Artificial graphites have been used in various applications, for example, as anode materials for Li-ion batteries, C/C composites, and electrodes for aluminum smelting, due to their unique mechanical strength and high thermal and electrical conductivity. Artificial graphites can be manufactured by a series of kneading, molding, carbonization and graphitization processes with an additional impregnation process. In this study, the influence of the process variables in the kneading and carbonization/graphitization process on the properties of the resulting carbon block was systemically investigated. During the kneading process, the optimum kneading temperature was 90 °C higher than the softening point of the binder pitch; thus, the binder pitch reached its maximum fluidity. On the other hand, during the carbonization and graphitization process, the structural properties of carbon blocks prepared at different heat treatment temperatures were examined and their structural change and evolution were closely described according to the temperature and divided into low-temperature carbonization and high-temperature carbonization/graphitization. Based on this study, we expect to provide a better understanding of setting the parameters for thermally conductive carbon block manufacturing.

Poly(ether block amide) (PEBA)는 이산화탄소 분리에 매우 적합한 상용 블록 공중합체 중 하나이다. 기체분리막의 경우 높은 투과도 뿐 아니라 강한 기계적 강도 또한 필요로 한다. PEBA공중합체의 결정성 폴리아마이드(polyamide) 블록은 기계적 강도를 제공하며 동시에 rubbery한 폴리에테르(polyether) 부분은 이산화탄소와의 친화도를 부여하여 이산화탄소 촉진 수송에 기여한다. PEBA공중합체에서 결정성 상과 rubber한 상의 조성은 기체분리막에 적합하게 조절될 수 있다. PEBA 공중합체를 기반으로 한 분리막은 좋은 투과도를 갖지만 추가적으로 분자체 효과를 이용하여 큰 기체 투과도 손실 없이 분리막의 선택도를 향상시킬 수 있다. 혼합 매질 분리막은 혼합막의 한 종류로서 고분자 매트릭스와 유기 첨가제로 이루어져 있다. 하지만 고분자 매트릭스와 유기 첨가제간의 양립성(compatibility)에 따른 문제점 또한 존재한다. 따라서 본 총설에서는 PEBA 공중합체를 기반으로 한 혼합막의 장점과 한계에 대해 다루고자 한다.

Coke aggregates and carbon artifacts were produced to investigate the interactions of coke and pitch during the kneading process. In addition, the kneading ratio of the coke and binder pitch for the coke aggregates was controlled to identify the formation of voids and pores during carbonization at 900°C. Experiments and thermogravimetric analysis revealed that carbon yields were improved over the theoretical yield calculated by the weight loss of the coke and binder pitch; the improvement was due to the binding interactions between the coke particles and binder pitch by the kneading process. The true, apparent, and bulk densities fluctuated according to the kneading ratio. This study confirmed that an excessive or insufficient kneading ratio decreases the density with degradation of the packing characteristics. The porosity analysis indicated that formation of voids and pores by the binder pitch increased the porosity after carbonization. Image analysis confirmed that the kneading ratio affected the formation of the coke domains and the voids and pores, which revealed the relations among the carbon yields, density, and porosity.

본 연구에서는 현재 전량 폐기되는 정수기용 폐 카본블록 필터를 재활용하고자 폐 필터의 특성을 파악한 후 열 처리를 진행하였다. 성능 평가를 위해 실제 정수기에서 사용 후 폐기되는 카본블록 필터 (도레이 케미칼에서 제조)를 회수하여 활성탄의 흡착능을 측정하였다. 대조군으로써 새 필터도 같은 조건으로 진행하였다. 재활용을 위한 열처리의 온도는 400, 550, 및 700℃로 진행하였으며 최적 조건을 찾기 위해 새 필터에 먼저 열처리를 진행하였다. 또한 TGA, DSC, SEM 및 BET를 이용하여 폐 필터의 표면 특성을 분석하였다. 이러한 결과를 바탕으로, 폐 필터 표면에 막 오염(fouling)과 정도를 확인하였으며, 폐 카본블록 필터의 재활용 및 복원기술 연구를 통한 순환 활용 기술을 확보하고자 한다.

This paper deals with block shear fracture behavior in base metal of carbon steel welded connection. Monotonic tensile experiments have been conducted to investigate the structural behaviors of carbon steel fillet-welded connection with the block shear fracture in base metal. Main parameters are weld lengths in the longitudinal and transverse directions of applied force. Finite element analysis in this paper focused on the ultimate strength and fracture mode of welded connections. It was shown that predictions by finite element analysis method were in a good correspondence with test results for ultimate behaviors such as fracture mode and ultimate strength.