The present investigation has attemped to optimize hydrogen reduction process for the mass production of Fe-8wt%Ni nanoalloy powder from ball milled powder. In-situ hygrometry study was performed to monitor the reduction behavior in real time through measurement of water vapor outflowing rate. It was found that the reduction process can be optimized by taking into account the apparent influence of water vapor trap in the reactor on reduction kinetics which strongly depends on gas flow rate, reactor volume and reduction.

The present investigation has been performed on full densification behavior and mechanical property of the powder injection molded Fe-8wt%Ni nanoalloy powder. The net shaping process of the nanopowder was conducted by powder injection molding (PIM) process. The key-process for fabricating fully densified net-shaped nanopowder by pressureless sintering is an optimal control of agglomerate size of nanopowder. Enhanced mechanical property of PIMed Fe-Ni nanopowder is explained by grain refinement and microstructural uniformity.

Densification behavior of nano-agglomerate powder during pressureless sintering of Fe-Ni nanopowder was investigated in terms of diffusion kinetics and microstructural development. To understand the role of agglomerate boundary for sintering process, densification kinetics of Fe-Ni nano-agglomerate powder with different agglomerate size was investigated. It was found that activation energy for densification was lower in the small-sized agglomerate powder. The increase in the volume fraction of inter-agglomerate boundary acting as high diffusion path might be responsible for the enhanced diffusion process.