In order to increase the usability of PLA in tissue engineering, we tried to improve the hydrophobicity and low mechanical properties of PLA. The basic solutions were prepared by mixing 3, 5, and 7wt.% of PLA in a solution of chloroform and acetone in a volume ratio of 3:1. Several types of nanofiber mats were fabricated using a mixed solution in which 0.5, 1, and 3wt.% of PEO and PVAc, which are biodegradable polymers, were added to these solutions, respectively, through the SBS method. As a result, it was found that when the content of PEO increased, the diameter and surface state of nano fibers became uniform and the water contact angle significantly decreased, but it did not affect the tensile strength. In addition, the hydrophobicity of PLA was improved to hydrophilicity by mixing with PVAc, but the strain was greatly reduced.

계면동전위 특성평가는 분리막의 막오염 개선연구와 분리막의 표면전하 분석을 통한 고분자의 개질 확인 및 치환기 확인에 대한 연구로 활발히 진행되고 있다. 제타전위 (zeta potential)란 전기역학적 현상으로 발생하는 전위차를 정량화 한 값을 측정하는 것을 말한다. 이러한 제타전위를 측정하기 위해서는 전기영동 (electrophoresis), 전기삼투 (eletrosmosis), 유동전위 (streaming potential)를 측정하는 예가 있다. 그 중 평막은 유동전위 측정을 하는 것에 있어 가장 높은 재현성을 보인다. 따라서, 본 연구에서는 SEBS (polystyrene-ethylenebutylene-styrene) 고분자 개질을 통해 아민화된 SEBS 평막형 분리막을 제막하고, 제막한 아민화된 SEBS 고분자 분리막의 계면동전위 측정을 통해 계면 유동전위를 측정하여 결과를 분석하였다.

수중 이 취미를 유발시키는 대표적인 미량오염물질인 2-methylisoborneal (MIB)과 geosmin(지오스민)의 배제율을 소수성 polyethersulfone (PES) 나노분리막(분획분자량 : 400 Da)을 적용하여 다양한 용액조성에서 관찰하였다. 실험결과 적용된 모든 조건에서 지오스민이 2-MIB보다 다소 높은 배제율을 나타내었다. 용액의 pH 효과를 관찰한 결과 pH가 증가할수록 2-MIB와 지오스민 양쪽 모두 배제율이 증가하는 경향을 나타내었다. 한편, 수중 자연유기물질의 존재는 두 미량유기물질의 배제율을 크게 증가시켰으며 이와 같은 현상은 높은 pH일수록 더욱 뚜렷하게 나타났다. 소수성 분리막을 친수성 TiO2 입자로 표면코팅 시킨 후 배제율을 관찰한 결과 분리막의 표면을 친수화한 후 소수성인 2-MIB와 지오스민의 배제율은 증가하는 경향을 나타내었다. 따라서 소수성 상호작용은 미량유기물질 나노여과 배제율의 중요한 기작 중 하나임을 확인할 수 있었다.