In this study, the following conclusions were obtained after friction stir welding of Al 6061-T651. 1) The organization of the welding unit is largely divided into four parts, the Stir zone, themal-mechanical affected zone, heat affected zone, it was confirmed that it is clearly separated into the material portion. 2) As a result of observing the hardness test results of the welding unit, the minimum hardness value was about 45Hv, which was significantly lower than the hardness of the base material about 72Hv. 3) The tensile strength of the welding part was about 2/3 compared to the tensile strength of the base material.

알루미늄합금 6061-T6 판재에 대하여 마찰교반용접과 텅스텐 이너트 가스 용접의 교차 용접부의 미세조직과 기계적 특성에 있어서 용접 순서의 영향을 분석하기 위한 시험편을 성공적으로 제작하였다. FSW-ED 시험편이 다른 조합들보다 가장 좋은 기계적 특성을 나타내었다. 흥미롭게도, TIG-FSW ED 시험편이 FSW-TIG ED 시험편보다 높은 인장강도를 나타내었다. 용접부 경도의 경우, FSW 시편이 TIG-FSW 및 FSW-TIG 시험편보다 높은 값을 나타내었고, TIG-FSW 시험편이 FSW-TIG 시험편보다 높은 값을 나타내었다. FE-SEM을 이용한 인장 파면에 대한 관찰을 통하여, 모든 시험편에서 연성파괴를 나타내는 다양한 크기의 딤플들이 관찰되었다. FSW-TIG 시험편의 파면에서는 용융지(熔融池) 표면 영역에서 기공들이 관찰되는 반면, TIG-FSW 시험편에서는 기공의 형성은 관찰되지 않았다. 경도와 미세조직의 결과를 통해 TIG-FSW 공정이 FSW-TIG 공정보다 높은 인장강도를 확보할 수 있는 공정임을 확인하였다.

In this study, Equivalent fracture strain and Fracture energy were evaluated with the small punch test(SP test) for friction stir welded(FSW) Al6061-T6 sheets. With the three rotation speeds and the three feeding rate, The nine different conditions of FSW were prepared for the SP test. The SP test specimens were manufactured and tested on the advancing side, center, and retreating side to the tool rotation direction. From the SP test data, the equivalent fracture strain and the fracture energy were analyzed. The high value of equivalent fracture strain was attained form tool rotational speed 900RPM and feeding rate 330mm/min. It is found that its characteristic is about 14% higher than the value of condition 1100RPM-330mm/min that have the lowest value. The high value of fracture energy was obtained from the tool rotation speed 900RPM and feeding rate 330mm/min. The lowest fracture energy, which from 1000RPM-300mm/min, was approximately 16% difference to the highest value.

In this study, the weldability of ADC12 FSW joints obtained by the load control type of the FSW machine is examined. The higher the tool plunge downforce the wider the range of the optimum FSW conditions is obtained. However, there is a limit of optimum range with increasing the tool plunge downforces. The three different types of defects are formed in ADC12 FSW joints, depending on the welding conditions. One is a large mass of flash due to the excess heat input, another is a cavity or groove-like defects caused by insufficient heat input and the other is a cavity caused by the abnormal stirring. As for the abnormal stirring, it is very clearly seen that the shape of the top part on the advancing side in the stir zone is completely different. For this type of defect, the effect of the tool plunge downforce is not significant, though the size of the defect due to insufficient heat input significantly is decreased with the increasing downforce