Hexagonal bolt, nut, fittings, and high-pressure valves with special alloy play an important role in many industrial products, for instance, such as semiconductor facilities, hydrogen stations and fuel cell electric vehicles. The purpose of this study is to investigate the structural stability of turning wheel using the reaction force of roller in variable hexagonal rolling die. As the results, the bearing groove had the possibility of damage in turning wheel, especially, in case of Bottom condition. Furthermore, the turning wheel showed structural instability by using safety factor but structural stability using strength, respectively, as a safety criterion.

This study has related to lightweight automobiles due to global warming with the reduction of fossil fuel reserves are rapidly progressing around the automobile industry. This study has revealed the relationship for the mechanical properties via the analyzed microstructure, precipitated phase variation of the wheel hub of a commercial vehicle manufactured using molten forging technology using A356 and A357 alloys, which are high-strength Al-Si-Mg base cast aluminum alloys. Differential scanning calorimetry has performed to analyze the precipitation amount of each alloy that influences the mechanical properties of aluminum alloy. The XRD analysis has measured for the microstructure's crystal phase on A356 and A357 alloys. In this paper has evaluated to compare the properties of the A356 alloy and the A357 alloy for the mechanical properties. The A356 alloy has confirmed that a microstructure is finer than A357 alloy, and a quantity of precipitated material is more than A357 alloy. Therefore, this study confirmed that the A356 alloy has better mechanical properties than the A357 alloy.

마그네슘은 20여년간 자동차 산업에서 휠소재로 사용되어 왔다. 마그네슘 휠은 무게가 알루미늄 휠보다 25% 가벼워서 주행성이 우수하다. 이 연구의 목적은 사형주조 및 영구금형주조 공정에 의한 AZ91D 합금제 췰을 개발하는 것이다 보호개스(SF6+CO2)를 사용하는 비플럭스 용해기술을 적용하여 용탕의 산화와 불순물의 유입을 배제하였다 마그네슘 용탕은 가압식 펌프시스템을 사용하여 가열된 파이프를 통하여 모울드에 자동으로 공급된다. 열처리 및 인고트의 조성에 따른 AZ91B 합금제 휠의 기계적 특성을 조사하였다.

2219 aluminum alloy bonded diamond wheels containing intermetallic compounds were fabricated by powder metallurgy method. Nickel and titanium were added in aluminum matrix piece. The hot pressing condition was and 20 Mpa in the furnace of the electric resistance type. The mechanical properties and grinding tests were carried out to confirm the wheel performance. Aluminum oxide ceramics were chosen for use in the grinding tests. The test proved that the heat resistance 2219 aluminum bonded diamond wheel containing 15 wt% nickel and 15 wt% titanium respectively showed the best performance.