General D-glass(Dielectric glass) fibers are adaptable to PCBs(Printed circuit boards) because they have a low dielectric constant of about 3.5~4.5. However, very few papers have appeared on the physical characteristics of D-glass fibers. D-glass fibers were fabricated via continuous spinning process using bulk D-glass. In order to fabricate the D-glass, raw materials were put into a Pt crucible, melted at 1650℃ for 2 hrs, and then annealed at 521 ± 10℃ for 2 hrs. We obtained transparent clear glass. The transmittance and adaptable temperature for spinning of the bulk marble glass were characterized using a UV-visible spectrometer and a viscometer. Continuous spinning was carried out using direct melting spinning equipment as a function of the fiberizing temperature in the range of 1368℃ to 1460℃, while the winder speed was between 100 rpm and 200 rpm. We investigated the physical properties of the D-glass fibers. The average diameters of the glass fibers were measured by optical microscope and FE-SEM. The average diameters of the D-glass fibers were 21.36 um at 100 rpm and 34.06 um at 200 rpm. The mechanical properties of the fibers were confirmed using a UTM(Universal materials testing machine). The average tensile strengths of the D-glass fibers were 467.03 MPa at 100 rpm and 522.60 MPa at 200 rpm.

금속 유기 골격체(Metal Organic Framework, 이하 MOF) 종류의 하나인 제올라이트형 이미 다졸레이트 골격체(Zeolitic Imidazolate Framework, 이하 ZIF) 중 ZIF-8은 Zn 금속이온과 imidazole 유기 리간드의 결합으로 이루어져 있다. 본 연구에서는 여러 종류의 용매에서 합성된 ZIF-8의 1차 결정과 2차 입자의 형성이 용매가 가진 특성에 영향을 받는 것을 확인하였다. HBD(hydrogen bond donation) 값이 큰 용매에서 합성된 ZIF-8의 1차 결정은 HBD 값이 작은 용매에서의 것보다 크기가 컸고, 용매의 유전상수의 값이 작을수록 2차 입자의 크기가 큰 ZIF-8이 합성되었다.

본 연구는 아스팔트 콘크리트의 유전율과 공극률의 상관성을 평가하기 위해 수행되었다. 이를 위해 다양한 범위 (0%~20%)의 공극률을 갖는 아스팔트 콘크리트 시편을 제작하였고, 저주파 유전율 측정법인 parallel plate법을 사용하여 아스팔트 콘크리트 시편의 유전율을 측정하였다. 아스팔트 콘크리트 시편의 경우 주파수가 증가함에 따라 유전율은 감소하는 경향을 나타내었고, 사용한 아스팔트 바인더의 종류에 따라 그 감소폭이 다르게 나타났다. 또한 공극률 0%~20% 사이에서 공극률이 증가함에 따라 유전율 값은 선형적으로 감소하는 경향을 보였다. 더불어 아스팔트 콘크리트 시편의 유전율에 대한 온도 및 함수량 영향을 보정하여 유전율에 따른 공극률의 상관식을 제시하였다. 본 연구를 통해 제시된 아스팔트 콘크리트의 유전율과 공극률의 상관식은 현재 국내외에서 사용하고 있는 유전율을 활용한 비파괴 밀도 측정장비의 보정모델로 활용 가능하며, 향후 국내에서 개발하고자 하는 아스팔트 포장 비파괴 밀도 측정장비의 기본적인 알고리즘으로 활용이 가능할 것이다.

[ ] is usually added as shifters in order to move the of to lower temperatures because it is well established that the of decreases linearly with a solid solution of in place of . It is not fully understood yet, however, how influences on the peak value of the dielectric constant at the of . This research reports the effect of addition on εmax at the of ceramics. Based on the chemical composition and the grain size dependence of the dielectric property of ceramics, functionally graded composites were designed and fabricated. Multi-layered composites with a compositional gradient of exhibited a low temperature coefficient and high dielectric constant in a wide temperature range.

플라즈마 화학기상증착법에 의해 증착된 저유전율 SiOF박막의 물성 안정화를 위하여 증착후 N2O플라즈마로 열처리함으로써 그 특성을 평가하였다. SiOF박막은 대기방치 및 열처리에 불안정한 성질을 가진다. SiOF 박막은 박막내의 F-Si-F 결합의 존재 때문에 흡습현상이 발생하며, 박막내의 F함량이 증가함에 따라 수분 흡수가 증가한다. 또한 열처리를 거치면서 F이 탈착되어 박막내의 F함량이 감소한다. N2O플라즈마 열처리는 표면에 얇은 SiON층을 형성시킴으로써 박막을 안정화시키는데 효과적이었다. 그러나 장시간의 N/sun 2/O플라즈마 열처리는 유전율을 크게 증가시킨다. 따라서 N2O플라즈마 열처리에 의한 유전율의 증가없이 물성을 안정화 시키기 위해서는, 대기방치나 열처리에 의한 안정화 효과를 유지하면서 N2O플라즈마 열처리에 의한 유전율의 증가를 최소화시킬 수 있는 공정의 확립이 필요하다.

물과 에탄올의 혼합용액에 HCI을 촉매로하여 금속알콕사이드의 가수분해로부터 코오디어라이트 분말을 제조하였다. 이때 HCI/precursor 몰비로써 촉매의 양을 조절하였다. 건조분말 중의 용매를 제거하기위해 800˚C에서 3시간 하소처리하였다. 이들 하소된 분말에 대하여 시차열분석과 X-선회절분석을 행한 결과-920˚C에서 μ-cordierite, -1030˚C에서 α-cordierite 결정상의 생성을 확인하였다. 또한, 하소분말을 가압성형한 후 1300˚C에서 4시간 열처리한 결과 HCI양에 따라 기공율 19.45-25.45%, 부피비중 2.06-1.70g/㎤, 유전상수 1.38-3.38 범위의 소결체를 얻었다. HCI양이 증가할수록 기공율은 증가한 반면에 비유전상수와 부피비중은 감소하였다.

In this study, an experimental research is conducted to determine the influence of field conditions on the soil dielectric constant in order to evaluate the feasibility of using TDR method as a cavity exploration. Dielectric constant of the ground considering field conditions(e.g. casing and ground disturbance) was measured using TDR method. The results conclude that the dielectric constant of ground tended to decrease with the increase in the water contents and density.