The p-type thermoelectric compounds of based doped with 3wt% Te were fabricated by a combination of rapid solidification and spark plasma sintering (SPS) process. The effect of holding time during spark plasma sintering (SPS) on the microstructure and thermoelectric properties were investigated using scanning electron microscope (SEM), X-ray diffraction (XRD) and thermoelectric properties. The powders as solidified consisted of homogeneous thermoelectric phases. The thermoelectric figure of merit measured to be maximum () at the SPS temperature of .

Fe based (FeCSiBPCrMoAl) amorphous powder, which is a composition of iron blast cast slag, were produced by a gas atomization process, and sequently mixed with ductile Cu powder by a mechanical ball milling process. The Fe-based amorphous powders and the Fe-Cu composite powders were compacted by a spark plasma sintering (SPS) process. Densification of the Fe amorphous-Cu composited powders by spark plasma sintering of was occurred through a plastic deformation of the each amorphous powder and Cu phase. The SPS samples milled by AGO-2 under 500 rpm had the best homogeneity of Cu phase and showed the smallest Cu pool size. Micro-Vickers hardness of the as-SPSed specimens was changed with the milling processes.

The with various phases were prepared by simple ex-situ hydrolysis and spark plasma sintering (SPS) process of Al powder. The nano bayerite phase was derived by hydrolysis of commercial powder of Al with micrometer size, whereas the bohemite (AlO(OH)) phase was obtained by hydrolysis of nano Al powder synthesized by pulsed wire evaporation (PWE) method. Compaction as well as dehydration of both nano bayerite and bohemite was carried out simultaneously by SPS method, which is used to fabricate dense powder compacts with a rapid heating rate of per min. under the pressure of 50MPa. After compaction treatment in the temperature ranges from , the bayerite and bohemite phases change into various alumina phases depending on the compaction temperatures. The bayerite shows phase transition of sequences. On the other hand, the bohemite experiences the phase transition from AlO(OH) to It shows AlO(OH) sequences. The compacted at shows a high surface area .

In this study the nanostructured ceramics have been fabricated by the combined application of magnetic pulsed compaction (MPC) and subsequent spark plasma sintering (SPS), and their density and hardness properties were investigated. The prepared by the combined processes showed an increase by in density, approaching the value close to the true density, and an enhancement by in hardness, compared to those fabricated by MPC or static compaction method followed by sintering treatment.

fine powder was synthesized by hydrothermal process from the mixture of titania-hydroxide() and barium hexa-hydroxide () as starting materials. Fine powder(< 100 nm) was made under the reaction conditions of 18,10 atm, 1.5 hr in autoclave and showed cubic structure. The powders were sintered by a spark plasma sintering technique from 1050~115 for 5 min. The grains of sample sintered at 110 were about 0.9 in average size and showed the mixture of cubic and tetragonal structures.