This research proposed MPC (Magnesia Phosphate Composite) mortar as a rapid repair material. But because this rapid reactivity inherently has issues related to microcracking caused by expansion and reaction heat, retarder and fibers are proposed to be used to control the hardening rate and cracking.

In this study, It was purpose to provide preliminary data for extension of the applicability of deep corrugated steel plate composite members by steel grade and shear reinforcement method. From the result of flexural test on deep corrugated plates composite members using GR40 and SS590, positive moment capacity was increased about 28% by SS590 steel. But to change steel grade was proved to have insignificant effects for increasement of negative moment capacity. In the moment test result of same overlapping length, Increasement rate of positive and negative moment capacity was not significantly improved by increasing the number of bolt. It was estimated to be due to the characteristics of bolt connection such as distance between centers of bolts, edge distance of bolt. In the test result on the spacing of shear reinforcement, positive moment capacity was increased and deformation of negative moment was reduced as the distance decrease. In the test result on the shape of shear reinforcement, positive and negative moment resistance was increased about 2% ~ 7% by U shaped shear reinforcement. In conclusion It was estimated that moment capacity of deep corrugated steel plate composite members are depend on steel grade of deep corrugated steel plate, spacing of shear reinforcement and reinforcing bar.

This research proposed MPC (Magnesia Phosphate Composite) mortar as a rapid repair material. But because this rapid reactivity inherently has issues related to microcracking caused by expansion and reaction heat, retarder and fibers are proposed to be used to control the hardening rate and cracking

본 연구에서는 반구형과 평탄형의 비상체를 이용하여 일반콘크리트와 섬유보강콘크리트에 충격시험을 진행한 후 파괴깊이와 형 태, 파괴직경, 배면의 인장변형을 평가하였다. 선단면적이 작을수록 충격력의 집중에 의해 파괴깊이는 크고 표면파괴 직경은 작게 되는 것으로 확인되었다. 반면에 선단면적이 클수록 파괴깊이는 작지만 표면파괴직경은 크게 되었다. 일반콘크리트와 섬유보강 콘크리트에서 유사한 표 면파괴와 배면변형이 발생하였으나 인장변형의 크기는 일반콘크리트에 비해 섬유보강 콘크리트가 작은 것으로 나타났다. 또한, 비상체의 선 단형상에 따른 표면관입의 형태와 배면의 인장변형 사이에 직접적인 연관이 있는 것으로 사료된다. 따라서 콘크리트의 배면박리한계두께 예 측 시에는 표면관입깊이뿐만 아니라 배면의 변형거동 또한 고려할 필요성이 있을 것으로 사료된다.

It is difficult to predict scabbing limit thickness of fiber reinforced concrete, because existing formulas are not consider fiber reinforcing effect. So, In this study, obtaining the fiber reinforced factor and factors are applied to Modified NDRC formula. As results, it was possible to make accurate prediction for scabbing limit thickness of fiber reinforced concrete.

The purpose of this study was to evaluate the dynamic mechanical properties of fiber reinforced cement composite according to the strain rate. Experiment result, the compressive strength was improved by increase the strain rate. But strain at the peak stress and elastic modulus was not affected by the strain rate.

Rebound hammer test, SonReb method and concrete core test are most useful testing methods for estimate the concrete compressive strength of deteriorated concrete structures. But the accuracy of the NDE results on the existing structures could be reduced by the effects of the uncertainty of nondestructive test methods, material effects by aging and carbonation, and mechanical damage by drilling of core. In this study, empirical procedure for verifying the in-situ compressive strength of concrete is suggested through the probabilistic analysis on the 268 data of rebound and ultra-pulse velocity and core strengths obtained from 106 bridges. To enhance the accuracy of predicted concrete strength, the coefficients of core strength, and surface hardness caused by ageing or carbonation was adopted. From the results, the proposed equation by KISTEC and the estimation procedures proposed by authors is reliable than previously suggested equation and correction coefficient.

본 논문의 주 목적은 ｢J. 알프레드 프루프록의 사랑 노래｣에 나타 난 근대성과 시간의 의제가 지닌 중요성을 탐구하는 것이다. 산업화 와 도시화의 결과로 인간소외 현상이 심화되는 후기 근대의 도시로 부터 탈주하고자 하는 프루프록은 대립적인 인간관계가 해소된 마법 화된 시공간을 꿈꾼다. ‘상상적인 동일시’를 통해 구성된 이 세계는 기본적으로 여성적인 영역으로, 방안의 여인들로 대표되는 이 공간 에서는 교감과 친밀성을 바탕으로 하는 인간관계가 유지되고 있다. 또한 프루프록은 동일한 것의 반복을 특징으로 하는 근대의 일상적 시간을 특이성과 우발성이 충만한 차이의 시간으로 대체하고자 한 다. 하지만, 프루프록을 표준화하고 사물화하는 근대성의 시선의 회 귀와 더불어 그는 인간의 시간이 중단된 신화적 세계에 감금되며, 이것은 사회적 존재로서의 프루프록의 상징적 죽음을 의미한다.

Shock wave caused by the high-velocity impact causing the tensile strain and stress on the rear side. When the tensile strain and stress exceeds the tensile strength of the concrete, scabbing and perforation were occurred. The strain on the rear side was reduced due to improvement of the tensile strength by fiber reinforcement.

Thin plate amorphous steel fiber has more tensile strength and corrosion resistance than general steel fiber, and it has different fiber direction by casting direction. In this study, evaluating impact resistance and sectional crack characteristic of amorphous steel fiber-reinforced cement composites by casting direction.

