Amorphous In-Ga-Zn-O (a-IGZO) thin film transistors, because of their relatively low mobility, have limits in attempts to fulfill high-end specifications for display backplanes. In-Zn-O (IZO) is a promising semiconductor material for high mobility device applications with excellent transparency to visible light region and low temperature process capability. In this paper, the effects of working pressure on the physical and electrical properties of IZO films and thin film transistors are investigated. The working pressure is modulated from 2 mTorr to 5 mTorr, whereas the other process conditions are fixed. As the working pressure increases, the extracted optical band gap of IZO films gradually decreases. Absorption coefficient spectra indicate that subgap states increase at high working pressure. Furthermore, IZO film fabricated at low working pressure shows smoother surface morphology. As a result, IZO thin film transistors with optimum conditions exhibit excellent switching characteristics with high mobility (≥ 30cm2/Vs) and large on/off ratio.

국내 전체 시설원예에서 파이프 골조로 시공된 비닐하우스가 99.2%이며 구조적으로 취약한 단동형 유리온실이 대부분이다. 이에 현재 국내에서 사용하고 있는 단동형 연통형 단동형 3개로 구성된 배치형 비닐하우스의 지붕면에 대한 피크외압계수에 대해서 알아보고자 한다. 실험결과 단동형이 연동형보다 30%정도 큰 피크외압계수로 분포하고 있었다. 배치형 비닐하우스의 지붕면 피크외압계수도 3개동 모두에서 단동형보다 크게 20-30%정도 크게 분포하고 있었다.

본 실험에서는 리튬 이차 박막전지의 음극물질로 주석 산화물 박막을 RF magnetron sputter을 이용하여 증착하였다. RF power를 2.5w/cm2로 고정시키고, 공정압력을 5mtorr에서 30mtorr까지 변화시키면서 막의 결정성 및 응력 변화, 굴절률 등을 측정하여 주석 산화물 박막의 음극 특성을 조사하였다. 분석한 결과, 압력이 증가함에 따라 증착 속도는 125Å/min에서 58Å/min까지 감소하였으며, 결정 구조는 (110)면에서 (101)면과 (211)면으로 천이됨을 보였다. 또한 막응력은 공정압력 20mtorr를 기준으로 압축응력에서 인장응력으로 바뀌었고, 굴절률도 1.93에서 1.79로 감소하였다. 공정압력변화에 따른 충방 전 시험결과 공정압력 5mtorr에서 가장 큰 가역적 용량(483.91μAh/cm2-μm을 보였으나, 사이클이 진행될수록 사이클 퇴화가 점차 증가하였고, 10mtorr에서는 가역적 용량 및 사이클 특성 모두 좋은 것으로 나타났다. 이는 공정 압력이 감소함에 따라 막의 밀도의 증가로 전기 화학적으로 반응할 수 있는 활물질의 양이 증가한 것으로 생각되며 또한, 사이클 특성은 막응력에 의해 크게 영향을 받는다고 생각된다.