As the time and cost of body repair can be greatly incurred due to differences in individual technologies, body repair technology should be discussed based on data on general working standards and costs, and as new material technology is applied to the body, continuous learning and experiment on vehicle body repair technology is essential. Since the left and right apron and side members with SPR bonding technology are made of different materials, aluminum and high-strength steel, the restoration of the left and right apron side members should be considered technically, as well as safety and environmental pollution. In this study, we experiment with heterogeneous apron and side members applied with SPR bonding and analyze the results.

이 연구에서는 강관말뚝과 확대기초의 연결을 위한 유공강판 전단연결재를 개발하기 위하여 유공전단키의 형상을 결정하기 위한 인장실험과 유한요소해석을 수행하였다. 즉, 인장시험편과 같은 평판 형태의 유공강판은 펀치 형 돌기와 굴곡형 돌기의 유공전단키를 갖도록 형성하고 이을 원주형 콘크리트 내에 매립하여 인장실험을 수행하였 으며, 실험 결과는 유한요소해석 결과와 비교하였다. 또한, 유한요소해석을 수행하여 적절한 유공전단키의 종류 및 돌기 폭을 결정하였으며, 이를 통해 결정한 굴곡형 유공전단키에 대한 높이를 결정하기 위한 추가 해석을 수행하였 다. 해석 결과, 굴곡형 돌기의 경우에는 전단저항력을 최대로 확보하고 인장력의 저하를 최소화하기 위하여 돌기의 높이를 두께의 2배로 하는 것이 바람직할 것으로 판단된다.

The damage to non-structural elements in buildings has been increasing due to earthquakes. In Korea, post-installed anchors produced overseas have been mainly used for seismic anchorage of non-structural components to structures. Recently, a new cast-in-place concrete insert anchor installed in concrete without drilling has been developed in Korea. In this paper, an experimental study was conducted to evaluate the tensile and shear strengths of the newly developed anchor under monotonic load. The failure modes of the tension specimens were divided into concrete breakout failure and steel failure, and all shear specimens showed steel failure. In both tension and shear, the maximum loads of specimens were greater than the nominal strengths predicted by the concrete design code (KDS 14 20 54). As a result, it is expected that the current code can also be used to calculate the strength of the developed cast-in anchor.

최근 국내 구조물들의 노후화가 진행됨에 따라 구조물 보강과 관련된 연구에 대한 관심이 높아지고 있다. FRP보강은 노후화가 진행되어 성능이 저하된 구조물을 보강하는데 사용되며 주로 유리섬유 및 탄소섬유를 사용한다. 그러나 이 두 가지의 섬유는 경제적으로나 환경적으로나 나쁜 점이 있다. 따라서 본 연구에서는 친환경적이고 내열성이 우수한 현무암 섬유를 구조 용 보강재로 제시하고자 하였다. 또한 본 연구에서는 현무암 섬유에 가장 적합한 수지를 찾기 위하여 에폭시, 폴리에스테르 및 비닐에스테르를 함침 하였다.그 결과, 에폭시 수지를 사용하였을 때 가장 높은 인장 강도 및 탄성계수를 보였으며 전단강도 및 전단탄성계수가 타 수지에 비하여 50%정도 높게 측정되었다. 현무암섬유와 탄소, 유리 섬유의 물성을 비교한 결과 인장강도는 CFRF의 약 60%정도이나 GFRP보다 30%정도 높게 나타내었다.

Tensile load tests were conducted on High-Shear Ring Anchors (HRAs) after shear load had been applied to the HRAs, which had been developed to reduce the number of the anchors. Test variables include the embedment length of the rod and the width of the specimens and a total of 12 specimens were tested. Test results show that the HRAs pulled out due to bond failure or steel failure occurred in case that the HRAs were installed to the members with 300mm or greater width and the embedment length of 160mm (the actual embedment of rod is 140mm) or deeper. Except 4 HRAs showing steel failure of rod, the minimum and average of test-to-prediction by ACI 318-14 ratios are 1.18 and 1.79, respectively. The tensile strength of HRAs, after shear load was applied to the HRAs, can be safely evaluated by the minimum among the concrete breakout strength and bond strength with the actual embedment length of the rod.

확대머리 SD600 고강도 인장철근으로 단부 정착된 SFRC 깊은보의 전단성능을 평가하기 위해 전단 실험을 수행하였다. 실험 변수는 주인장 철근의 단부 정착방법(확대머리 철근, 일자형 철근), 단부 정착길이, 전단보강근 유무 등이다. 전단경간비는 1을 가지는 실험체에 대한 전단실험결과, 모든 실험체는 초기 휨 균열이 발생한 후 경사균열이 진행되면서 최종적으로 압축전단파괴되었다. 확대머리 철근으로 기계적 정착된 실험체들이 일자형 철근 정착에 비하여 5.6∼22.4% 더 큰 전단강도를 나타내었다. 확대머리 철근으로 기계적 정착된 실험체들에 대하여 최대하중의 75%까지는 지압응력이 전체 정착응력의 0.9~17.2%에 도달하였으나, 최대하중 시점에서 지압응력이 전체 정착응력의 22.4%~46%에 도달하여 큰 응력 부담률을 나타내었다. 이를 통하여 확대머리 지압응력에 의한 정착응력 증가가 전단강도에 큰 영향을 미침을 알 수 있다. 실험 전단강도가 실용식에 의한 전단강도의 2.68~4.65 배로 평가되어, 실용식이 전단내력을 안전측으로 평가하였다.

In case of Enlargement method using Post-installed Anchors, mechanical expansion anchors were resisting tensile and shear force of Modular extension structure in exist building. The purpose of this study is to investigate strength of Post-installed Anchor on 16 MPa low strength Concrete under less than standard effective depth(hef). The fracture pattern of the specimens in Pull-out tests was pull-out failure and concrete break out failure. In monotonic load shear tests the fracture pattern was steel failure of anchor and concrete break out failure.

This study was intended to estimate the axial deformation of joint between pavement modules in the rapid-constructible modular pavement system, and to investigate the applicability of two-phase composites for a joint material, which was composed of cement paste, epoxy, or polyurethane as a matrix and sand as particles.