In this study, we utilized a multi-step stabilization method, incorporating dry-oxidation, to produce high-density polyethylene (HDPE)-based activated carbon fibers. This stabilization was achieved through electron-beam irradiation, sulfonation, and dry oxidation. The stabilized fibers were carbonized and activated at 900 ℃. The crystallite characteristics of the activated carbon fibers were observed using X-ray diffraction, and their surface morphologies were analyzed through scanning electron microscopy. The textural properties were analyzed using N2/ 77 K adsorption–desorption isothermal curves. And leveraging the microdomain model, we explored the influence of these stabilization methods on the HDPE-based activated carbon fibers texture properties. The results show that HDPE fibers treated with sulfonation only at 100 ℃ for 60 min were not sufficiently cross-linked and were completely decomposed during the carbonization stage. However, the sulfonated fibers treated with the new dry-oxidation process maintained their shapes and were successfully activated. The specific surface area of the resulting activated carbon fibers was as much as 2000 m2/ g.

본 연구는 고밀도폴리에틸렌 코편을 마스크에 적용 후 MRI 검사에 사용하여 SNR의 변화를 측정하고 만족도를 평가하였다. 연구 방법은 팬텀을 이용하여 HDPE 마스크 적용 전 후의 SNR 측정과 KF 94 마스크 적용 전 후의 SNR 측정을 하였고, 사용한 기법은 T1WI, T2WI, DWI였다. 또한 HDPE 마스크 착용군의 T2 mDixon, 3D T1영상 획득 후 안와와 교뇌의 SNR을 측정하였고, 설문을 통하여 MRI 검사 시 답답함 정도와 호흡의 용이성, HDPE 마스크의 선호도 평가를 하였다. 팬텀 실험 결과 HDPE 마스크 사용 전과 후의 SNR은 유의한 차이가 없었으며(p>0.05), KF 94 마스크는 적용 전 값과 유의한 차이가 있었다(p<0.05). HDPE 마스크 착용군의 SNR 측정 결과에서는 미착용군과 유의한 차이는 없었다(p>0.05). 마스크 착용 후 답답한 정도 측정 결과 착용군은 3.53 ± 0.73, 미착용군은 3.83 ± 0.75이었고, 호흡의 용이성 측정 결과 HDPE 마스크 착용군은 3.1 ± 0.89, 미착용군은 3.27 ± 0.91으로 나타났고, 두 조사 결과 모두 유의한 차이는 없었다(p>0.05). HDPE 마스크의 선호도는 4.48 ± 0.54으로 선호도가 높은 것으로 나타났다. 본 연구 결과 HDPE 마스크는 착용 후에도 MRI 영상의 신호 변화 없이 정확한 검사가 가능하고 환자의 만족도 또한 높게 평가되었기에 검사 중 호흡기 감염 예방을 위해 적극적으로 사용되어야 할 것으로 사료된다.

In this experimental work, the development of a multicomponent binder system based on high density polyethylene (HDPE) and paraffin wax for Powder Injection Molding of Alumina parts was carried out. The optimum composition of the injection mixture was established through mixing torque measurements and a rheological study. The maximum powder loading was 58 vol%. The miscibility of organic components and the optimum injection temperature was evaluated by thermal characterization of binder and feedstock. The thermal debinding cycle was developed on the basis of thermogravimetrical analysis of the binder. After sintering the densities achieved were closed to 98% of the theoretical one.

본 연구의 목적은 저열 시멘트를 활용한 콘크리트와 고밀도 폴리에틸렌을 활용한 친환경 저수조를 평가하는 것이다. 친환경 저수조의 강도와 파괴모드를 평가하기 위하여 콘크리트와 고밀도 폴리에틸렌 복합체의 인장강도 시험, 다양한 종류의 콘크리트 수화열 실험, 다양한 혼화재를 활용한 수화열 실험 등을 수행하였다. 수행결과 전단키가 콘크리트와 고밀도 폴리에틸렌의 복합체로 거동할 수 있는 중요한 역할을 한다는 것을 규명하였고, ㄱ 타입의 전단키가 V 타입보다 40% 이상 인장강도를 증진시킨다는 것을 보여주었다. 연구결과 새로운 친환경 저수조는 기존의 콘크리트 저수조보다 안전성을 개선시키며, 보다 적용성과 활용성이 많은 것으로 기대된다.