        This study was carried out to isolate and identify Salmonella species from poultry slaughterhouses and pork meat processing plants during the period from January 1997 to August 1998, and analyze resistance of antimicrobial agents and plasmid profiles of isolated Salmonella strains. A total of 15 Salmonella strains was isolated from poultry carcasses, swine carcasses, pork meats and cutting boards. Identified Salmonella strains were S. typhimurium, S. heidelberg, S. hilingdon, S. mbandaka, and S. virginia. Ten (66.7%) of 15 Salmonella strains showed resistance to antimicrobial agents and five strains (33.3%) of them were resistant to two or more antimicrobial agents. Plasmids were isolated from three Salmonella isolates which had two or more plasmids.
        4,000원
        3.
        1997.02 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        AI-xSi/ySiC( x:6~18wt%, y: 3~9wt%, SiC 입자크기: 10~28μm) 복합재료를 재용해한 후 항온 유지하고 응고 시킬때 SiC 입자가 몰드의 하부로 침강하는 현상을 계통적으로 조사하였다. AI-Si/SiC 복합재료 용탕을 항온으로 유지하면 입자가 없는 지역은 유지시간이 약 처음 30분 동안 빠르게 증가한다. SiC 입자가 크기가 클수록 SiC입자의 크기가 클수록 SiC입자의 침강속도가 빠르다. 또한 복합재료중 철가한 SiC 입자의 부피분율이 증가하면 입자의 침강속도는 감소한다.
        4,000원
        4.
        1993.12 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        침상의 괴타이트 합성조건을 구하고 Co/가스에 의한 침탄법으로 Fe3C 단상을 얻을 조건을 구하여 그 자기적 특성을 조사한 결과 침상의 괴타이트는 공기 유입량을 1500ml/min, 반응온도 50˚C의 조건하에서 교반속도 500rpm, pH 12.0 이상에서 이상적인 분말을 합성할 수 있었으며 교반속도가 증가할수록 미세하고 입도 분포도 좁고 균일하였다. 탄화반응은 유리탄소를 방지하기 위하여 CO가스와 N2가스를 1:2로 혼입하였으며 550˚C, 60min. 이상의 반응조건하에서 Fe3C단상의 포화자화값은 탄화반응 온도에 관계없이 100/emu/g으로 일정하였으며 보자력은 780 에서 400Oe까지, 각형비는 0.35에서 0.13까지 탄화잔응 온도가 증가할수록 감소하였다.
        4,000원