PURPOSES : The purpose of this study is to conduct basic research on the development of repair materials for cross-sectional repair of the concrete of the lower slab ceiling of an old bridge. METHODS : To estimate the performance as restoration materials, cross section rebound test, compressive strength test, flexural strength test, and firing shrinkage test was done. Rebound test was done by weight of amount of rebound and weight of concrete accumulated in frame. Cross section rebound test was done by put ruler in the deepest part of concrete stick on frame. Compressive and flexural strength test was done based on KS F 2405 and KS F 2408. Firing shrinkage test was done based on ASTM C 1579-16. RESULTS : As a result of the experiment, an appropriate bonding thickness was secured by mixing natural fibers, polymers, early steel cement, and expansion materials, and the dust reducing agent was excluded due to the problem of lowering compressive strength. In addition, the amount of rebound was reduced by using a hydro mix nozzle, and plastic shrinkage cracks were also reduced due to the internal curing effect of natural fibers. CONCLUSIONS : This study was a basic study in the development of repair materials for cross-sectional repair of the lower ceiling of an aged bridge slab, and developed a material with appropriate performance. However, there is a problem that the amount of rebound and dust increases depending on the type of cement, so experiments will be conducted by changing the type of cement in future research.

PURPOSES: This study aims to develop a repair material that can enhance pavement performance, inducing rapid traffic opening through early strength development and fast setting time by utilizing MgO-based patching materials for repairing road pavements. METHODS : To consider the applicability of MgO-based patching materials for repairing domestic road pavements, first, strength development and setting time of the materials were evaluated, based on MgO to KH2PO4 ratio, water to binder ratio, and addition ratio of retarder (Borax), by which the optimal mixture ratio of the developed material was obtained. To validate the performance of the developed material as a repair material, the strength(compressive strength and bonding strength) and durability (freezing, thawing, and chloride ion penetration resistance) was checked through testing, and its applicability was evaluated. RESULTS : The results showed that when an MgO-based patching material was used, the condensation time was reduced by 80%, and the compressive strength was enhanced by approximately 300%, as compared to existing cement-based repair materials. In addition, it was observed that the strength (compressive strength and bonding strength) and durability (freezing and thawing, and chloride ion penetration resistance) showed an excellent performance that satisfied the regulations. CONCLUSIONS : The results imply that an emergent repair/restoration could be covered by a rapid-hardening cement to meet the traffic limitation (i.e. the traffic restriction is only several hours for repair treatment). Furthermore, MgO-based patching materials can improve bonding strength and durability compared to existing repair materials.

This study is subway tunnel field application about repair materials with crack self-healing capability. It was found that it showed good durability compared to the existing repair materials through lab test. Utilization of these mortars may have high potential for a new repair material.

Due to special chemical environment, sulfuric acid can be produced in sewerage system. This sulphuric acid may react with hardened cement paste and originate expansive products which can induce swelling and disaggregation of concrete. Therefore, the aim of this paper is to study the strength and acid resistance properties of cementless restorative mortar

본 연구에서는 고유동성의 SBR 개질 시멘트 모르타르의 기초적 성능을 바탕으로 콘크리트의 보수용 재료에 매우 중요한 요구성능인 부착강도에 대한 피착체의 표면에 존재하는 표면수량의 영향을 검토하는 연구가 수행하였다. 고유동성 SBR 개질 시멘트 모르타르의 기초적인 성능을 토대로 부착강도, 잔갈림성, 재료분리 저항성이 좋은 시험체를 선택하였다. 시험체는 C:F=1:1인 경우 P/C=20%, 30%의 시험체 2개, C:F=1:3인 경우 P/C=50%의 시험체 1개, 총 3개가 선택되었으며 이 3개의 배합에 대하여 피착체의 표면수량에 따른 고유동성 SBR 개질 시멘트 모르타르의 특성을 파악하였다. 표면수는 콘크리트 피착면의 단위 면적 (cm2) 당 각각 0, 0.006, 0.012, 0.017, 0.024 g이 균등하게 살포되었으며, 이에 따른 연도변화, 플로우값, 부착강도, 부착파괴형상, 내균열성 및 재료분리여부를 파악하였다. 본 연구를 통해 콘크리트 피착체에 살포된 표면수는 고유동성 SBR 개질 시멘트 모르타르의 부착강도를 증진하는 효과가 있다는 결론을 얻었다.

