FePt nanoparticles for high-density magnetic recording media were synthesized by the simultaneous chemical reduction of Fe(acac) and Pt(acac) with 1,2-hexadecanediol as the reducing reagent. TEM images showed that the shape of as-synthesized FePt nanoparticle was spherical and average particle size was 3 nm. Also, SAD pattern showed that crystal structure was disordered FCC (face centered cubic). These FCC structured nanoparticles were transformed FCT (face centered tetragonal) structure by annealing at 55 for 30 min in Ar atmosphere. XRD analysis revealed that as-synthesized FePt nanoparticles were transformed from disordered FCC to ordered FCT. Finally, the coercivity of 2 kOe for FePt nanoparticles with FCT structure was obtained by VSM measurement.

In this study, chemical solution mixing and hydrogen reduction method was used to fabricate nanostructured alloy powders. Fe-Co chloride mixture, FeCl and COCI with 99.9％ purity, were reduced in hydrogen atmosphere. Nanostructured Fe-Co alloy powders with a grain size of 50 nm were successfully fabricated. Magnetic properties of fabricated (x=0, 10, 30, 50, 70, 100) alloy powders with the same grain size were measured because size factor can affect magnetic properties. Coercivity of Fe-Co alloy powders were increased with increasing Co contents. Maximum value of coercivity in various Co contented Fe-Co alloy powders with similar grain size was 125 Oe at Fe. Saturation magnetization value at FeCo composition showed maximum value of 219 emu/g and saturation magnetization value decreased with increasing Co contents and minimum value of 155 emu/g was observed at Co.

The purpose of this study is the fabrication of nano-sized Fe-Co alloy powders with soft magnetic properties by the slurry mixing and hydrogen reduction (SMHR) process. 0 and powders with 99.9% purities were used for synthesizing nanostructured Fe-Co alloy powder. Nano-sized Fe-Co alloy powders were successfully fabricated using SMHR, which was performed at 50 for 1 h in H atmosphere. The fabricated Fe-Co alloy powders showed ' phase (ordered body centered cubic) with the average particle size of 45 nm. The SMHR powder exhibited low coercivity force of 32.5 Oe and saturation magnetization of 214 emu/g.

(hfac)Cu(1, 5-DMCOD)(1, 1, 1, 5, 5, 5-Hexafluoro-2, 4-pentanedionato Cu(I) 1, 5-dimethyl-cyclooctadine) 전구체와 He 운반기체를 이용하여 MOCVD(Metal Organic Chemical Vapor Deposition) 방법으로 Cu 박막을 형성하였으며, He 운반기체와 함께 H2 gas 및 H(hfac) Ligand의 첨가가 Cu 박막 형성에 미치는 영향에 대하여 조사하였다. He운반기체만을 사용한 경우, Cu 박막의 증착율은 기판온도 180~230˚C에서 20~125Å/min 정도로 낮은 값을 보였으며, 특히 기판온도 190˚C에서는 매우 얇은 두께 (700Å)이면서 낮은 비저항(2.8μΩcm)을 갖는 Cu 박막이 형성됨을 알 수 있었다 He 운반기체와 함께 환원가스(H2) 및 화학첨가제 (H (hfac) ligand)의 첨가 실험에서는 낮은 기판온도 (180~190˚C) 구간에서 현저하게 증착율이 증가하였으며 얇은 두께 (~500Å)의 Cu 박막이 낮은 비저항(3.6~2.86μΩcm)을 갖는 것으로 나타났다. 또한 얇은 두께의 MOCVD Cu박막들의 표면 반사도(reflectance)는 300˚C에서 열처리한 sputter Cu의 반사도에 근접하는 우수한 surface morphology를 보였다 결국, (hfac)Cu(1,6-DMCOD) 전구체를 이용하여 얻어진 MOCVD Cu박막은 얇은 두께에서 낮은 비저항을 갖는 우수한 막질을 보였으며, Electrochemical deposition공정에서 conformal seed layer로써의 적용이 가능할 것으로 기대된다.