In this study, lanthanum boron silicate glasses were prepared with a composition of x Li2O-(60-x)B2O3-5CaO- 5BaO-7ZnO-10SiO2-10La2O3-3Y2O3 where x = 1,3,5,7, and 9 mol%. Each composition was melted in a platinum crucible under atmospheric conditions at 1,400 °C for 2 h. Clear glasses with a transmittance exceeding 85 % were fabricated. Their optical, thermal, and physical properties, such as refractive index, Abbe number, density, glass transition (Tg) and Knoop hardness were studied. The results demonstrated that refractive index was between 1.6859 and 1.6953 at 589.3 nm. The Abbe number was calculated using an equation for 589.3 nm (nd), 656.3 nm (nf) and 486.1 nm (nc) and was observed to be in the range from 57.5 to 62.6. As the Li2O content increased, the glass transition temperature of the optical glass decreased from 608 °C to 564 °C. If glass mold pressing is performed using a material with a low transition temperature and high mechanical strength, then the optical glasses developed in this study can be completely commercialized.

사용후핵연료 파이로프로세싱에서는 방사성 희토류 염화물(RECl3)을 함유한 LiCl-KCl 공융염폐기물이 발생되며, 핫셀시설에서 운영을 목적으로 단순한 형태의 공융염폐기물 처리공정을 개발하는 것이 필요하다. 본 연구에서는, LiCl-KCl 공융염폐기물 내 희토류 핵종 분리/고화공정의 단순화를 목적으로 Li2O-Al2O3-SiO2-B2O3계의 무기합성매질을 이용하여 LiCl-KCl 공융 염 내 희토류 핵종(Nd)을 분리한 후 분리생성물을 바로 고화하는 시험을 실시하였다. 공융염 내 희토류 염화물(NdCl3) 대비 0.67의 무게비에 해당하는 무기합성매질의 양으로도 Nd 핵종을 98wt% 이상 분리할 수 있었고, 이 때 얻은 희토류 핵종 포집생성물은 약 50wt% 수준의 희토류 산화물 함량을 보유하고 있었으며, 이 포집생성물을 화학적 내구성이 우수한 단일상의 균질한 유리고화체로 제조할 수 있었다. 이 결과들은 LiCl-KCl 공융염폐기물 내 희토류 핵종의 분리/고화공정을 단순화하기 위한 방안수립에 활용될 수 있을 것이다.

졸겔법에 의해서 trimethylborate (TMB)/tetraethylorthosilicate (TEOS) 몰비 0.01, 온도 800°C에서 SiO2⋅B2O3가 제조되었다. 그리고 제조된 SiO2⋅B2O3와 PDMS[poly(dimethylsiloxane)]로부터 PDMS-SiO2⋅B2O3 복합막을 제조하고 막의물리화학적 특성을 TG-DTA, FT-IR, BET, X-ray, SEM에 의해 조사하고 그리고 H2와 N2의 투과도와 선택도를 조사하였다.TG-DTA, BET, X-ray, FT-IR 측정에 의하면 SiO2⋅B2O3는 무정형의 다공성 SiO2⋅B2O3였으며, 기공의 평균직경은 37.7821Å, 표면적은 247.6868 m2/g이었다. TGA 측정에 의하면 PDMS 내에 SiO2⋅B2O3가 첨가되었을 때 PDMS-SiO2⋅B2O3 복합막의 열적 안정성은 향상되었다. SEM 관찰에 의하면 SiO2⋅B2O3는 약 1 μm 크기로 PDMS 내에 덩어리 상태로 뭉쳐서 분산되어 있었다. 기체투과실험에 의하면 PDMS 내에 SiO2⋅B2O3 함량이 증가하면 H2와 N2의 투과도는 증가하였고,

