Considering the characteristics of aldehydes among volatile organic compounds, a combined process was established by linking an absorbent and a photocatalytic reactor. Experiments to find the optimal operating conditions of the combined process showed that as the amount of photocatalyst coating increases, the wavelength of the ultraviolet lamp used becomes shorter, the photodegradation rate becomes faster, and the removal efficiency increases. It was also demonstrated that by controlling the relative humidity during the connection process of the combined process, the re-evaporation phenomenon at the front end (absorption area) of the hybrid process can be improved and the removal efficiency at the back end (photocatalytic reaction area) can be significantly enhanced. This confirmed the need for a combined process that complements the advantages and disadvantages of each process.

활성 의약품 성분(APIs)의 존재가 수생 생태계와 인간의 건강에 위험하다는 증거가 있다. 물에 항생물질인 테트 라사이클린과 같은 API가 존재하면 미생물에 항균제 내성(AMR)이 발생해 개인과 사회에 막대한 비용이 발생한다. TiO2 또 는 비스무트 기반 촉매와 같은 촉매가 내장된 막은 유기 유출물을 분해하고 폐수로부터 분리한다. 촉매의 광촉매 활성은 귀 금속 도핑 및 탄소성 물질의 첨가 및 다른 반도체와의 헤테로 접합 형성으로 향상될 수 있다. 광촉매의 회수는 고분자 막에 서 광촉매의 고정화를 통해 가능하다. 이 검토에서는 물 속 항생제의 분해가 논의된다.

막여과는 흡착, 응집 등의 폐수 처리 방법에 비교해 경제적이며, 높은 효율을 보인다는 장점을 가지고 있다. 하지 만, 막의 표면에 오염물질이 흡착하여 발생하는 막오염 현상으로 인해 막여과의 효율이 크게 줄어들게 된다. 다양한 종류의 막 중에서 세라믹 분리막은 친수성을 띄며, 화학적으로 안정되었기 때문에 오염방지에 효과적이다. 또한, 산화 그래핀 등을 활용한 복합막도 막오염을 예방하는 데 도움이 될 수 있다. 최근에는 막오염을 방지하고 시너지 효과를 얻기 위해 광촉매 분 리막이 해결책으로 제시되었다. 막 분리는 광촉매의 단점인 촉매의 낮은 재사용률을 보완할 수 있으며, 광촉매 반응은 오염을 막을 수 있다.

A porous photocatalyst concrete filter was successfully produced to remove NOx, by mixing TiO2 photocatalyst with lightweight aerated concrete. Ultra Fine Bubbles were used to form continuous pores inside the porous photocatalytic concrete filter, which was mixed via a bubble generation experiment. The optimal mixing condition was determined to be with 4% of the bubble generation agent B. NO removal specimens were prepared for various photocatalytic loading conditions, and the specimen containing 3% P-25 removed NO at a concentration of 1.03 μmol in 1 h. The NO removal rate of the porous photocatalytic concrete filter prepared in this study was 10.99%. This photocatalytic filter performance was more than 9 times the amount of NO removed by a general photocatalytic filter. The porous photocatalyst concrete filter for removing NOx developed in this study can be applied to various construction sites and the air quality can be solved by reducing NOx contributing to the formation of fine particles.

성장하는 산업화는 심각한 수질 오염으로 이어진다. 폐수로 배출되는 약품과 섬유산업에서 나오는 유기배출물은 환경과 생명에게 악영향을 미친다. 항균치료에 사용되는 항생제가 폐수에 존재하면 인체에 매우 해로운 약제 내성균의 성장 을 야기하게 된다. 섬유산업에서 사용되는 유기염료 분자의 제조에는 다양한 유기 저분자가 사용된다. 이러한 분자들은 인쇄 및 염색 산업의 폐수 배출물에 존재하여 분해가 잘 이루지지 않는다. 이러한 문제들을 해결하기 위해 광분해성 촉매를 분리 막에 도입하고 폐수를 처리한다. 이 과정을 통해 유기 분자는 광분해되며 동시에 분해된 화합물들은 분리막을 통과하여 분리 된다. 이산화티타늄(TiO2)은 뛰어난 광촉매 역할을 하는 반도체이다. 다른 전이 금속 산화물과 화합물을 만들고 고분자 막에 도입하여 광촉매 능력을 증가시킨다. 본 총설에서는 광촉매성 분리막에 의한 염료 및 약물 분자의 분해에 대해 논의한다.

