In this study, a composite material suitable for flexible transparent electrodes was fabricated using Norland Optical Adhesive 68 (NOA 68), an ultraviolet (UV) curable polymer, and silver nanowires (Ag nanowire, AgNW). The mechanical behavior of this composite was then analyzed. A AgNW network structure was embedded in the NOA 68 polymer and cured using UV energy. The composite was prepared with an AgNW network structure formed approximately 4 μm from the top of the NOA 68 matrix. Tensile test specimens were prepared according to ASTM standards, and tensile tests were conducted at room temperature in air. Scanning electron microscopy (SEM) and tensile tests were used to analyze the changes in mechanical behavior according to UV exposure time and the presence of AgNW. The results showed that as UV curing time increased, the yield strength of the composite increased while the elongation decreased. Regardless of the presence of the AgNW filler, the stress-strain curves of the ductile polymer exhibited the typical mechanical behavior of semi-crystalline polymers as UV curing time increased, characterized by strain softening. It was also confirmed that the composite impregnated with AgNW exhibited higher strength in response to changes in mechanical properties due to UV curing.

Among various organic materials suitable for silicon-based inorganic-organic hybrid solar cells, poly(3,4-ethylenedioxythiophene): poly(styrene sulfonate) (PEDOT:PSS) has been extensively studied due to its high optical transmittance, high work function, and low bandgap characteristics. The electro-optical properties of PEDOT:PSS have a significant impact on the power conversion efficiency of silicon-organic hybrid solar cells. To enhance the photovoltaic properties of the silicon-organic hybrid solar cells, we developed a method to improve the properties of the PEDOT:PSS film using Ag nanowires (NW) instead of conventional solvent addition methods. The influence of the Ag NW on the electro-optical property of the PEDOT:PSS film and the photovoltaic performance of the silicon-organic hybrid solar cells were investigated. The addition of Ag NW further improved the sheet resistance of the PEDOT:PSS film, enhancing the performance of the silicon-organic hybrid solar cells. The present work using the low sheet resistance PEDOT:PSS layer paves the way to develop simple yet more efficient siliconorganic hybrid solar cells.

We report on stretchable electrochromic films of poly(3-hexylthiophene) (P3HT) fabricated on silver nanowire (AgNW) electrodes. AgNWs electrodes are prepared on polydimethylsiloxane (PDMS) substrates using a spray coater for stretchable electrochromic applications. On top of the AgNW electrode, poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) is introduced to ensure a stable resistance over the electrode under broad strain range by effectively suppressing the protrusion of AgNWs from PDMS. This bilayer electrode exhibits a high performance as a stretchable substrate in terms of sheet resistance increment by a factor of 1.6, tensile strain change to 40%, and stretching cycles to 100 cycles. Furthermore, P3HT film spin-coated on the bilayer electrode shows a stable electrochromic coloration within an applied voltage, with a color contrast of 28.6%, response time of 4-5 sec, and a coloration efficiency of 91.0 cm2/C. These findings indicate that AgNWs/PEDOT:PSS bilayer on PDMS substrate electrode is highly suitable for transparent and stretchable electrochromic devices.

Fluorine-doped SnO2 (FTO) thin film/Ag nanowire (NW) double layers were fabricated by means of spin coating and ultrasonic spray pyrolysis. To investigate the optimum thickness of the FTO thin films when used as protection layer for Ag NWs, the deposition time of the ultrasonic spray pyrolysis process was varied at 0, 1, 3, 5, or 10 min. The structural, chemical, morphological, electrical, and optical properties of the double layers were examined using X-ray diffraction, X-ray photoelectron spectroscopy, field-emission scanning electron microscopy, transmission electron microscopy, the Hall effect measurement system, and UV-Vis spectrophotometry. Although pure Ag NWs formed isolated droplet-shaped Ag particles at an annealing temperature of 300 oC, Ag NWs covered by FTO thin films maintained their high-aspect-ratio morphology. As the deposition time of the FTO thin films increased, the electrical and optical properties of the double layers degraded gradually. Therefore, the double layer fabricated with FTO thin films deposited for 1 min exhibited superb sheet resistance (~14.9Ω/□), high optical transmittance (~88.6 %), the best FOM (~19.9 × 10−3 Ω−1), and excellent thermal stability at an annealing temperature of 300 oC owing to the good morphology maintenance of the Ag NWs covered by FTO thin films.