본 연구에서는 탄소나노튜브/화이버/폴리머 복합소재 구조에 대한 재료 물성 및 강성 추정을 다룬다. 수정된 Halpin-Tsai 모델을 적용한 멀티 스케일 해석은 탄소나노튜브의 함유량 비율, CNT 두께-길이 비율, 화이버 부피 함유량, 그리고 화이버 보강각도 변화에 따라서 수행되었다. 본 연구에서 제시한 멀티-스케일 접근방법은 기존 모델을 적용하여 얻은 결과와 비교하여 검증하였다. 매개변수 해석을 통하여 CNT의 적절한 함유량은 적층된 CNTFPC 구조의 구조성능의 향상시킬 수 있는 중요한 특성을 규명하였다.

In order to expand the application of oxide dispersion-strengthened (ODS) steel, a composite material is manufactured by adding mechanically alloyed ODS steel powder to conventional steel and investigated in terms of microstructure and wear properties. For comparison, a commercial automobile part material is also tested. Initial microstructural observations confirm that the composite material with added ODS steel contains i) a pearlitic Fe matrix area and ii) an area with Cr-based carbides and ODS steel particles in the form of a Fe-Fe3C structure. In the commercial material, various hard Co-, Fe-Mo-, and Cr-based particles are present in a pearlitic Fe matrix. Wear testing using the VSR engine simulation wear test confirms that the seatface widths of the composite material with added ODS steel and the commercial material are increased by 24% and 47%, respectively, with wear depths of 0.05 mm and 0.1 mm, respectively. The ODS steel-added composite material shows better wear resistance. Post-wear-testing surface and cross-sectional observations show that particles in the commercial material easily fall off, while the ODS steel-added material has an even, smooth wear surface.

복합재는 높은 비강도와 비강성을 가지고 있어 자동차, 항공기 등 전반적인 산업분야에서 널리 사용되는 재료이다. 우주선의 노즐 부분과 같이 높은 온도뿐만 아니라 높은 압력이 작용하는 환경에서 사용하기 위한 재료로 복합재가 필요하다. 복합재의 물성치를 아는 것은 매우 중요한데 모재(matrix)와 강화섬유(fiber) 각각의 물성치를 수치적으로 대입해 얻는 결과는 실험값과의 오차가 커 예측하는데 있어 더 정확한 방법이 필요할 것이다. 본 연구에서는 유한요소법을 이용한 EDISON용 CASAD solver 프로그램을 활용해 분석하였다. matrix와 fiber의 물성치를 대입해 복합재의 물성치를 구해 실험으로 측정된 물성치, 경험식으로 계산된 물성치와 비교를 하였다.

Compared to steel of the same weight in steel concrete structures, fiber reinforced polymer (FRP) is known to have greater strength and better resistance to corrosion. As such, it is being proposed as an effective structural material. Despite its many advantages, FRP has not been rapidly adopted in civil structures. This is because it is more expensive, prone to brittle fracture, and has weak fire resistance. To examine changes in the mechanical properties of FRP and the effectiveness of fire resistant coating, this study conducted tensile tests on coated and uncoated specimens over varying temperature. Glass fiber has excellent fire resistance since it does not melt or burn at high temperatures. However, epoxy is unable to withstand exposure to temperatures exceeding the transition temperature, thus leading to unsatisfactory structural performance and fire resistance. This study investigated the behavioral changes in FRP by exposing the specimens to temperatures ranging from room temperature (approx. 25℃) to 300℃, so as to improve the fire resistance of epoxy.

Asbestos is being replaced throughout the world among friction materials because of its carcinogenic nature. This has raised an important issue of heat dissipation in the non-asbestos brake pad materials being developed for automobiles etc. It has been found that two of the components i.e. carbon fibres as reinforcement and graphite powder as friction modifier, in the brake pad material, can playa vital role in this direction. The study reports the influence of these modifications on the thermal properties like coefficient of thermal expansion (CTE) and thermal conductivity along with the mechanical properties of nonasbestos brake pad composite samples developed in the laboratory.

서로 다른 기지의 성질을 갖는 재료들을 혼합하여 만든 합성재료의 새로운 물성치는 일반적으로 실험으로 규명하고 있다. 혼합하는 재료들의 체적비에 따라 실험으로 측정한 합성재료의 탄성계수와 포와송비는 그 합성재료로 만들어지는 구조물의 역학적 거동을 예측하는 해석적 모델의 기본자료로 사용된다. 합성재료 탄성물성치의 수치적 예측은 합성재료에 대한 유한요소 모델로 해석한 정적변위와 균질.등방성으로 가정한 모델을 해석한 정적변위와의 차이를 최소화하는 구속적 비선형 최적화기법을 사용하여 수행하였다. 유한요소 모델은 체적비에 따라 혼합물질을 분배하기 용이하도록 제안하였으며 구속조건 및 하중조건은 일축인장에 의한 거동을 예측하도록 설정하였다. 본 논문에서는 고체입자를 섞어 만든 합성재료의 탄성물성치를 예제를 통하여 수치적으로 예측하고 그 결과를 실험결과 및 이론식들과 비교.검토하였다.

This paper describes the hydration heat properties of cement composite different with phase change material (PCM) type. The test results indicated that use of barium materials has more effective to delayed time of hydration of cement composite. On the other hand, strontium based PCM more effective to reduction of hydration heat of cement composite.