일상적인 화학제품들의 사용량이 증가함에 따라 사용되었던 염료 폐기물 처리 또한 중요한 환경 적인 문제로 대두되었다. 이러한 염료폐기물은 광촉매를 이용하여 분해시킬 수 있는데, 졸-겔 기술을 활용 하면 매우 비용 효율적으로 광촉매를 합성할 수 있다. 졸-겔 기술은 나노스케일의 막 형성에도 상당히 유 용하며 간단하게 다층구조를 형성할 수도 있다. 본 연구에서는 다양한 염료 분해에 효과가 있는 산화아연 (ZnO) 이용하여 다중 회전도포 방법으로 다층구조(3층, 5층)를 가진 ZnO 막을 형성하였다. 성능비교를 위해 단일 회전도포 방법에 의한 단층구조를 가진 ZnO 막을 대조군으로 준비하였다. X선 회절분석기 및 에너지 분산 X선 분광계를 이용하여 ZnO의 구조 및 원소분석을 수행하였고, 주사전자현미경을 통해 나노 선같은 표면형상을 관찰할 수 있었다. 추가적으로 UV-Vis 분광광도계를 활용하여 자외선의 흡수도를 측정 하였다. 5층구조를 가진 ZnO 막이 단층 구조를 가진 ZnO 막에 비해 모의 메틸렌 블루를 49% 더 많이 분해하였다. 결론적으로, 다층구조를 가진 ZnO 는 메틸렌블루 염료를 더욱 효과적으로 분해하는 광촉매로 써 유용하다는 알 수 있었다.

To improve light absorption ability in the visible light region and the efficiency of the charge transfer reaction, Pd nanoparticles decorated with reduced TiO2 nanotube photocatalyst were synthesized. The reduced TiO2 nanotube photocatalyst was fabricated by anodic oxidation of Ti plate, followed by an electrochemical reduction process using applied cathodic potential. For TiO2 photocatalyst electrochemically reduced using an applied voltage of -1.3 V for 10 min, 38% of Ti4+ ions on TiO2 surface were converted to Ti3+ ion. The formation of Ti3+ species leads to the decrease in the band gap energy, resulting in an increase in the light absorption ability in the visible range. To obtain better photocatalytic efficiency, Pd nanoparticles were decorated through photoreduction process on the surface of reduced TiO2 nanotube photocatalyst (r10-TNT). The Pd nanoparticles decorated with reduced TiO2 nanotube photocatalyst exhibited enhanced photocurrent response, and high efficiency and rate constant for aniline blue degradation; these were ascribed to the synergistic effect of the new electronic state of the TiO2 band gap energy induced by formation of Ti3+ species on TiO2, and by improvement of the charge transfer reaction.

The issue surrounding the problem of air pollution arising from rapid industrialization is one that is being continuously raised for discussion among the public, and concerns about indoor air quality have emerged both at home and abroad due to the longer periods of time spent indoors in modern times. Various studies are being conducted to solve this problem, and photocatalysts are also being studied as a solution. Accordingly, this research sought to verify the performance of reducing indoor pollutants by applying photocatalysts to building materials. As a result of evaluating the indoor pollutant reduction performance, it was confirmed that acetaldehyde was reduced by about 31%, toluene 29%, and total volatile compounds by 11%, and adhesion strength, an important factor regarding finishing material, was also enhanced 1.3 times or more based on Korean Industrial Standards. From these results, it is believed that indoor air pollution can be lowered to a certain extent through building materials using photocatalysts, and, therefore, research on long-term performance verification and evaluation methods should be continuously conducted and pursued in the future in relation to photocatalysts.

