The effect of sublimable vehicles on the pore structure of Cu fabricated by freeze drying is investigated. The 5 vol% CuO-dispersed slurries with camphene and various camphor-naphthalene compositions are frozen in a Teflon mold at -25oC, followed by sublimation at room temperature. After hydrogen reduction at 300oC and sintering at 600 °C, the green bodies of CuO are completely converted to Cu with various pore structures. The sintered samples prepared using CuO/camphene slurries show large pores that are aligned parallel to the sublimable vehicle growth direction. In addition, a dense microstructure is observed in the bottom section of the specimen where the solidification heat was released, owing to the difference in the solidification behavior of the camphene crystals. The porous Cu shows different pore structures, such as dendritic, rod-like, and plate shaped, depending on the composition of the camphornaphthalene system. The change in pore structure is explained by the crystal growth behavior of primary camphor and eutectic and primary naphthalene. Keywords: Porous Cu, Pore structure

Porous Cu-14 wt% Co with aligned pores is produced by a freeze drying and sintering process. Unidirectional freezing of camphene slurry with CuO-Co3O4 powders is conducted, and pores in the frozen specimens are generated by sublimation of the camphene crystals. The dried bodies are hydrogen-reduced at 500oC and sintered at 800oC for 1 h. The reduction behavior of the CuO-Co3O4 powder mixture is analyzed using a temperature-programmed reduction method in an Ar-10% H2 atmosphere. The sintered bodies show large and aligned parallel pores in the camphene growth direction. In addition, small pores are distributed around the internal walls of the large pores. The size and fraction of the pores decrease as the amount of solid powder added to the slurry increases. The change in pore characteristics according to the amount of the mixed powder is interpreted to be due to the rearrangement and accumulation behavior of the solid particles in the freezing process of the slurry.

The hydrogen reduction behavior of the CuO-Co3O4 powder mixture for the synthesis of the homogeneous Cu-15at%Co composite powder has been investigated. The composite powder is prepared by ball milling the oxide powders, followed by a hydrogen reduction process. The reduction behavior of the ball-milled powder mixture is analyzed by X-ray diffraction (XRD) and temperature-programmed reduction at different heating rates in an Ar-10%H2 atmosphere. The scanning electron microscopy and XRD results reveal that the hydrogen-reduced powder mixture is composed of fine agglomerates of nanosized Cu and Co particles. The hydrogen reduction kinetics is studied by determining the degree of peak shift as a function of the heating rate. The activation energies for the reduction of the oxide powders estimated from the slopes of the Kissinger plots are 58.1 kJ/mol and 65.8 kJ/mol, depending on the reduction reaction: CuO to Cu and Co3O4 to Co, respectively. The measured temperature and activation energy for the reduction of Co3O4 are explained on the basis of the effect of pre-reduced Cu particles.

본 연구에서는 교도소 재소자를 대상으로 반사회적 성향과 우울감이 공존하는 경우 자살 위험성이 높을 가능성이 있는지를 알아보고자 하였다. 이를 위해 본 연구에서는 우울과 반사회적 성향이 공존하는 재소자들의 자살생각, 절망감, 분노감을 포함한 정서특성, 그리고 기질 및 성격 특성의 관계를 조사하고, 자살 생각 위험군을 구분한 뒤 이들의 자살생각을 설명해주는 예측변인을 탐색하였다. 본 연구의 대상자는 충북에 위치한 두 곳의 교도소에 수용된 재소자 중 215 명으로서, 이들에게 Cloninger의 한국판 단축형 기질 및 성격검사(TCI), Beck의 절망감척도, Reynold's 자살생각척도, STAXI 상태-특성 분노척도를 실시하였다. 이들을 Zung의 우울척도(SDS) 점수와 한국판 성격장애 검사(PDQ-4+)의 ASPD(antisocial personality disorder) 하위척도 점수를 기준으로 우울집단, 우울-ASPD집단, ASPD집단, 통제집단으로 구분하여 비교하였다. 그 결과 우울 -ASPD 집단의 특성은 다음과 같았다. 절망감과 자살생각이 네 집단 중 가장 높 았다. TCI 상의 기질/성격특성에서는 자극추구 척도의 하위척도 중 법과 규칙을 어기고 좌절을 주는 상황을 피하려는 성향(NS4)이 높았고, 위험회피의 하위 척도 중 예기불안(HA1)과 불확실성에 대한 두려움(HA2)이 가장 높았으며, 인내력은 가장 낮았고, 자기초월의 하위척도 중 자신을 우주의 일부로 지각하는 연대감(ST2)이 통제집단보다 높았다. 또 정서특성에서는 다른 집단에 비해 특성분노 및 상태분노가 가장 높았고, 분노를 많이 억제하는 동시에 표출하였으며 분노-통제가 낮은 것으로 나타났다. 요약하면, 우울-ASPD 공존 집단은 다른 집단에 비해 자살 관련 위험성이 높으며, 좌절감을 못 견디고 불안과 분노는 높은 반면 인내력이 낮고 분노조절을 못하는 것으로 여겨진다. 단계적 회귀분석결 과, 자살생각은 TCI 기질차원 척도 중 자율성과 인내력, 정서 및 행동특성으로는 특성분노, 절망감, 상태분노, 반사회적 특성, 그리고 우울에 의해 34.7%가 설명되었다. 특히 특성분노의 단독 설명량이 제일 컸는데, 이는 특성분노가 자살 생각에 가장 큰 영향을 미칠 가능성을 시사한다. 특성분노는 우울-ASPD집단에서 가장 높았다.