A huge amount of de-icing agent is sprayed during winter to promote traffic safety in cold regions, and the quantity of de-icing agent sprayed has increased each year. The main ingredients in commonly used de-icing agents are chlorides, such as calcium chloride(CaCl2) and sodium chloride(NaCl). While calcium chloride is mostly used in Korea and sodium chloride is usually used in the U.S. and Japan, all de-icing agents include chloride ions. The chlorides included in sprayed calcium chloride-based de-icing agents have severe adverse effects, including the corrosion of reinforcing steels through salt damage by infiltrating into road structures, reduced structural performance of pavement or damage to bridge structures, and surface scaling, in combination with freezing damage in winter, as well as water pollution. In addition, the deterioration of paved concrete road surface that occurs after the use of calcium chloride-based de-icing agent accelerates the development of visual problems with traffic structures. Therefore, the present study was performed to prepare an environment-friendly liquid de-icing agent through a reaction between waste organic acids and calcium-based by-products, which are industrial by-products, and to analyze the properties of the de-icing agent in order to evaluate its applicability to road facilities.

The number of areas where slopes is exposed is increasing constantly due to continuous expansion of infrastructure and urban development in our country where is mostly mountainous areas, and the number of man-made disasters is also increasing accordingly. It is necessary to develop new durable seed spraying soil materials that enable stable greening on rock slopes and establish the optimal construction method that is suitable for such materials. Therefore, a basic rearch on a method to replicate the field construction method of seed spraying soil materials indoors, produce and evaluate the specimen was carried out in this study.

Chloride-based deicing materials have been reported as the major culprit behind degradation of performance of structures such as surface deterioration and steel corrosion, leading to active researches on development of eco-friendly deicing materials as countermeasures for such issues. However, these eco-friendly deicing materials suffer the issue of poor economic feasibility compared to existing chloride-based deicing material. In order to secure economic feasibility of eco-friendly deicing materials, this research has developed a new eco-friendly deicing material with calcium-based industrial byproducts and assessed its snow-removing performance.

Korea features mountainous areas, and the exposed slop area is on the rapid rise due to constant spread of national infrastructure and urban development, which leads to accompanied increase of artificial disasters. Thus there is a demand for developing long-lived seed spray materials that will enable stable tree planting and establishing an optimal construction method to suit such a material.

In this study, fluidity and compressive strength characteristics of latex modified mortar was compared with each latex types. From the test result, fluidity of the product "A-a" was most outstanding and the product "B-b" revealed the highest compressive strength. Following this experiment range, when using the produce "B-b" it is considered to be able to secure proper fluidity and strength.

Semi-rigid pavement is one of excellent paving methods adopting merits of asphalt-concrete and concrete paving. However, conventional paving methods were mainly used on the new constructed roads. Therefore, in this research we have examined the possibility of using the semi-rigid pavement on occupied roads. Also, confirmed the early-open possibility of pavement by applying the rapid hardening binding material to semi-rigid pavement.

The durability of Latex modified concrete(LMC) is increased when compared with conventional pavement concrete. But LMC have a several problems. In odrer to improve the problem of LMC, Remicon latex modified concrete(Remicon LMC) was developed. In this study, the durability of Remcion LMC containing extra admixture was compared with latex ratio. From the results, when latex and admixture was mixed in concrete, the micro-pores are decreased. And, the durability of Remicon LMC is increased comparing to conventional concrete.

Concrete shrinkage is happened due to the cement hydration and water evaporation from early ages, and it induces crack of concrete. In this study, the crack resistance of remicon latex-modified concrete was compared with latex and admixture ratio. From the results, if admixture ratio is constant, cracking is delayed when the latex ratio is increased.

1990년대 후반부터 사용된 폴리머 콘크리트로 제작된 맨홀은 이 맨홀이 가지고 있는 다양한 장점 때문에 현재까지 널리 이용되고 있다. 그러나, 고유가 시대로 접어들면서 석유화학 재료의 가격인상과 더불어 폴리머 콘크리트의 제조원가가 상승되고 이에 따른 폴리머 콘크리트의 약점이 대두되고 있다. 따라서, 고가의 폴리머 콘크리트로 제작된 맨홀의 뛰어난 휨강도를 대체할 수 있는 경제적인 시멘트 콘크리트 맨홀의 개발이 요구되어 왔다. 본 연구에서는 비정질 칼슘알루미네이트 (Armorphous calcium aluminate, ACA)계의 속경형 시멘트기술을 기반으로 플라이 애쉬와 고로슬래그, 실리카 퓸, 메타카올린 등의 산업부산물을 이용하여 시멘트의 사용량을 최소화시킴으로써 CO2를 저감시킬 수 있는 친환경적인 맨홀용 고인성 콘크리트를 개발하고자 하였다. 연구결과, 경제적이고 친환경적이면서도 요구성능을 만족시키는 시멘트 콘크리트 맨홀을 개발하였다.

