In this study, a MWCNT(multi-wall carbon nanotube) was added to polysulfone(PSf) support layer to improve flux of TFC(thin film composite) RO(reverse osmosis) membrane. Two different kinds of MWCNT were used. Surfaces of some MWCNTs were modified hydrophilically through acid treatment, while those of other MWCNTs were modified through heat treatment to maintain their hydrophobicity. MWCNT/PSf support layer was prepared by adding PSf to the NMP mixed solvent containing 0.1 wt% MWCNTs using a phase inversion method. The surface porosity of the MWCNT/PSf support increased by 42~46% while its surface pore size being maintained. The TFC RO membrane made of MWCNT/PSf support layer showed a 20% flux increase while its salt rejection characteristics is sustained. In addition, the MWCNT/PSf support layer has better mechanical stability than the PSf support layer, there resulting in an increased resistance of flux reduction due to physical pressure.

본 연구에서는 정삼투 중공사막 모듈에서 중공사막의 가닥을 비틀어 배치하였을 때의 효과를 알아보기 위해 CFD 전산 유체 역학 프로그램을 통해 5개의 다른 각도로 비틀린 중공사막 모듈을 설계하고 시뮬레이션하여 비틀리지 않은 모듈과 비교하였다. 실험 결과, 중공사막이 비틀렸을 때, 모듈 내부의 유도 용액의 농도가 비틀리지 않을 때에 비해 고르게 분포하였 다. 모듈 입구의 압력은 중공사막의 비틀림과 관계없이 일정한 값을 보였지만 출구의 압력은 중공사막이 비틀린 정도가 커질 수록 증가하는 추세를 보였다. 출구의 압력이 높아짐에 따라 막 내부의 유체 속도가 감소하고 모듈 체류 시간이 증가하여 막 사이의 물질 교환이 원활하게 이루어질 것으로 예측된다. 이는 결과적으로 막이 비틀려 있을 때의 모듈 플럭스가 투과 수량 이 차지하는 비율이 그렇지 않을 때에 비해 2배 증가하였다.

Pretreatment system of desalination process using seawater reverse osmosis(SWRO) membrane is the most critical step in order to prevent membrane fouling. One of the methods is coagulation-UF membrane process. Coagulation-UF membrane systems have been shown to be very efficient in removing turbidity and non-soluble and colloidal organics contained in the source water for SWRO pretreatment. Ferric salt coagulants are commonly applied in coagulation-UF process for pretreatment of SWRO process. But aluminum salts have not been applied in coagulation-UF pretreatment of SWRO process due to the SWRO membrane fouling by residual aluminum. This study was carried out to see the effect of residual matal salt on SWRO membrane followed by coagulation-UF pretreatment process. Experimental results showed that increased residual aluminum salts by coagulation-UF pretreatment process by using alum lead to the decreased SWRO membrane salt rejection and flux. As the salt rejection and flux of SWRO membrane decreased, the concentration of silica and residual aluminum decreased. However, when adjusting coagulation pH for coagulation-UF pretreatment process, the residual aluminum salt concentration was decreased and SWRO membrane flux was increased.

정삼투 공정(forward osmosis, FO)은 역삼투 공정(reverse osmosis, RO)에 비해 저압으로 운영되므로 오염 제어, 유지 보수, 막 세정 및 잠재적 에너지 저감 측면에서 큰 이점이 있어 다양한 분야에 적용할 수 있는 기술이다. 특히, 정삼투 공정의 막오염층이 비교적 느슨하고 분산된 특성을 가지므로 역삼투 공정과 달리 물리세정만으로도 충분한 막오염 제어가 가능하다. 하지만 기존 연구들의 경우 정삼투 물리세정에 적합한 세정 유속을 적용하지 않아 최적화 운전을 하지 못했다는 한계가 있다. 따라서 이 연구는 경제적인 에너지량으로 높은 효율의 세정을 보일 수 있는 적절한 유속의 정당성 평가를 목적으로 한다. 정삼투 공정 막오염 실험을 8.54 cm/s 순환 유속으로 유지하고 세 가지 세정유속으로 회복률과 SEC(specific energy consumption) 비교 평가하였다. 이 실험의 결과로 2배속 세정이 3배속 세정의 수투과도 회복률 만큼의 높은 효율을 보 이는 동시에, 2배속 세정이 높은 세정효율 및 경제적인 SEC를 보이는 적절한 유속이라는 것을 확인하였다.

기후변화로 인해 가속화되고 있는 충남 지역 가뭄현상에 대응하고 대산 임해산업단지의 증가하는 용수 수요를 만족하기 위해서, K-water에서는 100,000 m3/일 규모 역삼투 해수담수플랜트 건설 사업을 추진하고 있다. 이에 본 연구에서는 해수담수플랜트 운영비용의 70% 이상을 담당하는 역삼투 공정 성능에 영향을 미치는 주요 인자에 대한 성능 분석을 수행하였다. 대산 지역 해수 염분농도 및 수온 변화 조건에서 RO 공정의 전력소모는 2.39 ± 0.13 kWh/m3로 나타났으며, 막여과유속과 회수율이 낮을수록 전력소모가 절감되어 연간 운영비용이 감소하였다. 주요 막 제조사별 고유량 막의 성능 비교 결과, 전량 2단 여과공정(full two pass) 기준 생산수 TDS는 평균 3.84 mg/L로 양호하였고, 전력소모는 2.22 ± 0.13 kWh/m3 수준으로 확인되었다. 역삼투 공정 구성을 전량 2단 여과방식에서 partial 또는 split partial 방식으로 변경함에 따라 전력소모는 최대 0.29 kWh/m3, 막모듈 설치비용은 최대 15.6% 절감 가능할 것으로 기대된다.