화재시 콘크리트 구조물의 노출 온도를 판단하여 화재 피해 범위를 신속하게 판단할 수 있는 무기질 변온색소를 포함한 시멘트의 개발을 목적으로 한다. 400℃의 온도에 노출된 콘크리트는 물리·화학적 변화에 의해 내구성과 내하력이 감소한다. 따라서 400℃ 온도에 노출 유무를 확인하기 위해 400℃의 온도에서 보라색에서 흰색으로 변하는 망간바이롤렛 변온색소를 사용하여 무기질 시멘트를 제조하였다. 제조된 시멘트는 400℃에서 색상의 변화와 함께 30분과 60분 이상의 노출시간도 판단할 수 있는 특징을 나타내었다.

In this study, the changes in compressive strength of steel tubular short columns with local corrosion is investigated using a finite element approach. The dimensions of the local corrosion are defined by its depth (0, 1.5, 3, 4.5 and 6 mm), height (0, 20, 40, 60, 80, 100, 120, 140, 160 and 180 mm), circumference (0, 90, 180, 270 and 360°) and location of damage along the steel tubular short column. There are 42 finite element models executed in this study that are categorized as Type A, Type B and Type C specimens. The results of the finite element models were compared against the previous experimental tests for model validation. Moreover, a parametric study was used to study the effect of the corrosion depth, height and circumference to the compressive strength of a steel tubular short column. Comparing the results of the finite element analysis, experimental and calculated compressive strengths, the percentage error is found to be within 10%.

This study investigates the coating deterioration of water-borne inorganic zine under marine environment. In order to evaluate the corrosion environment at installed site, the corrosion currents were measured by atmospheric corrosion monitoring(ACM) sensor. The deterioration grade of water-borne inorganic zine was investigated by visual inspection method depending on ASTM D610. The deterioration grade of structural member was compared based on corrosion environment such as wet time, amount of deposited salt etc.

In this study, compressive tests were carried out on seamless circular tubular short columns with corrosion-damaged end, and investigated change in compressive strength of columns with local corrosion at the end. Local corrosion was artificially introduced by milling machine, and differed in corrosion depth (0, 1.5, 3, 4.5 mm), corrosion height (0, 20, 60, 120 mm), and corrosion circumference (0, 90, 180, 360˚ ). As a result, the compressive loads were linearly decreased with increasing of corrosion degrees, and a quantitative evaluation for residual compressive strength of seamless circular tubular short column with corrosion-damaged end was suggested by using corroded volume loss ratio.

Thermal spray coatings and organic coatings are often individually used in corrosion protection of steel structures. Duplex coating systems of thermally sprayed metal coating combination with organic coating represent a new generic type of coatings on offshore steel structures under the highly corrosive environments. In this study, weathering test were carried out on four types of duplex coated specimens; thermally sprayed metals of zinc, zinc-aluminum alloy, aluminum and aluminum-magnesium alloy in combination with painting of acrylic urethane. From the test results, weathering performance of the duplex coating systems were evaluated.

강구조물은 주로 도장에 의해 방식처리 되고 있지만, 장기간 사용함에 따라 강재표면에 부식손상이 발생하게 된다. 이러한 부식손상은 단면감소와 이로 인한 좌굴내하력을 저하시킬 우려가 있다. 현재 다양한 등단면형상과 지지조건에 대한 좌굴강도 추정식 및 설계식이 제안되어 있으나, 부식손상으로 인한 불규칙한 변단면 강부재의 축압축 좌굴강도 평가법은 아직 확립되어 있지 않다. 본 연구에서는 부식 손상된 가시설 강부재에서 절취한 강재시편의 축압축 좌굴실험을 실시하여, 부식강재의 좌굴강도 평가에 대한 기초적 연구를 수행하였다. 본 실험에서는 먼저 가시설 주형보의 웨브로부터 시편 지지길이를 200, 300, 400, 500, 600mm로 달리한 5종류 시편을 각각 2개씩 총 10개의 강재시편을 절취하고, 화학적 방법에 의해 녹을 제거하였다. 그리고 3차원 광학 스캐너를 이용하여 1×1mm 간격으로 표면형상을 측정하여, 각 시편의 잔존두께를 산출하였다. 그리고 10개의 부식 손상된 시편과 부식 손상되지 않은 무부식 시편 12개를 양단 완전고정지지 조건하에서 축압축 좌굴실험을 실시하여, 부식두께감소량 및 시편의 표면형상과 축압축 좌굴강도와의 상관관계를 분석하였다. 그 결과, 부식 손상정도에 상관없는 무부식 등단면 강재와 동일하게 좌굴강도를 평가할 수 있는 불규칙 변단면 부식강재의 폭방향평균 최소두께 또는 평균잔존두께와 표준편차의 차로 계산되는 유효두께를 적용하여 축압축 좌굴강도을 추정할 수 있음을 제안하였다. 또한 이러한 결과를 실무에도 적용할 수 있도록 실용적인 부식강재의 잔존두께 측정간격도 제시하였다.