The effect of titanium dioxide (TiO2) on the properties of color conversion glasses was examined for glasses based on BaO-ZnO-B2O3-SiO2. One glass sample, containing 25 mol% of each component, was used as a reference; the other three glass samples contained 1, 3, and 5 mol% TiO2, respectively. The four color conversion glass samples were prepared by sintering a mixture of glass frits and a YAG:Ce+ phosphor. The characteristics of the color conversion glass samples, such as luminous efficacy, luminance, CIE (Commission International de I'Eclairage) chromaticity, CCT (Correlated Color Temperature), and CRI (Color Rendering Index) were analyzed according to the PL spectrum. The refractive index of the glass samples was found to increase with the titanium dioxide content. In conclusion, luminous efficacy of color conversion glasses increased as the content of TiO2 was raised in the glass matrix.

In fabricating plasma display panels, the photolithographic process is used to form patterns of barrier ribs with high accuracy and high aspect ratio. It is important in the photolithographic process to control the refractive index of the photosensitive paste. The composition of this paste for photolithography is based on the B2O3-SiO2-Al2O3 glass system, including additives of alkali oxides and rare earth oxides. In this work, we investigated the density, structure and refractive index of glasses based on the B2O3-SiO2-Al2O3 system with the addition of Li2O, K2O, Na2O, CaO, SrO, and MgO. The refractive index of the glasses containing K2O, Na2O and CaO was similar to that of the [BO3] fraction while that of the SrO, MgO and Li2O containing glasses were not correlated with the coordination fraction. The coordination number of the boron atoms was measured by MAS NMR. The refractive index increased with a decrease of molar volume due to the increase in the number of non-bridging oxygen atoms and the polarizability. The lowest refractive index (1.485) in this study was that of the B2O3-SiO2-Al2O3-K2O glass system due to the larger ionic radius of K+. Based on our results, it has been determined that the refractive index of the B2O3-SiO2-Al2O3 system should be controlled by the addition of alkali oxides and alkali earth oxides for proper formation of the photosensitive paste.

졸겔법에 의해 Si(OC2H5/)4-(CH3O)3B-C2H5OH-H2O계로부터 다공성의 SiO2-B2O3 막을 제조하였다. SiO2-B2O3막의 특성을 BET, IR spectrophotometer, X-ray diffractometer, SEM 과 TEM을 사용하여 조사하였다. 700{℃에서 얻어진 SiO2-B2O3 막의 평균 기공직경은 0.0048 mu{m}이고, 표면적은 354.398 m2/g이었으며, 입자의 크기는 7 nm인 무정형의 다공체이었다. SiO2-B2O3 막의 수소/질소 혼합 기체 분리 특성은 기체분리 압력을 달리하여 조사하였다. 25{℃, ΔP 155.15cmHg에서 수소/질소 혼합 기체를 분리하여 본 결과 SiO2-B2O3 막의 수소에 대한 real separation factor(α)는 4.68이었다. 그리고 투과셀의 압력차(ΔP)값이 증가할수록 real separation factor(α), head separation factor(β), tail separation factor((equation omitted))값이 증가하였다.

PDP용 투명유전체 재료로 사용되는 PbO-B2O3-SiO2-Al2O3계의 소성과정 중에서 투명전극 (ITO)과의 반응성 및 광학적, 열적, 전기적 특성을 조사하였다. 본 연구에서 유전체막.두께는 12μm으로, 온도는 550-580˚C에서 소성한 후 여러 물성을 평가하였다 그 결과로, 유전체와 투명전극(ITO)의 반용에서, In 이온이 유전체층으로 확산이동하였으며, Sn 확산은 거의 발생하지 않았다. 선팽창계수, 유전상수, 유리전이온도,광 투과율은 유전체 조성의 PbO 양에 큰 영향을 받았다. PbO양 증가는 선팽창계수와 유전상수를 증가시킨 반면, 유리전이온도와 광 투과율온 저하시켰다. Al2O3/B2O3 비가 증가함에 따라서는 선팽창계수는 감소, 유전상수는 증가, 광 투과율은 감소하였으며, 유리 전이점 변화는 거의 나타나지 않았다.