In this paper, the mechanical properties according to the rCF weight percent(10, 20, 30, 40, 50wt%) of the rCFRP specimen were evaluated and analyzed. First, to prepare rCFRP specimens, pellets were prepared according to the type of weight percent, and rCFRP tensile specimens according to ASTM D638 were prepared using an injection molding machine. Tensile tests were performed on each of 10 specimens according to weight percent conditions, and tensile strength and modulus of elasticity were calculated. For a detailed analysis of the correlation between the internal structure of the specimen and the mechanical properties, the weight percent to the constituent materials of the rCFRP specimen was calculated using mCT and used for the analysis of mechanical properties. For a more detailed analysis, a detailed analysis of the mechanical properties of rCFRP was performed through the fracture surface analysis of the specimen using FE-SEM.

본 실험에서는 폴리프로필렌를 이용하여 중공사의 형태로 제조되었다. 권취속도를 달리하여 중공사막을 제조하였으며, 코어로는 질소를 사용하였다. 제조된 중공사는 만능재료시험기를 이용하여 응력과 변현율을 측정하였다. 그리고 시차 주사열량계(DSC)를 이용하여 각각의 샘플의 결정화도를 측정하였고, 권취속도와 어닐링 효과에 따른 결정화도의 거동을 조사하였다. 냉연신과 열연신을 거친 중 공사 분리막은 전계방출형주사현미경(FE-SEM)을 이용하여 단면, 표면의 모폴로지를 관찰 하였다.

탄소섬유 한외여과막 및 광촉매 혼성 수처리를 위해 관형 여과막 외부와 원통형 막 모듈 내부 사이 공간에 광촉매를 충전하였다. 광촉매는 PP (polypropylene) 구에 이산화티타늄 분말을 플라즈마 화학증착 공정으로 코팅한 것이다. 휴믹산과 카올린 모사용액을 대상으로 막오염을 최소화하기 위해 10분 주기로 10초 동안 물 역세척을 시행하였다. 기존 결과와 동일하게 휴믹산을 10 mg/L부터 2 mg/L로 변화시킴에 따라, 막오염에 의한 저항 (Rf)이 감소하여 2 mg/L에서 최대 총여과부피 (VT)를 얻었다. 탁도와 휴믹산의 처리효율은 각각 97.1%와 74.2% 이상으로 휴믹산 농도의 영향을 받지 않았다. 그러나 기존 결과에서는 휴믹산의 농도가 증가할수록 휴믹산의 처리효율이 다소 증가하는 경향을 나타냈다.

The main goal of this work is to study the effect of glass fiber volume fraction on the result of tensile test with respect to glass fiber/polypropylene(GF/PP) composites. The tensile test and failure mechanisms of GF/PP composites were investigated in the fiber volume fraction range from 10% to 30%. The tensile strength and the fracture strength increased with the increasing of the fiber volume fraction in the tested range. Fiber pull-out and debonding of this composites increased with the fiber volume fraction in thc tested range. The major failure mechanisms were classified into the debonding, the fiber pull out, the delamination and the matrix deformation.

섬유함유율이 0%, 20% 그리고 30%인 단섬유 GF/PP 복합재료를 사용하여 80℃, 50℃ 그리고 실온에서 인장시험을 통하여 온도의 변화에 대한 파괴강도의 거동을 고찰한 결과는 다음과 같다. 1) 유리섬유로 강화하지 않은 순수 PP보다 유리섬유로 강화한 복합재료의 인장강도가 높게 나타났으며 섬유함유율이 증가할수록 그 값은 높게 나타났다. 2) 동일한 섬유함유율을 가지는 GF/PP 복합재료의 온도변화에 따른 인장강도는 실온의 경우가 가장 높게 나타나고 고온으로 갈수록 그 값이 낮게 나타났다. 3) GF/PP 복합재료의 파괴기구는 온도의 변화에 따라 매트릭스의 변형이 나타났으며 섬유의 풀아웃, 섬유와 매트릭스 사이의 디본딩을 관찰할 수 있었으며, 이와 같은 파괴기구가 종합적으로 상호작용한다고 생각된다.

The critical fracture energy and failure mechanisms of GF/PP composites are investigated in the temperatures range of the ambient temperature to -50℃ The critical fracture energy increase as fiber volume fraction ratio increased The critical fracture energy shows a maximum at ambient temperature and it tends to decrease as temperature goes up. Major failure mechanisms can be classfied such as fiber matrix debonding, fiber pull-out and/or delamination and matrix deformation.

In this paper, internal thermal stresses of the cementitious matrix were evaluated by incorporating polypropylene fibers. By using the temperature heating method specified in KS F 2257-1, the temperatures by a depth were measured. Thermal stress was calculated based on Kodur's thermal stress formula. Different thermal stress behaviors were observed depending on amount of PP fiber. Thas, it will become fundamental data to analyze the thermal stresses behavior of structure members subjected to higher temperature.

폴리비닐알코올 섬유와 폴리에틸렌 섬유 등의 합성 섬유는 고연성 섬유보강 시멘트 복합재료를 제조하는데 성공적으로 사용되고 있다. 폴리프로필렌 섬유 역시 복합재료를 제조하는데 사용되고 있지만, 고연성을 구현하는 목적보다는 고온에 노출된 콘크리트의 내화 성능 향상 목적으로 사용되고 있다. 이 연구에서는 폴리프로필렌 섬유로 보강된 시멘트 복합재료의 성능을 향상시키는 방법에 대하여 논하고자 한다. 폴리프로필렌 섬유보강 시멘트 복합재료의 성능을 평가하기 위하여 5가지 배합을 결정하였다. 1종 보통포틀랜드시멘트 (OPC)와 OPC를 다량 치환한 플라이애시를 결합재로 사용하였고 물-결합재 비는 0.23~0.25이다. 또한 부피비로 2%의 폴리프로필렌 섬유가 사용되었으며, 연성을 향상시킬 목적으로 폴리스틸렌 비드가 사용되었다. 슬럼프, 밀도, 압축강도, 1축 인장 실험을 포함한 일련의 실험을 수행하였으며, 실험결과, 파괴역학, 마이크로역학, 통계이론을 이용하여 폴리프로필렌 섬유보강 시멘트 복합재료의 성능을 향상할 수 있는 것으로 나타났다.

폴리프로필렌섬유보강 시멘트 복합재료와 구조용 합성섬유의 부착특성을 평가하였다. 폴리프로필렌섬유는 0.10%, 0.15% 및 0.20%의 체적비로 적용하여 dog-bone 시험을 실시하였다. 구조용 합성섬유와 폴리프로필렌섬유보강 시멘트 복합재료 사이의 부착강도는 폴리프로필렌섬유의 혼입률이 증가할수록 증가하였으나 0.20% 이상이 되면 감소하였다. 또한 폴리프로필렌섬유의 첨가는 계면인성과 마찰저항을 증가시킨다. 인발시험 후 구조용 합성섬유 표면의 미소구조 분석은 폴리프로필렌섬유의 혼입률이 증가할수록 긁힘 현상이 증가하였다.