The carbon concentration in the carburized steels was measured by electron probe microanalysis (EPMA) for a range of soluted carbon content in austenite from 0.1 to 1.2 wt%. This study demonstrates the problems in carbon quantitative analysis using the existing calibration curve derived from pure iron (0.008 wt%C) and graphite (99.98 wt%C) as standard specimens. In order to derive an improved calibration curve, carbon homogenization treatment was performed to produce a uniform Kα intensity in selected standard samples (AISI 8620, AISI 4140, AISI 1065, AISI 52100 steel). The trend of detection intensity was identified according to the analysis condition, such as accelerating voltage (10, 15, 30 keV), and beam current (20, 50 nA). The appropriate analysis conditions (15 keV, 20 nA) were derived. When the carbon concentration depth profile of the carburized specimen was measured for a short carburizing time using the improved calibration curve, it proved to be a more reliable and accurate analysis method compared to the conventional analysis method.

A developed molybdenum hybrid-alloyed steel powder is based on a molybdenum prealloyed steel powder to which molybdenum powder particles are diffusion bonded. The sintered compact made of this powder has a finer pore structure than that of the conventional molybdenum prealloyed steel powder, because the ferritic iron phase with a high diffusion coefficient is formed in the sintering necks where molybdenum is concentrated resulting in enhanced sintering. The rolling contact fatigue strength of the sintered and carburized compacts made of this powder improved by a factor of 3.6 compared with that of the conventional powder due to the fine pore structures.

플라즈마 침탄한 저 탄소 Cr-Mo 강(0.176C-1.014Cr-0.387Mo)의 침탄 특성과 피로성질을 고찰하였다. 플라즈만 침탄한 시편의 유효경화깊이는 가스 침탄한 시편에 대해 상대적으로 침타나시간이 짧고 침탄온도가 낮음에도 불구하고 50%정도까지 증가되었다. 플라즈만 침탄시 유효경화깊이의 증가는 표면탄소농도의 증가와 같은 경향을 보였으며, 표면탄소농도의 증가와 같은 경향을 보였으며, 표면탄소농도의 증가율이 침탄시간의 증가에 따라 감소하였다. 플라즈만 침탄간의 피로한도는 가스 침탄강의 경우보다 높았다. 이를 표면근처의 미세구조, 경화깊이 잔류, 오스테나이트와 압축잔류응력으로 조사한 결과 경화깊이와 압축잔류응력의 차이가 거의 없었다. 따라서 플라즈만 침탄의 피로강도 향상은 가스침탄에 비해 표면이 상승층이 저감되어 표면에서의 미소균열의 발생 및 초기 균열 전파과정이 지연 되어진 것으로 판단된다. 파단면 관찰결과 표면에서 균열이 시작되고 플라즈마 침탄의 경우 입내파괴가 현저하였다.