Novel Ni- and Fe-based alloys are developed to impart improved mechanical properties and corrosion resistance. The designed alloys are manufactured as a powder and deposited on a steel substrate using a high-velocity oxygen-fuel process. The coating layer demonstrates good corrosion resistance, and the thus-formed passive film is beneficial because of the Cr contained in the alloy system. Furthermore, during low-temperature heat treatment, factors that deteriorate the properties and which may arise during high-temperature heat treatment, are avoided. For the heattreated coating layers, the hardness increases by up to 32% and the corrosion resistance improves. The influence of the heat treatment is investigated through various methods and is considered to enhance the mechanical properties and corrosion resistance of the coating layer.

Martensitic stainless steel is commonly used in the medical implant instrument. The alloy has drawbacks in terms of strength and wear properties when applied to instruments with sharp parts. 440C STS alloy, with improved durability, is an alternative to replace 420 J2 STS. In the present study, the carbide precipitation, and mechanical and corrosion properties of STS 440C alloy are studied as a function of different heat treatments. The STS 440C alloy is first austenitized at different temperatures; this is immediately followed by oil quenching and sub-zero treatment. After sub-zero treatment, the alloy is tempered at low temperatures. The microstructures of the heat treated STS 440C alloy consist of martensite and retained austenite and carbides. Using EDX and SADP with a TEM, the precipitated carbides are identified as a Cr23C6 carbide with a size of 1 to 2 μm. The hardness of STS 440C alloy is improved by austenitization at 1,100 oC with sub-zero treatment and tempering at 200 oC. The values of Ecorr and Icorr for STS 440C increase with austenitization temperature. Results can be explained by the dissolution of Cr-carbide and the increase in the retained austenite. Sub-zero treatment followed by tempering shows a little difference in the properties of potentiodynamic polarizations.

The acrylic coating emulsions were prepared by the emulsion polymerization to protect the surface of steel plate from the corrosion chemicals like acid, base and salt water. MMA(methyl methacrylate), styrene, BA(butyl acrylate), and 2-HEMA(2-hydroxyethyl methacrylate) were used as monomer. KPS(potassium persulfate) and SBS(sodium bisulfite) as redox initiator and SDBS(sodium dodecylbenzene sulfonate) as emulsifier were used on the emulsion polymerization reaction. The most stable in-situ coating was obtained when 10% of MMA was added. Both particle size and quantity in emulsion were decreased as increasing the mount of SDBS. the most stable prepared coating emulsion with polyisocyanate crosslinker showed very high anticorrosion properties on the coated steel layer to salt water, whereas no significant improvement of anticorrosion property to acdic and basic condition it showed.

가압경수형 원자력발전소 일차계통에서 발생되는 방사성 부식생성물(크러드)은 원자력발전소 작업종사자 피폭의 주요원인이다. 또한, 최근 원자력발전소의 장주기운전 추세에 따라 장기간 노심에 침적된 방사성 부식생성물은 hideout 현상으로 노심의 출력에 영향을 주는 축방향이상출력 (AOA) 현상의 원인이 되고 있다. 크러드의 주요 성분은 마그네타이트, 니켈 페라이트, 코발트 페라이트가 주를 이루며, 이러한 산화물 형태는 강자성의 자기적 성질을 가지고 있다. 따라서, 전자석과 영구자석의 적절한 배치를 통하여 자기장을 발생시켜 크러드를 제거하는 필터 개발을 위해 개념 설계를 하였다. 기존의 필터와 달리 유체의 흐름을 방해하지 않아 압력저하 현상이 발생하지 않고, 연속적으로 사용할 수 있는 장점이 있다. 크러드 제거 기술의 하나로써 활용될 수 있을 것으로 기대된다.