Nowadays, the automotive industry has target to improve the fuel consumption due to restricted exhaust gas regulation. For this reason, the applicability of lightweight material, Al alloys, Mg alloys are also being expanded. In this concept, high strength steel, DP780 and light alloy, AL5052 are joined in the right place of the car body. However, it is difficult to join to steel and aluminum by conventional fusion welding. Generally, in respect to dissimilar metal joining by fusion welding, intermetallic compound layer formed at joint interface; hot cracking in generated. To evaluate the welding quality, tensile test and metallographic examination was carried. Especially, correlation between Heat per unit length and formation of intermetallic compound layer was minutely analyzed. Finally, optimal welding condition was selected for improvement of strength at weldment and practical use.

A5J32-T4 and A5052-H32 dissimilar aluminum alloy plates with thickness of 1.6 and 1.5 mm were welded by friction stir lap welding (FSLW). The FSLW were studied using different probe length tool and various welding conditions which is rotation speed of 1000, 1500 rpm and welding speed of 100 to 600 mm/min and material arrangement, respectively. The effects of plunge depth of tool and welding conditions on tensile properties and weld nugget formation. The results showed that three type nugget shapes such as hooking, void, sound have been observed with revolutionary pitch. This plunge depth and material arrangement were found to effect on the void and hooking for- mation, which in turn significantly influenced the mechanical properties. The maximum joint efficiency of the FSLWed plates was about 90% compared to base metal, A5052-H32 when the A5052-H32 was positioned upper plate and plunge depth was positioned at near interface between upper and lower plates.

The spot weldability of dissimilar metal joints between stainless steels (AISI316) and interstitial free (IF) steels were investigated. This study was aimed to determine the spot welding parameters for a dissimilar metal joint and to evaluate the dissimilar metal joint's weldability, including its welding nugget shape, tensileshear strength, hardness, and microstructure. The fracture surface was investigated by using a Scanning Electron Microscopy (SEM). The experimental results showed that the shape of nugget was asymmetric, in which the fusion zone of the STS316 sheet was larger due to the higher bulk-resistance. The microstructure of the fusion zone was fully martensite. In order to evaluate the microstructure further, dilution of stainless steels were calculated and imposed onto the Schaeffler diagram. The predicted microstructure from the Schaeffler diagram was martensite. In order to confirm the predicted microstructure, XRD measurements were carried out. The results showed that that initial weld nugget was composed of austenite and martensite.