본 연구에서는 건축폐기물로 분류되는 레미콘회수수를 재활용함과 동시에 지구온난화의 주범 인 CO2의 자원화를 위한 시스템의 공정최적화를 진행하였다. 레미콘회수수를 이용한 액상탄산화 반응에 서 가장 중요한 공정은 Ca2+를 용출하는 공정이다. 일정량의 레미콘회수수를 이용해 고순도의 CaCO3을 생성하기 위해 Ca2+ 용출시 질산에 의해 낮아지는 pH 농도를 기준으로 실험을 진행하였으며, CO2는 발전기 배기가스를 이용해 MEA용액에 포집하였다. 본 연구를 통해 1톤의 레미콘회수수에서 최대 11 kg의 CaCO3를 합성할 수 있었다. 생성된 CaCO3 분석결과 제지용으로 사용 가능한 것을 확인하였다.

So many drinking water treatment plants are under various difficulties by new reinforced effluent standards. Since the target turbidity, much higher than annual average, for designing sludge thickener have to be set to confront high turbidity season, the sludge at thickener should be put up for a long time during usual days. So the soluble manganese and chloroform may be formed under the anaerobic environment in the sludge thickener when the sludge retention time is longer with low turbidity. This phenomenon results in difficulties to keep regulatory level of the discharged effluent. For an effort to overcome the problems, a sludge aeration was successfully implemented into the thickening process. As a result, the final effluent quality and sludge volume were much improved; 41 % of manganese, 62 % of chloroform and 35 % of sludge volume. Additionally, effluent quality was improved ; 61 % of Manganese on aeration with pH control and we could make sure of stability effluent quality despite a long sludge retention time. We recommended the standard of installation sludge aeration equipment to nationally supply water treatment plant under effluent water quality problem ; Manganese, Chloroform, etc.

정수장 슬러지는 수 처리 역 세척 과정에서 발생되는데, 기계적인 방법 또는 자연건조방법으로 탈수된 후 주로 해양투기, 매립등의 방법으로 처리한다. 최근에는 런던협약에 의해 해양투기가 상당히 제약을 받고 있다. 탈수된 정수장 슬러지를 위생매립장의 복토재로서의 활용가능성을 파악하기 위하여 실내실험을 통하여 정수장슬러지의 물리 화학적 특성과 지반공학적 특성을 파악하였다. 슬러지의 지반공학적 특성을 향상시키기 위하여 슬러지에 일반토사를 혼합한 시료에 비중계실험, 액 소성한계실험 비중실험, 다짐실험. 일축압측 실험등을 실시하였다. 슬러지에 일반토사를 혼합한 혼합토는 정수장슬러지와 비교하여 최대건조단위증량은 증가하고, 최적함수비는 감소하였고, 최대압축응력과 마찰각을 증가한 반면 점착력은 감소하였다. 미국환경청의 복토재 기준을 확보하기 위해서 슬러지와 일반토사를 3:7로 혼합하여야 하며, 혼합토의 압축강도는 3.6kg/cm2이다.

Composite adsorbents were prepared by mixing water plant sludge with phenolic resin having the ratio of 1 : 1, 1 : 2, and 1 : 3 respectively, curing from 100℃ to 170℃ under N2 atmosphere, and then activating with N2 at 700℃. Thermal property, specific surface area and morphology of the composite adsorbents as well as their precursors were measured by TGA, BET and SEM respectively. Removal efficiency of the composite adsorbents to NH4+ and TOC was compared with those of commercial zeolite and activated carbon. The adsorbents presented very promising TOC removal efficiency of 98%, which was identical level to that of commercial activated carbon while they displayed removal efficiency, only 32%, of NH4+. Therefore, this composite adsorbent considered as the alternative material of commercial activated carbon, used as an expensive removal agent of organic substances and THM in water treatment plant and it also suggested a possibility of practical application in other processes.

This study was conducted to recover the aluminum from water treatment plant sludge containing alumina. The optimum reaction conditions about chlorination of sludge with NH4Cl are as follows: the weight ratio of sludge to NH4Cl is 4, the reaction time is 60min, and the temperature is 300℃. And the result of leaching time test showed that the highest yield of alumina at 160℃ was 96% but the result of leaching test at 160℃ was little better than that of leaching test at 100℃ while the leaching concentration of HCl was 4N. The optimum reaction conditions of chlorinated sludge with NH4Cl, gave the highest yield of 95.41% based on aluminum.

상수도 슬러지(WSPS)를 분화용 배지로 활용하고자 피트모스 와 휠라이트의 혼합상토에 WSPS를 다른 비융로 혼합하여 HederG helix를 식재 60일과 90일 후 생장과 무기원소함량올 조사하였다. 식재 전 배지의 유기물함량은 WSPS가 혼합된 처리구에서 대조구 에 비해 다소 높게 나타났고 유효인산은 전반적으로 WSPS가혼합 된 배지에서 낮게 나타났다. 질산태질소의 함량은 WSPS가 부피비 로 각각 25，50%가 합유된 처리구에서 높게 나타났다. 처리 후 60일과 90일이 경과한 후, 초장과 엽수，지상부 생체중은 대조구와 CW구에서 통계적￡로 유의성이 없었으나 분지수는 CW구가 가 장 높게 나타났다. 식물체 부위별 미량원소 함량은 Fe과 Mn에서 대조구에 비해 WSPS가 혼합된 배지에서 높았고 특히 Fe는 지상 부보다지히부에서 10배 가까이 높게 나타났다. 중금속의 경우，Cd 는 모든 처리구에서 검출되지 않았으며 Pb는 WSPS가 혼합된 배지에서 미량으로 검출되었다. 이상의 결과에서 WSPS는 H. helix 의 재배용 배지로 이용가능성이 높을 것으로 판단된다.