Zintl phase Mg3Sb2 is a promising thermoelectric material in medium to high temperature range due to its low band gap energy and characteristic electron-crystal phonon-glass behavior. P-type Mg3Sb2 has conventionally exhibited lower thermoelectric properties compared to its n-type counterparts, which have poor electrical conductivity. To address these problems, a small amount of Sn doping was considered in this alloy system. P-type Mg3Sb2 was synthesized by controlled melting, pulverizing, and subsequent vacuum hot pressing (VHP) method. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to investigate phases and microstructure development during the process. Single phase Mg3Sb2 was successfully formed when 16 at.% of Mg was excessively added to the system. Nominal compositions of Mg3.8Sb2-xSnx (0 ≤ x ≤ 0.008) were considered in this study. Thermoelectric properties were evaluated in terms of Seebeck coefficient, electrical conductivity, and thermal conductivity. A peak ZT value ≈ 0.32 was found for the specimen Mg3.8Sb1.994Sn0.006 at 873 K, showing an improved ZT value compared to intrinsic one. Transport properties were also evaluated and discussed.

본 연구는 ‘청도반시’ 감을 열대지역으로 수출하는 상황을 모의하여 실시하였다. 수송 중이나 수송 후 유통과정에서 홍시를 만들기 위한 적절한 수송 온도(0℃, 5℃, 10℃)와 에틸렌 발생제 투입시기(수송 전, 수송 후)를 구명하고자 하였다. 15일간 모의 수송 후와 이후 30℃에서 5일간 모의 유통 후에 과실의 숙성과율과 품질을 조사하였다. 에틸렌 발생제를 처리하여 15일간 모의 수송한 후의 숙성과율은 10℃에서는 모두 홍시가 되었으나 0℃와 5℃에서는 홍시가 되지 않았고, 수송 전에 에틸렌 발생제를 처리하지 않은 과실은 모든 온도에서 홍시가 되지 않았다. 이후 30℃에서 5일간 모의 유통한 과실은 수송 전 에틸렌 발생제를 투입한 처리는 5℃와 10℃에서 모두 홍시가 되었으나 0℃에서는 38.5%만 홍시가 되었다. 수송 후 에틸렌 발생제를 투입한 처리는 모두 홍시가 된 처리구가 없었으며, 0℃와 5℃에서는 각각 63.5%와 59.6%로 비슷했으나 10℃에서는 19.2%로 오히려 낮았다. 결론적으로 수송 직후 바로 출하하기 위해서는 수송 전에 에틸렌 발생제를 투입하고 10℃에서 수송하는 것이, 그리고 5일간의 현지 유통 중에 숙성을 유도하기 위해서는 수송 전에 에틸렌 발생제를 투입하여 5℃에서 수송하는 것이 효과적인 것으로 판단되었다. 수송 후 에틸렌 발생제를 투입해서 유통 중 숙성을 유도하여 홍시를 제조하는 방식은 수송 온도에 따른 차이는 있으나 10℃ 이하에서 15일간 수송한 감에서는 홍시가 잘 되지 않으므로 앞으로 그 원인과 적절한 수송온도에 대한 연구가 더 필요하다.

The porous Mg3Sb2 based compounds with 60~70% of relative density were prepared by powder compaction at room temperature and reactive liquid phase sintering at 1023 K for 4hrs. The stoichiometric Mg3Sb2 compounds were synthesized from elemental Sb and Mg powder in the mixing range of 61~63 at% Mg. The increased scattering effect due to the micro-pores reduced the mobility of the charge carrier and the phonon, which caused the electrical conductivity and the thermal conductivity to decrease, respectively. But the scattering effect was greater for the electrical conductivity than for the thermal conductivity. Excess Mg alloyed in the Mg3Sb2 compounds decreased the electrical conductivity, but had no effect on the thermal conductivity. On the other hand, the large increase of the Seebeck coefficient was the result of a decrease in the charge carrier density due to the excess Mg. Dimensionless figure of merit of the porous Mg3Sb2 compound reached a maximum value of 0.28 at 61 at% Mg. The obtained value was similar to that of Mg3Sb2 compounds having little pores.

본 연구는 8주령 Sprague-Dawley계통의 암컷 랫드에서 제독유황을 반복경구투여 독성평가를 하기위해 시행하였다. 랫드에 처치한 물질은 사료섭취량의 0.2%, 1%, 5% 제독유황과 사료섭취량의 1% 유황으로 13주 경구투여를 하였다. 제독유황의 안전성을 확인하기 위해 다음과 같은 관찰 및 검사를 하였다. 검사항목으로는 체중과 사료 섭취를 측정하였고 임상증상, 안과학적 검사, 혈액학적 검사, 혈청 생화학적 검사를 관찰하였다. 또한 랫드에 간과 신장에서 의 병리조직학적 변화를 관찰하였다. 그 결과 체중, 사료섭 취량, 혈액학적 및 병리조직검사 소견에서 대조군과 제독 유황 그룹 간의 유의적인 차이가 보이지 않았다. 혈청생화 학적 검사소견에서는 0.2% 및 1% 투여군에서는 대조군과 비교시 용량의존적으로 유의적인 차이를 보이는 항목은 보이지 않았으나, 고용량군에서는 glucose 감소에 의한 저칼 륨혈증, 인슐린 과잉분비의 독성을 의심할 수 있었으며, 또 한 ALT와 ALP의 증가는 간 독성이나 간암, 황달의 유발이 의심되었다. 한편, 병리조직학적인 검사에서는 시험 전체군에서 대조군과 비교시 유의할만한 병리조직이상이 관 찰되지 않았다. 따라서 본 연구에서는 사료섭취량 1%의 제독유황까지 투여는 랫드에서 독성을 나타내지 않는 것으로 사료된다.

We investigated the effect of PE film thickness on the modified atmosphere packaging (MAP) deastringency of ‘Sanggamdungsi’ (Diospyros kaki cv.) astringent persimmon at room temperature (25°C) and low temperature (-1°C). The fruits were individually packaged with PE film of which the thickness is 60, 80, 100, 115 or 130 μm and stored at room or low (-1°C) temperature. At room temperature, firmness shows the highest value (23.3-26.5) at 100 μm thickness. Top flesh browning and decay was monitored at 20 days after storage, and peel blackening and style-end softening was negligible at optimal thickness. Therefore, optimal film thickness of deastringency at room temperature is 80-100 μm. At this thickness, the astringency was removed after 5 days and the fruits can be distributed until 10 days after the MAP. At low (-1°C) temperature, firmness was maintained regardless of film thickness. However, the firmness is higher as the film is thicker. Top flesh browning and decay was not occurred even after 90 days after storage. Peel blackening and style-end softening was monitored at 90 days after storage. Off-flavor was monitored at 115 and 130 μm thickness. Therefore, optimal film thickness of deastringency at low (-1°C) temperature is 80-100 μm. At this thickness, the astringency was removed after 50 days and the fruits can be distributed until 80 days after the MAP.