This study tried to investigate the difference of the legibility in different age groups (young and old) with same near visual acuity and to provide preliminary guidelines for the text sizes in the pesticides products based on the legibility experiments. To achieve the objective, legibility evaluation experiments were conducted to test the effects of different age(20s, 50-60s), gender, font type(thick gothic-type and fine gothic-type), thickness (plain and bold), and number of syllables(2 and 3 syllables) in the same near visual acuity(0.6). The results showed that legibility 50s was higher than 20s. And 20s are appealed higher discomfort than 50s. Considering these experimental results, it was recommended that the 14 pt or larger characters (100% readable size) should be used the important information such as toxicity, and the minimum character size was 7 pt (50% readable size) for other information.

본 연구에서는 용액 캐스팅법을 이용하여 각기 다른 함량의 VMT가 첨가된 SPAES/VMT 복합막이 제조되었다. SPAES 매트릭스 내의 VMT입자 분산은 전자주사현미경으로 관찰된 평균분포에 의해 확인되었다. 1 wt%보다 적은 함량을 포함한 복합막은 고분자 매트릭스 내에 좋은 분산성을 나타내어 막의 상부층과 하부층에 매끈한 표면을 가졌다. 복합막의 함수율은 온도가 증가함에 따라 급격하게 증가되었으며 VMT는 높은 이온교환능력으로 인하여 강한 수분친화도를 가짐으로 인해 높은 모든 흡착된 수분은 bound water인 것으로 확인하였다. VMT의 함량이 1 wt%보다 적게 첨가된 복합막에서 증가된 이온전도도와 낮아진 메탄올 투과도를 확인할 수 있었다. 모든 복합막 중에서 SPAES/VMT 1.0 wt% 복합막은 선택도 측면에서 가장 뛰어난 연료전지 성능을 가졌으며 Nafion 112과 비교하여 두배 이상 우수한 값을 나타내었다. 이것은 SPAES/VMT 1.0 wt% 복합막이 직접메탄올 연료전지의 구동을 위한 가장 우수한 조건이 될것이라 사료된다.

본 연구에서는 셀룰로오스 트리아세테이트(CTA)를 사용한 loose RO 중공사 막이 상전환 법으로 제조되었고 이들의 수처리 특성이 평가되었다. 1,4-dioxane과 리튬클로라이드(LiCl)는 각각 스킨층 형성제와 기공 형성제로 사용되었다. 제조된 CTA 중공사막의 특성을 알아보기 위하여 전자주사현미경을 통하여 모폴로지를 관찰하였고, 수투과도 및 염 제거율, 내염소성 테스트, 그리고 분획분자량을 측정하였다. CTA/NMP/1,4-dioxane = 18/72/10 (wt%) 에어갭 30 cm의 중공사 분리막의 경우 20.5 L/m2hr의 수투과도와 60%의 염 제거율, NaOCl 10,000 ppm/hr의 내염소성 및 약 5,000 Da값의 MWCO를 나타내는 우수한 특성의 loose RO 막이 제조되었다.

본 연구에서는 연료전지용 강화 복합막 지지체 제조를 위해 높은 다공성을 가지는 PVdF 평막을 제조하였다. 높은 다공도로 인한 낮은 기계적 강도를 보완하기 위한 방법으로 나노 사이즈의 laponite를 막 내에 분산시켰다. 제조된 PVdF/Laponite 복합막의 모폴로지 및 다공도는 SEM 분석 및 무게 중량법을 사용하여 평가하였고, 60% 이상의 다공도를 보였다. 첨가된 laponite 함량에 따른 막의 열적 안정성은 105℃, 135℃에서의 수축률을 이용하여 평가하였으며, laponite 함량이 5%일 때 135℃에서 MD와 TD방향으로의 열 수축률 2~3%와 2~3.5%를 나타내었다. Laponite 첨가 후 막의 기계적 강도가 향상되었으며, 순수 PVdF 막에 비해 약 30%의 모듈러스 증가를 나타내었다.

