To establish low-temperature process conditions, process-property correlation has been investigated for Ga-doped ZnO (GZO) thin films deposited by pulsed DC magnetron sputtering. Thickness of GZO films and deposition temperature were varied from 50 to 500 nm and from room temperature to 250 oC, respectively. Electrical properties of the GZO films initially improved with increase of temperature to 150 oC, but deteriorated subsequently with further increase of the temperature. At lower temperatures, the electrical properties improved with increasing thickness; however, at higher temperatures, increasing thickness resulted in deteriorated electrical properties. Such changes in electrical properties were correlated to the microstructural evolution, which is dependent on the deposition temperature and the film thickness. While the GZO films had c-axis preferred orientation due to preferred nucleation, structural disordering with increasing deposition temperature and film thickness promoted grain growth with a-axis orientation. Consequently, it was possible to obtain a good electrical property at relatively low deposition temperature with small thickness.

Various thicknesses of Al-doped ZnO (AZO) films were deposited on glass substrate using pulsed dcmagnetron sputtering with a cylindrical target designed for large-area high-speed deposition. The structural,electrical, and optical properties of the films of various thicknesses were characterized. All deposited AZO filmshave (0002) preferred orientation with the c-axis perpendicular to the substrate. Crystal quality and surfacemorphology of the films changed according to the film thickness. The samples with higher surface roughnessexhibited lower Hall mobility. Analysis of the measured data of the optical band gap and the carrierconcentration revealed that there were no changes for all the film thicknesses. The optical transmittances weremore than 85% regardless of film thickness within the visible wavelength region. The lowest resistivity,4.13×10-4Ω·cm-1, was found in 750nm films with an electron mobility (µ) of 10.6cm2V-1s-1 and a carrierconcentration (n) of 1.42×1021cm-3.

Indium Gallium Zinc Oxide (IGZO) thin films were deposited onto 300 nm-thick oxidized Si substrates and glass substrates by direct current (DC) magnetron sputtering of IGZO targets at room temperature. FESEM and XRD analyses indicate that non-annealed and annealed IGZO thin films exhibit an amorphous structure. To investigate the effect of an annealing treatment, the films were thermally treated at 300˚C for 1hr in air. The IGZO TFTs structure was a bottom-gate type in which electrodes were deposited by the DC magnetron sputtering of Ti and Au targets at room temperature. The non-annealed and annealed IGZO TFTs exhibit an Ion/Ioff ratio of more than 105. The saturation mobility and threshold voltage of nonannealed IGZO TFTs was 4.92×10-1cm2/V·s and 1.46V, respectively, whereas these values for the annealed TFTs were 1.49×10-1cm2/V· and 15.43V, respectively. It is believed that an increase in the surface roughness after an annealing treatment degrades the quality of the device. The transmittances of the IGZO thin films were approximately 80%. These results demonstrate that IGZO thin films are suitable for use as transparent thin film transistors (TTFTs).

Ti-6Al-4V 합금을 타겟트로 사용하여 유리 기판위에 dc reactive magnetron sputtering법으로 N2/(Ar+N2) 비, 기전력 및 시간등의 여러 가지 증착 조건에서 Ti-6Al-4V-N 필름을 증착하였고, 각각의 증착 조건에 따른 결정구조 및 우선방위 거동은 X-선 회절장치를 사용하여 조사하였다. Ti-6Al-4V-N 필름은 본질적으로 fcc 결정구조의 δ-TiN에 Al과 V이 결함으로서 고용된 변형된 형태의 δ-TiN구조이고, TiN의 격자상수(4.240 )보다 작은 값을 나타내었는데, 이는 Ti(1.47 )에 비하여 상대적으로 원자반경이 작은 Al(1.43 )과 V (1.32 )이 Ti의 격자위치에 치환된 결과이다. 그리고 Ti-6Al-4V-N 필름은 N2가스 분압이 감소됨에 따라 (111) 우선방위 성장거동을 하였을 뿐만아니라 증착시간의 증가에 따라 뚜렷한 (111) 우선방위 성장거동을 나타내었다. 그리고 증착속도 및 결정입도의 거동 또한 여러 가지 증착 조건에 크게 의존한다

DC마그네트론 스퍼터링 방식으로 Ti/SiO2/Si 구조 위에 Pt(200) 박막을 배향 성장시키기 위해 증착조건(스퍼터링 가스의 종류와 압력, 기판의 온도)과 후속열처리(RTA, Furnace annealing)에 따른 Pt 박막의 전기, 결정학적 특성을 조사하였다. 실험결과, 20mTorr의 Ar+O2(20%)의 혼합가스 분위기에서 기판온도를 500˚C로 유지하여 Pt박막을 증착하고 600˚C에서 30초간 급속 열처리를 실시한 경우, 90% 이상의 결정 배항도를 갖는 Pt(200) 박막을 제작할 수 있었다. 제작된 Pt(200) 박막은 30~40μΩ.cm의 낮은 전기저항율과 우수한 열적 안정성을 나타내었으며 600˚C의 고온에서 장시간 열처리를 실시하여도 전기저항율이나 우선 배향성의 변화, 박막내 미세 결함 및 열적응집현상 등이 발생되지 않았다.