For the purpose of manufacturing a high efficiency TiO2 photocatalyst, B-doped TiO2 photocatalysts are synthesized using a plasma electrolytic oxidation method in 0.5 M H2SO4 electrolyte with different concentrations of H3BO3 as additive. For the B doped TiO2 layer fabricated from sulfuric electrolyte having a higher concentration of H3BO3 additive, the main XRD peaks of (101) and (200) anatase phase shift gradually toward the lower angle direction, indicating volume expansion of the TiO2 anatase lattice by incorporation of boron, when compared with TiO2 layers formed in sulfuric acid with lower concentration of additive. Moreover, XPS results indicate that the center of the binding energy peak of B1s increases from 191.45 eV to 191.98 eV, which suggests that most of boron atoms are doped interstitially in the TiO2 layer rather than substitutionally. The B doped TiO2 catalyst fabricated in sulfuric electrolyte with 1.0 M H3BO3 exhibits enhanced photocurrent response, and high efficiency and rate constant for dye degradation, which is ascribed to the synergistic effect of the new impurity energy band induced by introducing boron to the interstitial site and the improvement of charge transfer reaction.

단순 침전법으로 제조한 CdZnS/ZnO 광촉매를 이용하여 가시광선하에서 메틸렌블루의 광분해 반응에 대한 연구를 수행하였다. X선 회절분석법과 UV-vis 확산반사 분광법 등을 이용하여 제조된 촉매들의 물리화학적 특성을 분석하였다. 그리고 CdZnS/ZnO 광촉매의 활성을 조사하고 CdS 및 TiO2와 비교 검토하였다. CdZnS/ZnO 광촉매는 자외선뿐만 아니라 400nm에서 600nm 범위의 가시광선 영역에 있어서도 우수한 광흡수 특성을 나타내었다. 가시광선하에서 메틸렌 블루의 광분해 반응에 대해서 CdZnS/ZnO 광촉매는 CdS 와 TiO2 보다 우수한 광촉매 활성을 나타내는 것을 알 수 있었다. 그리고 가시광선하에서의 메틸렌블루의 광분해 반응에는 광촉매 반응뿐만 아니라 감광반응도 관여하고 있음을 확인할 수 있었다.

PURPOSES : The purpose of this study was to analyze the effect of reducing nitrogen oxide concentration in a photocatalyst (titanium dioxide) using statistical methods such as the Anderson-Darling test. METHODS : To compare and analyze the effect of reducing the nitrogen oxide concentrations in titanium dioxide, titanium dioxide was applied to the public road, and data acquisition in terms of nitrogen oxide concentration was conducted from roads with/without applying titanium dioxide (test section and reference section, respectively). Then, the probabilities of occurrence of nitrogen oxide concentrations in the test and reference sections were estimated and compared using the Anderson-Darling test. RESULTS : According to the comparison and analysis of probabilities in the nitrogen oxide concentration of the test and reference sections, the probabilities of nitrogen oxide concentration on December 4th were estimated as ‘High’ (17.5%, 37.9%), ‘Moderate’ (30.5%, 40.8%), and ‘Low’ (52.0%, 21.3%), respectively, and on December 5th, as ‘High’ (20.6%, 39.1%), ‘Moderate’ (26.2%, 33.0%), and ‘Low’ (53.2%, 27.9%), respectively. In addition, the probabilities of nitrogen oxide concentration in the test and reference sections were analyzed on December 6th as ‘High’ (16.5%, 36.8%), ‘Moderate’ (27.9%, 38.5%), and ‘Low’ (55.6%, 24.8%), respectively. CONCLUSIONS : Based on the results of this study, in the test section with application of titanium dioxide, the nitrogen oxide concentration was found to have a low probability, and in the reference section, the nitrogen oxide concentration was found to be higher than that in the test section. Therefore, it can be concluded that titanium dioxide applied to road facilities has a nitrogen oxide reduction effect.

In this work, TiO2 3D nanostructures (TF30) were prepared via a facile wet chemical process using ammonium hexafluorotitanate. The synthesized 3D TiO2 nanostructures exhibited well-defined crystalline and hierarchical structures assembled from TiO2 nanorods with different thicknesses and diameters, which comprised numerous small beads. Moreover, the maximum specific surface area of TiO2 3D nanostructures was observed to be 191 m2g-1, with concentration of F ions on the surface being 2 at%. The TiO2 3D nanostructures were tested as photocatalysts under UV irradiation using Rhodamine B solution in order to determine their photocatalytic performance. The TiO2 3D nanostructures showed a higher photocatalytic activity than that of the other TiO2 samples, which was likely associated with the combined effects of a high crystallinity, unique features of the hierarchical structure, a high specific surface area, and the advantage of adsorbing F ions.