Recently corrugated steel member filled with concrete has been applied to various construction structures. In this study, the compressive strength was evaluated based on the number of bolt joints of corrugated steel. And compressive strength was also evaluated according to the shape and spacing of the steel rebar to improve the performance of the corrugated plates.

In this study, rear strain behavior of concrete panel considering the projectile nose shape was evaluated. It was considered that penetration and scabbing properties are different by each projectile nose shape. so it should be taken into account the rear strain behavior by projectile nose shape, when predicting scabbing, perforation of concrete by projectile impact.

저자들은 비파괴시험에 의한 고강도콘크리트의 강도 예측식을 제안하기 위하여 실험적 연구를 수행하였다. 본 연구에서 사용된 콘 크리트의 설계압축강도는 40~80 MPa 범위이며, 압축공시체를 제작하여 반발경도법과 초음파 속도법으로 실험한후 KS기준에 따라 압축강도 실험을 실시하였다. 실험결과는 기존의 연구자들에 의하여 제안된 다양한 실험예측식들과 비교분석하였다. 실험결과 고강도 콘크리트에서도 반발경도법과 초음파속도법의 경우 간편성과 신뢰성에 있어 콘크리트 강도를 측정하기에 충분한 유용성을 확보한 것을 확인할 수 있었다. 기 존식들과의 비교를 통하여 고강도 콘크리트에 적합한 강도예측식을 제안하였으며, 실험결과에 대한 충분한 신뢰성을 확보한 것으로 판단되 어, 향후 고강도 콘크리트 구조물에 적용할 수 있을 것으로 판단된다.

콘크리트의 강도를 평가하기 위하여 반발경도법과 초음파속도법이 폭넓게 사용되고 있다. 그러나 재료의 상태뿐만 아니라 콘크리 트의 재령, 성숙도 및 손상도 등에 따라 예측강도와 현장의 실제강도가 차이가 발생하게 된다. 표준공시체와 현장에서 드릴링에 의하여 채취하 는 코어공시체의 압축강도는 드릴링하는 동안 기계에 의한 교란이 발생하여 압축강도에 영향을 미치게 된다. 또한 반발경도 및 초음파속도의 경우에도 콘크리트의 재령 및 성숙도가 변화함에 따라 표면의 경도와 내부 미세조직의 변화에 의해서도 변화하게 된다. 저자들은 재령와 코어 의 영향을 비파과시험결과에 반영하기 위하여 실험을 실시하였으며, 코어 및 콘크리트 재령에 의한 영향을 압축강도 실험 및 예측결과와 비교 분석하였다.

When the concrete is subjected to impact of the projectile, compressive stress wave is transmitted to the rear side. When the compressive stress wave reached the rear side, is was reflected as a tensile wave. And, when the tensile stress in the concrete matrix exceeded the dynamic tensile strength, crack in the concrete was occurred.

Fracture behavior of concrete subjected to dynamic loading is affected by loading rate and strain rate. In this study, compressive strength properties according to strain rate of fiber reinforced concrete by rapid loading with 500ton rapid loading test machine was analyzed.

Authors investigated the fatigue bond performance on the grouted joint connection of wind tower. High strength cementeous grout has 140MPa of a compressive strength was incerted in the gap of small scaled steel tube simulated the wind tower joint. The stress level was 65 and 74% of static strength that is 35MPa, respectevely. From the test, each specimens endured the repeated loads up to 2,000,000 cycles.

In this study, rear failure properties of fiber reinforced concrete considering projectile type was evaluated. It was considered that scabbing of Flat nose projectile reduced more than sperical nose projectile by dispersion of impact force.

본 연구는 폴리비닐 알코올 섬유 및 강섬유를 체적비율로 1.5% 혼입한 고인성 섬유보강 시멘트복합체에 대한 비상체의 고속충돌시험을 실시하고, 충돌조건에 따른 파괴특성을 실험적으로 검토하는 것을 목적으로 하였다. 비상체의 충돌에 의한 고인성 섬유보강 시멘트복합체의 파괴특성을 평가하기 위하여 화약압력식 충격시험장치를 활용하였으며, 충돌속도의 범위는 약 150 ~ 1,000m/s로 설정하였다. 파괴특성에 대한 평가결과, 고인성 섬유보강 시멘트복합체는 섬유를 혼입하지 않은 Plain시험체의 약 3배 이상의 비상체 운동에너지가 작용하는 범위에서도 표면관입의 파괴등급으로 평가되었으며, 시험체가 파단되지 않는 내충격성능이 확인 되었다. 또한, 충돌시험 전후에 대한 시험체의 질량감소율의 경우, Plain시험체는 비상체의 운동에너지의 증가율과 비례적인 관계를 보였지만, 고인성 섬유보강 시멘트복합체는 비상체의 운동에너지의 영향을 크게 받지 않는 것으로 나타났다. 특히, 이와 같은 경향은 시험체 배면의 파괴특성과 밀접한 관계를 가지며, S시험체에 비해 PVA시험체의 배면박리 억제효율이 큰 것으로 평가되었다. 한편, 국부손상에 대한 표면관입깊이 및 배면박리깊이의 관계를 검토한 결과, 고인성 섬유보강 시멘트복합체는 Plain과 달리 시험체 단면의 중앙선을 기준으로 배면에 가까운 영역에서 배면박리가 발생하는 것을 알 수 있었다. 본 연구를 통해 비상체의 충돌에 대한 고인성 섬유보강 시멘트복합체의 주요 파괴거동이 검토되었으며, Plain과 비교하여 내충격성능의 향상을 명확히 확인하였다.