Membrane-based CO2 capture is an energy-saving way to separate CO2 from N2 in post-combustion. Chabazite (Si-CHA) zeolites with a pore size of 0.37 nm × 0.42 nm are expected to separate CO2 from larger N2 (0.364 nm) by recognizing minute size differences. The pore mouth size on the Si-CHA zeolites outer surface was reduced via the chemical vapor deposition (CVD) to increase the molecular sieving effect by disfavoring the penetration of N2. The CVD process was conducted on CHA membranes to improve their CO2/N2 separation performance. Compared to the intact CHA membranes, the CO2/N2 max separation factor for CVD-treated CHA membranes increased by ~2.5 fold under dry conditions and by ~6.4 fold under wet conditions. It is noteworthy that the membrane kept its separation performance without degradation in the presence of H2O.

방사성 폐기물의 주요 성분 중 하나인 Cs의 자연에서 정출되는 제올라이트인 차바자이트 (chabazite)에 대한 흡착 특성을 알아보기 위해 XRD, EPMA, EC, pH, ICP 분석방법을 이용하여 동정 및 화학성분 분석을 하였다. 그리고 추가적으로 양이온 교환능력을 확인하였고 시간과 농도에 따른 Cs 흡착 및 타 양이온(Li+, Na+, K+, Rb+, Sr2+)에 대한 경쟁흡착 실험을 실시하였다. 본 연구에 사용된 차바자이트의 화학식은 Ca1.15Na0.99K1.20Mg0.01Ba0.16Al4.79Si7.21O24였고 Si/Al 비율과 양이온 교환능력은 각각 1.50와 238.1 meq/100 g으로 측정되었다. 시간과 농도에 따른 Cs 흡착 등온 실험결과를 흡착 반 응 속도 모델과 등온 흡착 모델에 적용해본 결과 각각 유사 2차 반응과 Freundlich 모델에 부합하였으 므로 고체 표면에 흡착 물질이 2개 이상의 다중 흡착 층을 이루는 것을 알 수 있으며 모델로부터 유 도되는 상수 값을 통해 차바자이트의 Cs 흡착 능력정도를 평가하였다. 경쟁 흡착 실험 결과 이온의 종류에 따라 이온 교환되어 차바자이트 내에 존재하는 Cs의 몰 분율에서 차이를 보였다. 각 양이온과 세슘과의 액체에서 고체 내로 흡착되는 경쟁 경향이 Na+, Li+, Sr2+, K+ 그리고 Rb+ 순으로 선택성이 있었으며 이는 수화 직경의 순서와 유사한 양상을 보였다. Kielland 도시법을 이용하여 Cs과 타 양이 온의 교환 평형관계를 도시해 보았을 때에는 Sr2+가 가장 선택성이 높았으며 그 다음으로 Na+, Li+, K+, Rb+ 순으로 선택성이 나타났고 모든 타 양이온에 대하여 양의 값을 나타내었다. Kielland 도시법 에서 나타나는 평형상수 값의 순서는 열역학 및 반응 속도론적인 의미를 내포하고 있으므로 수용액에 서 공극 내로 들어가는 Cs은 Sr2+과의 공존 시 선호도가 높다는 것을 알 수 있다. 이는 경쟁하고 있는 수화된 양이온 간의 직경 차이가 원인일 것으로 추측된다. 본 연구 결과는 차바자이트가 높은 Cs 친 화력을 가지는 것을 보여줌으로써 방사성 물질로 오염된 물에서 Cs을 선택적으로 교환할 수 있음을 보여주고 있다.