Hexagonal bolt, nut, fittings, and high-pressure valves with special alloy play an important role in many industrial products, for instance, such as semiconductor facilities, hydrogen stations and fuel cell electric vehicles. The purpose of this study is to predict the reaction force of roller in drawing system. Numerical analysis was conducted to obtain data for designing the turning wheel, which is key parts in drawing system, using the reaction force of roller. As the results, the reaction force of X axis direction was about 9~20 times larger than that of Z axis direction and the reaction force of Y axis direction was negligible. The maximum reaction force of roller was the case of 4 stage and the numerical results in this study could be helped for designing the mechanical parts of variable hexagonal rolling die.

SUS hexagonal bar have been widely used to manufacture the hexagonal bolt/nut, adapter and fittings. Raw SUS circular bar is used to make SUS hexagonal bar using drawing system. The purpose of this study is to investigate the characteristics, for instance, such as stress, strain and reduction ratio of area for bar. As the results, it was confirmed that the maximum stresses were occurred at edge of hexagonal bar, thus it could be worked as residual stress of hexagonal bar. The phenomenon of spring back was almost no found in all parts of hexagonal bar. Furthermore it showed that the reduction ratios of area were about mean 26% when SUS circular bar was changed to SUS hexagonal bar in this study.

In the present study the microstructure of low-carbon steels fabricated by controlled rolling and accelerated cooling processes was characterized and identified based on various microstructure analysis methods including optical and scanning electron microscopy, and electron backscatter diffraction(EBSD). Although low-carbon steels are usually composed of α-ferrite and cementite(Fe3C) phases, they can have complex microstructures consisting of ferrites with different size, morphology, and dislocation density, and secondary phases dependent on rolling and accelerated cooling conditions. The microstructure of lowcarbon steels investigated in this study was basically classified into polygonal ferrite, acicular ferrite, granular bainite, and bainitic ferrite based on the inverse pole figure, image quality, grain boundary, kernel average misorientation(KAM), and grain orientation spread(GOS) maps, obtained from EBSD analysis. From these results, it can be said that the EBSD analysis provides a valuable tool to identify and quantify the complex microstructure of low-carbon steels fabricated by controlled rolling and accelerated cooling processes.

Marine casualties of vessel are serious problems on social and national aspects, because it results in sacrifice of lives, a great lose of properties and marine pollution. According to recent statistics of marine casualties of vessel, fishing boats are more likely to be ended in the casualty, and especially, small fishing boats cause much more accidents than any other big vessels. Most of marine casualties were caused by the human factors such as poor watch keeping, inadequate manoeuvering and negligent action for engine, etc. This study is intended to provide navigator of small fishing boat with a specific information of necessary to assist both the manoeuvering and the avoidance of capsizing. The manoeuvering characteristics of ship can be adequately judged by the results of typical ship trials manoeuvres. For this purpose, the author measured the roll responses of a small fishing boat in waves using the real sea experimental measuring system, and analyzed the experimental data by the statistical and spectral analyzing methods to get the characteristics of the roll motion responses of the small boat through the wave directions and the ship's speed.

알루미나이징강에 대하여 초기마모영역에서 rolling-sliding 마모시험을 한 결과를 요약하면 다음과 같다. 1) 2차 확산재의 내마모성이 가장 우수하고 처녀재에 비하여 저응력 레벨에서 약 18%, 고응력에서 약 40%의 마모감소를 나타낸다. 2) 2차 확산재는 피복층과 합금층 경계부근의 공공생성으로 인하여 예상보다 내마모성이 낮다. 3) 알루미나이징강의 rolling-sliding 접촉에 의한 마모파양의 형태는 spalling 이며 spalling crack은 합금속의 경계부근에서 발생한다.