Recently, the amount of the mineral admixture including fly ash and ground granulated blast-furnace slag was increased for the purpose of CO2 gas emission reduction in the concrete industry. However, in the case of korea, estimation model of strength development in concrete structural design code was prescribed a constant value according to cement type and curing method about the portland cement. therefore, the properties of strength development according to time of concrete using fly ash and ground granulated blast-furnace slag does not reflected estimation model of strength development. Accordingly, this paper was evaluated strength according to time on the concrete strength range using fly ash and ground granulated blast-furnace Slag and the strength development constant Bsc of concrete according to the kind of the mineral admixture and mixing ratio was proposed

To the goal of improving the early compressive strength of the mortar including Ground granulated blast furnace slag under low-temperature environment, Industrial byproducts including SiO2 and Al2O3 was fired and than 7% of it was added into Ground granulated blast furnace slag. By checking compressive strength and activity index from different mixing rate, in spite of low strength development than OPC 100%, when using firing powder, the expectation of increasing strength by curing time was affirmative

This study is to compare and analyze the characteristics of blast furnace slag for use in a NPP concrete, strength, drying shrinkage of concrete using fly ash and OPC. Experimental results, the OPC concrete drying shrinkage is the largest and most FA and GS the similar level.

Ground granulated blast furnace slag is known to be much less quality variation compared to the fly ash can be substituted. Have high salt damage resistance, and chemical resistance of concrete with ground granulated blast furnace slag substitution. The case of NPP concrete using fly ash in concrete, and is defined as less than 20% fly ash utilization. In this paper, consider a resistance to freezing-thawing of currently used to concrete in NPP structures and substitutes for ground granulated blast furnace slag

Investigated the factors to effect on the flow of geopolymer mortar based on on ground granulated blast furnace slag in order to develop cementless alkali-activated concrete GGBS.

본 연구는 표준실험체인 전단보강근이 없는 철근콘크리트 보(SSS)와 전단보강근이 있는 철근콘크리트 보(BSS), 성능개선실험체로는 전단보강근이 없는 철근콘크리트 보에 고로슬래그미분말을 혼입한 고인성섬유 복합모르타르를 타설한 실험체(SHF시리즈, SHFSC시리즈)로 총 11개의 실험체를 축소 제작하여 실험을 수행하였다. 실험을 통하여 얻어진 결과를 비교․분석하여 하중-변위, 파괴형태, 최대내력, 전단응력 등을 규명함으로써 구조성능의 개선정도를 평가하였다. 고로슬래그미분말을 혼입한 고인성섬유 복합모르타르를 이용한 철근콘크리트 보 실험체(SHF시리즈, SHFSC시리즈)의 경우 전단보강근이 없는 표준실험체(SSS)보다 전단응력은 각각 26%, 28%, 연성능력은 각각 5.27, 5.75배 증가하는 결과를 나타내었다. 또한, 충분한 연성적인 거동과 안정적인 휨인장 파괴를 나타내었다.

본 연구는 동결융해, 염해 및 중성화가 복합적으로 작용하는 콘크리트 구조물의 내구성능을 평가하기 위하여 일반강도 콘크리트를 대상으로 동결수를 달리하여 동결융해 시험을 실시함으로서 염해와 동결융해 복합작용에 의한 콘크리트의 열화를 평가하였고, 염해, 동결융해 및 중성화의 세가지 열화가 복합적으로 발생되는 복합열화에 대해서는 적절한 평가방법이 부재하여 동결수에 따른 동결융해 시험 후의 시험체에 대하여 중성화 촉진시험을 실시함으로서 복합열화에 의한 콘크리트 내구성능 저하 특성을 평가하고자 하였다. 본 연구를 통하여 동결수의 종류나 물-결합재비 수준과 무관하게 고로슬래그미분말을 사용한 배합의 경우 염해와 동결융해가 동시에 복합적으로 발생되는 환경에서도 우수한 저항성능을 보이는 결과를 나타내므로 동결융해를 포함한 복합열화 환경에서 충분한 내구성 확보를 위해서는 최소한의 설계기준강도의 확보와 고로슬래그미분말 등 적절한 시멘트 결합재의 선정이 무엇보다 중요하다는 결론을 얻었다.