This study have interests in presenting the process of material optimization design. This study was designed by using design of experiment. To present the form of model and explore the optimal point of response surface model, central composite design(CCD) and Response Surface Methodology(RSM) were used in the design of the experiment and in the analysis of the results.

콘크리트 구조물은 시간 경과에 따라 화학적인 물질에 노출되거나, 염해, 중성화 등으로 인하여 콘크리트표면 결손 등이 발생하고 이에 따라 수명이 단축되는 현상이 발생할 수 있다. 특히 황산염 침식의 경우 표면 결손이 급격하게 발생하고 이에 따른 수분의 침투에 의하여 보강 재료로 사용되는 철근의 부식이 발생함에 따라 구조적으로 안정성이 하락하는 특성을 보이고 있다. 본 연구는 시멘트계 보수재의 가장 큰 단점중의 하나인 내산성의 문제점을 해결하기위하여 알루미노실리게이트를 적용한 내산모르타르에 관한 물리적 특성을 시험을 통하여 연구하였으며 시험결과 압축강도 및 휨강도의 경우 동등한 강도를 발현하였으며, 황산용액에 침지하여 중량변화를 관찰한 내산성의 경우 시멘트계 단면복구재가 80% 이상의 중량 변화를 나타내는 반면 시험시료의 경우에는 4% 정도의 중량결손이 발생하여 내산성에 효과적인 특성을 가지는 것으로 나타났다. 따라서 알루미노실리케이트류를 첨가한 내산 모르타르의 특성이 우수한 것으로 나타나 산에 의한 침식 등이 우려되는 곳에 단면복용재료로서 효과적인 특성을 발휘할 수 있을 것으로 판단된다.

이산화탄소에 의해 열화된 콘크리트 구조물의 보수 후 잔존수명을 평가할 때 보수재의 효과를 고려하기 위해 본 연구에서는 탄산화에 의해 열화를 받은 콘크리트 부재의 보수 후 재열화과정을 Fick's 확산(diffusion) 제1법칙을 이용하여 모델링함으로써 단면복구재에 의해 보수된 콘크리트 부재의 독특한 상황을 고려한 합리적인 예측식을 제시하였다. 연구결과는 보수재의 이산화탄소 확산 프로파일과 기존 구체콘크리트의 탄산화된 부분의 이산화탄소 확산 프로파일을 효과적으로 모델링할 수 있음을 보여줬다. 제시된 평가모델식에 대한 검증예제를 통해 보수재의 이산화탄소 확산지연효과를 확인할 수 있었으며 보수된 콘크리트 구조물의 보수 후 잔존수명을 객관적이고 수치계산적인 방법으로 평가할 수 있었다.

하수시설 콘크리트의 열화현상은 하수시설의 특수한 환경조건상 황산화세균 등의 서식에 의해 발생된 황화수소(H2S)에 기인하는 생화학적 부식이 대표적인 것으로 알려져 있으나, 국내의 경우 근본적으로 방지대책이 전혀 고려되지 않은 채 정비사업이 수행되고 있어 근본적으로 황산화세균을 억제할 수 있는 보수재료․공법의 개발이 시급히 필요한 실정이다. 이에 본 연구에서는 항균금속을 포함한 도포형 항균제를 개발한 후, 개발된 항균제의 황산화세균에 대한 항균성능과 항균제를 도포한 단면복구재의 부착강도, 흡수 및 투기저항성, 중성화 깊이, 염화물이온 침투깊이 및 화학저항성 등의 기초물성을 평가하였다.

콘크리트의 열화 및 철근부식에 대응하기 위하여 다양한 보수재료가 존재하나 이러한 보수재료를 평가하는 방법은 단순히 염해, 중성화 등의 단독열화만을 대상으로 하고 있어 여러 가지 열화인자가 복합적으로 작용하는 실제 환경과는 차이를 나타내게 된다. 따라서 본 연구에서는 폴리머시멘트계 보수용 단면복구재가 KS 기준을 만족하는지 확인한 후 복합열화 환경 하에서 염해, 중성화. 철근부식을 평가하였다. 실험결과 각각의 보수재료들은 KS 기준을 만족하였지만 내구성능은 상이하게 나타나 향후 이에 대한 고려가 필요할 것으로 사료된다.