Semi-Rigid Pavement is one of excellent paving methods adopting merits of Ascon and concrete paving. But, it has placed just only normal road pavement. In this case, we have constructed Semi-rigid pavement method at Deck pavement on service bridge and we have estimated Semi-rigid pavement as a new paving method replacing Ascon and concrete pavement.

이 연구에서는 시멘트계 광물로 제조된 그라우트의 사용에 의해 발생되는 환경문제인 pH의 증가와 중금속오염을 MC계와 킬레이트고분자를 이용하여 평가하고자 하였다. 그라우트 재료로 보통포틀랜드시멘트와 슬래그시멘트를 사용하였고 급결재로 칼슘알루미네이트계 급결성재료의 혼합물을 사용하였으며, 중금속과 pH의 발생을 방지하기 위해 증점제를 사용하였다. 측정결과, 킬레이트고분자를 사용할 경우에 그라우트에 의한 pH의 증가가 최소화되었으며 중금속(Cr6+)은 용출되지 않았다. 그 이외의 경우에는 pH의 증가와 중금속 용출이 뚜렷이 증가하였다. 또한, 재령에 따른 중금속 발생량은 용출시험 1일에서 전 용출량의 약 97% 이상이 용출되었고 이후는 추가 발생되지 않는 것으로 나타났다. 이 연구의 결과로부터 pH의 증가와 Cr6+과 같은 중금속의 용출을 제어하기 위해서 BSC와 킬레이트고분자를 사용하는 것이 아주 유용함을 알 수 있었다.

세계적인 고유가의 영향으로 석유 소비가 높은 산업의 생산성은 현저히 저하되었다. 고강도 PHC 파일 중 AC 방식은 2차례의 증기양생 공정을 거쳐 제조되고 있으며, 이는 제품의 제조원가에 심각한 상승을 초래하고 있다. 다른 형식의 파일 제조 공정인 NAC 방식은 1차례의 증기양생을 함으로써 제조 원가가 절감되는 장점이 있지만, 초기 강도가 AC 방식보다 저하되기 때문에 약3일 정도의 양생기간을 거쳐 출하되고 있으며, 양생기간에 따른 제품 재고의 증가를 피할 수 없으므로 이는 제조원가 상승의 요인으로 작용하고 있다. AC 방식은 양생 직후, 즉시 출하되며 현장 도입 (항타현장 등) 시 파손 등의 문제가 발생되지 않으나, NAC의 경우는 최소 3일의 양생기간을 거쳐 강도 80 MPa이상을 발현 후 현장에 출하된다. 따라서, NAC는 종류별 적정 재고유지 비용의 증가와 강도부족 시 현장에서 파손이 발생되는 문제점을 안고 있다. 본 연구에서는 NAC 방식의 PHC 파일에 대하여 AC 방식과 동등한 1일 강도를 발현하기 위한 배합특성 연구를 수행하였고, 원재료 변화에 따른 강도 특성도 파악하였다.

이 연구에서는 프리캐스트 콘크리트용으로 공장에서 생산되며 그 동안 국내에서 많이 사용되어온 음이온계 계면활성제의 일종인 나프탈렌 설폰산염계(Poly-Naphthalene Sulfonate Type) 혼화제와 국내 J사에서 개발된 조강형 폴리카본산계(Polycarboxilic Type) 혼화제인 WF2000의 성능을 평가하였다. 실험결과에 의하면, WF2000은 PNS계보다 20% 줄어든 사용량에도 제품이 가지고 있는 높은 감수율과 고온에서 콘크리트 응결의 촉진효과 및 우수한 분산작용으로 인하여 작업성의 개선되었으며 PHC 파일의 조기강도와 장기강도 발현에 유리하였다. 그리고 감수력과 유지력의 조절이 가능하여 원재료의 변동및 환경조건의 변화에 적절한 대응이 가능한 혼화제로 하절기의 생산성과 작업성 저하 그리고 성형성 불량의 문제 및 동절기의응결지연으로 인한 조기강도의 저하에 대한 문제 해결 등에 유리하였다.