This study surveyed the reading discomforts and the reasons for discomfortable reading of the safety and health information (texts and icons) presented on the agricultural vehicles/machines, pesticides, fertilizers, and feeds. Eighty seven people residing in rural area participated in the survey interview. Questionnaire survey showed that the most discomfortable product in reading the texts was pesticides. Forty three (49%) among participants had very-discomfortable or discomfortable in reading the texts used in the label of pesticides, and the main reason for the discomfort was small text size. The reading discomforts in reading the texts (varied from 4 point to 19 point and presented in 50 cm reading distance) showed different pattern according to the age groups. Three age groups (50s, 60s and older than 70s) showed a similar discomfort pattern, but different from the group of 30s and 40s. Forty four people (51%) had a problem in understanding the meaning of the icons and the main reasons were the small size and the difficulty in inferring the meaning of the icons. Thus, the more detailed and practical guidelines for the presentation format, particularly about the text heights and the size of icons, are required. Also, more comprehensive research is needed to investigate the readability and legibility of texts and icons.

본 연구에서는 연료전지용 전해질 복합체용 지지체 막을 저가의 우수한 기계적 열적 안정성을 가지는 Polysulfone으로 상전이 법을 이용하여 제조하였다. 제조된 막을 이용하여 농도변화와 노출시간의 변화에 따른 열 수축율, 통기도, 모폴로지, 기계적 물성 및 다공도를 측정하였다. 모폴로지를 조절하기 위해 공기 중 노출 시간과 고분자 농도가 제어되었으며, 제조된 막은 고분자 농도 변화에 관계없이 모두 스폰지 구조를 나타내었다. 고분자의 농도가 증가함에 따라 기계적 열적 안정성은 증가하였지만, 다공도는 감소하는 결과를 보였다. 실험결과 20 wt%의 PSf 고분자 용액을 사용하여 2분의 노출시간을 두고 제조된 고분자 막에서 연료전지용 복합막으로 사용되기 위한 충분한 다공도(80%)와 기계적(tensile : 1.3 MPa), 열적(MD, TD shrinkgage < 1%) 안정성을 나타내었다.

전 세계적으로 물 부족 문제를 해결하기 위한 한 가지 대안으로서 해수 담수화 기술이 높은 관심을 받고 있다. 본 연구에서는 해수 담수화를 위한 고효율 저에너지 소모 공정으로 떠오르고 있는 역삼투막의 제조를 위해 cellulose triacetate(CTA)의 적용 가능성을 살피고자 하였다. 염소에 대한 안정성과 유기물에 대한 저항성을 가지는 CTA를 사용하여 막을 제조할 시 아세틸화도, 용매, 첨가제와 같은 제막 조성의 변화가 막의 성능에 미치는 것으로 나타난다. 높은 아세틸화도와 CTA의 용매인 다이옥산과 아세톤의 비에서 다이옥산의 함량이 높을수록 높은 유량과 염 제거율을 가지는 막의 제조가 가능하다. 첨가제로는 acetic acid와 maleic acid가 선호된다. 실제 해수 담수화 플랜트에 상용화된 CTA 막(HOLLOSEPⓇ)을 적용해 본 결과 다른 화학적 처리 없이 계속적인 염소 처리만으로 장기간 안정된 유량과 수질을 나타낸다.

오늘날 대부분의 공압시스템에 압축공기 드라이어가 설치되어 있는데 이는 공압장치가 적절히 그리고 신뢰성 있게 작동되기 위해서는 제습된 공기를 사용해야 할 필요가 있을 뿐 아니라 이외에도 많은 이점을 더 가지고 있기 때문이다. 현재 사용되고 있는 압축공기드라이어는 전력이나, 흡착제의 사용으로 경제성이 떨어지며, 냉매제 등 환경적인 제약을 받고 있다. Membrane dryer는 경제적, 환경 친화적으로 이로우며, 각 산업체 뿐만 아니라 제습기능과 정수 기능이 합쳐진 에어정수기의 새로운 응용으로 물이 부족한 열대 우림지역에서 사용될 수 있다.