MPS-34 4040 NF 막을 대상으로 구리이온을 고농도(5~25 g/L)로 함유한 모의 황산 폐에칭액의 회분식(dead-end) 나노여과 실험을 수행하여 투과 플럭스와 구리이온의 총괄 배제도를 측정하였다. 이 결과 황산용액에의 막 보관기간이 길수록, 황산용액의 pH가 낮을수록 황산에 의한 NF 막의 손상이 더 크게 발생하여 순수 투과 플러스가 증가하였다. 황산 폐에칭액의 투과 플럭스는 황산용액 내 구리이온의 농도가 증가할수록 막 표면에의 구리이온 농축(농도분극)의 증가에 따라 감소하였으며, 구리이온의 배제도는 구리이온의 농도가 높을수록, pH가 낮을수록, 황산용액 내의 막 보관기간이 길수록 낮아져 초기 37%에서 최소 15% 수준으로까지 감소하였다.

본 연구는 전자 및 반도체 산업의 각종 에칭공정에서 발생되는 중금속 함유 산성 폐에칭액을 NF 막분리법을 이용하여 에칭액 회수와 중금속 처리를 효율적으로 수행하기 위한 NF 막공정의 운전조건을 설정하기 위한 기본 자료를 확보하는데 있다. 이를 위해 3가지 종류의 상용 NF 막(General Electric Co. Duraslick NF-4040 막, Dow Co. Filmtec LP-4040 막 및 Koch Co. SelRO MPS-34 4040 막)을 대상으로 Pb+2 중금속을 함유한 모의 질산 폐에칭액의 회분식(dead-end) 막여과 실험을 수행하여 폐에칭액의 투과 플럭스와 Pb+2 중금속 이온의 총괄 배제도를 측정하여 폐에칭액 처리에 우수한 NF 막을 선정하였다. 실험결과 질산용액에의 막 보관기간이 길수록, 질산용액의 pH가 낮을수록 산에 의한 막의 손상이 심해졌으며, 질산에 의한 막의 손상은 SelRO MPS-34 4040 < Duraslick NF-4040 < Filmtec LP-4040 막의 순서로 심하게 일어났다. 또한 질산용액에의 막 보관기간이 길수록, 질산용액의 pH가 낮을수록 Pb+2 이온의 배제도가 낮아졌으며, 배제도 값은 Duraslick NF-4040 막의 경우에는 95% 수준의 초기 배제도 값에서 질산용액에의 4달 보관 후에는 20% 수준으로, SelRO MPS-34 4040 막의 경우에는 초기 85% 수준에서 4달 후 65% 수준으로, Filmtec LP-4040 막의 경우에는 초기 90% 수준에서 4달 후 10% 이하 수준으로까지 감소하였다. 3종류의 상용 NF 막 중 내산성 용도로 개발된 SelRO MPS-34 4040 막이 중금속 함유 산성 폐에칭액의 재생에 가장 적합하였다.

전통적으로 초경합금은 무라까미 용액에서 에칭하거나 묽은 염산에 넣고 끓이는 방법에 의해 그 밋구조를 관찰하였다. 그러나 carbide 입자가 suvmicron 크기인 초경합금에서는 전통적인 에칭 방법으 에칭 후에도 입자/기지상, 입자/입자 입계를 동시에 구분시킬 수 있는 SEM 사진을 얻을 수 없다. 본 연구에서는 submicron 크기 초경합금의 고배율 SEM 사진을 얻을 수있는 90H2O2 - 10HNO3 (vol%)의 새로운 에칭 용액을 개발하였다

고순도알루미늄 유전체의 내부표면적을 증가시키기 위하여 1M의 염산 에칭용액에 첨가제를 사용했을 때 나타나는 에칭특성의 변화를 조사하였다. 염산용액에 에틸렌글리콜이 첨가된 혼합용액에서 에칭을 실시했을 경우 알루미늄 기지 표면에 미세하고 균일한 에치피트가 형성되어 표면적 증가 효과가 크게 나타났으며, 또한 양극 산화 후 측정된 정전용량의 결과에서도 에틸렌 글리콜이 첨가된 에칭액에서 제조된 유전체는 표면적 증가에 의한 높은 정전용량 값을 나타냈다.

본 연구를 통해 반도체 산업에서 유래된 마이크로웨이브 증폭 에칭기술(MEE)을 이용하여, 마이카의 표면 구조를 변화시키고 오일 흡유량을 조절할 수 있었다. 마이크로웨이브 에너지가 마이카에 조사되면, 마이카 표면이 몇 분 이내에 에칭이 된다. 에칭의 결과로 마이카의 오일 흡유량이 증가되고, 마이카 SiO2층의 표면 변화에 의해 백색도가 증가한다. 추가적으로, 땀을 흡수한 이후에도 높은 백색도가 유지된다. 마이카의 표면구조의 변화는 불산에 슬러리화된 마이카에 마이크로웨이브 조사를 통해서 이루어졌다. 에칭의 정도는 산의 농도, 조사 시간, 조사 에너지의 양, 슬러리의 농도에 의해 조절되었다. 에칭된 마이카의 표면 구조는 ‘달' 표면 모양과 유사하게 보인다. 표면적과 거칠기 등의 특성은 Brunauer-Emmett-Teller (BET), atomic force microscopy (AFM), scanning electron microscopy (SEM), Spectrophotometer, goniophometer로 측정되었다.