Positron annihilation lifetime spectroscopy is applied to BaSrFBr:Eu film which is used for the phosphore layer,and afterwards the reliability and self-consistency of source corrections in the positron lifetime spectroscopy is investigated usinga 22Na positron emitter covered by thin foils. The positron lifetime showed no significant change through the various protonirradiation energies. It is unusual that the measurements of the defects indicate that most of the defects were likely to have beengenerated by X-ray radiation. This may have resulted from the Bragg peaks of the proton characteristics. The Bragg peak doesnot affect the defect signals enough to distinguish the lifetimes and intensities in a material that is includes multi-grains. Thelifetime (τ1) associated with positron annihilations in the Ba, Br, and Eu of the sample was about 250ps, and due to theannihilations at F-centers or defects from the irradiated protons in sample, the lifetime (τ2) was about 500ps.

The mechanical property of a phosphore layer was investigated by measuring the resolution (LP/mm) and by positron annihilation spectroscopy and SEM. Image plate samples containing the phosphore layer were irradiated by X-rays in a hospital numerous times over a course of several years. The LP/mm values of a (Ba,Sr)FBr : Eu image plate irradiated by X-rays varied between 2.2 and 2.0 over a period of four years. Coincidence Doppler Broadening (CDB) positron annihilation spectroscopy was used to analyze defect structures. The S parameters of the samples from hospital use varied from 0.6219 to 0.6232. There was a positive relationship between the time of exposure to the X-rays and the S parameters. Most of the defects were found to have been generated by X-rays.

농축 우라늄 UF6로 건식법 중의 하나인 DCP법으로 핵연료 UO2+x 분말을 제조하였다. Rotary kiln 내로 수증기를 주입할 때 일어나는 온도 변화에 따른 UO2+x 분말 특성을 우라늄 분석기, 수분 측정기, SEM 등으로 측정하였다. 그 결과 불소의 함유량은 8ppm을 나타냈고, 수분 함량의 경우 최적화되었음을 알 수 있었다.

This study examines preventive technology that is to control the leak by rebuilding the waterproofing layer using adhesive gel for the damaged area expected to raise any disaster if there are making leakage in an underground structure.

대부분의 대공간 구조물은 도시의 상징물인 동시에 구조물의 용도를 만족하여야 하므로 기초가 구조물의 지지, 형태유지 또는 전도방지, 부력저항 등의 다양한 역할을 갖도록 설계되었다. 이에 따라 여러 형태의 기초가 도입되었는데 본 연구에서는 이중 구조물 형태유지 및 전도방지를 위해 앵커력을 도입한 두가지 월드컵 운동장의 경우를 비교 검토하여 건설공정에서 점검된 앵커력의 변화를 검토하였다. 본 연구에서는 반구형지붕의 바깥방향으로 작용되는 수평력 제어를 위해 시공된 앵커(Case1)와 캔틸레버 지붕의 전도방지를 위한 앵커(Case2) 2가지 사례에 대한 앵커력의 도입과정과 최초 앵커력 도입에 따른 대공간 구조물의 장기거동에 대하여 알아보았다.

본 연구는 풍화암에 근입된 영구 앵커의 극한인발력에 관한 연구를 수행하기 위하여 현장에서 실규모 인발시험을 실시한 실험 결과이다. 현장 실물 실험에서는 정착길이가 다른 4개의 앵커에 대한 하중-변위 곡선으로부터 극한인발력을 산정하였다. 또한, 앵커의 수용 여부를 결정하기 위해 단계별 최대하중에서 15분 동안의 크리프 시험을 실시하여 극한하중까지의 크리프치를 평가하였다. 그리고 풍화암에 근입된 영구 앵커의 파괴메카니즘을 규명하기 위해 지표면에 다이얼게이지를 설치하여 하중 변화에 따른 지반의 파괴 거동 범위를 측정하였다.