It has been well known that concrete structures exposed to chloride and sulfate attack environments lead to significant deterioration in their durability due to chloride ion and sulfate ion attack. The purpose of this experimental research is to evaluate the resistance against chloride ion and sulfate attack of the cementless concrete replacing the cement with ground granulated blast furnace slag. For this purpose, the cementless concrete specimens were made for water-binder ratios of 40%, 45%, and 50%, respectively and then this specimens were cured in the water of 20±3℃ and immersed in fresh water, 10% sodium sulfate solution for 28 and 91 days, respectively. To evaluate the resistance to chloride ion and sulfate attack for the cementless concrete specimens, the diffusion coefficient for chloride ion and compressive strength ratio, mass change ratio, and length change ratio were measured according to the NT BUILD 492 and JSTM C 7401, respectively. It was observed from the test results that the resistance against chloride ion and sulfate attack of the cemetntless concrete were comparatively largely increased than those of OPC concrete with decreasing water-binder ratio.

In this study, the resistance of chloride penetration and sulfate attack of mortar substituted heavyweight waste glass were evaluated. As a result, chloride penetration depth and diffusion coefficient decreased with the substitution of waste glass, chloride penetration resistance is increased. For sulfate attack resistance, the effect of heavyweight waste glass was little.

Based on the theory of the chemical reaction and the Tixier Model, we established a time-varying function of the porosity of concrete. The function, which has taken the filling effect of the ettringite to the capillary porosity into consideration, can obtain the change of the porosity at different stages of the corrosion subjected to external sulfate attack. Numerical simulation is utilized to analyze the distribution of porosity and sulfate ion concentration inside the concrete at different moment of the corrosion.

The purpose of this experimental research is to evaluate the long-term resistance against sulfate attack of the alkali activated cementless concrete replacing the cement with ground granulated blast furnace slag. For this purpose, the cementless concrete specimens were made for water-binder ratios of 40%, 45%, and 50%, respectively and then this specimens were immersed in fresh water and 10% sodium sulfate solution for 28, 91, 182, and 365 days, respectively. To evaluate the long-term resistance to sulfate attack for the cementless concrete specimens, compressive strength ratio, mass change ratio, and length change ratio were measured according to the JSTM C 7401. It was observed from the test results that the resistance against sulfate attack of the cemetntless concrete was comparatively largely increased than that of OPC concrete irrespective of water-binder ratio.

The purpose of this study was to evaluate the sulfate attack of ternary blended concrete based on low-heat cement for reducing the heat of hydration. The main parameters were water-to-binder ratio and curing temperature on the matching mixtures. Test results revealed that compressive strength ratio at each age was superior to the developed mixtures than control mixtures. Whereas, the mass change ratio was superior to the control mixture at all ages.

본 연구는 실리카 퓸의 대체율을 4단계(시멘트 중량의 0, 5, 10 및 15%)로 달리하여 제조한 시멘트 모르타르의 황산마그네슘 침식 저항성을 평가하며, 침식에 의한 성능저하 원인을 조사하기 위하여 수행되었다. 실리카 퓸 혼합 모르타르를 5% 황산마그네슘 용액에 360일 동안 침지한 후, 재령별 압축강도 및 팽창을 측정하였으며, XRD, SEM 및 DSC와 같은 여러 기기분석법을 활용하여 침식에 의한 시멘트 경화체의 성능저하 원인을 고찰하였다. 실험 결과에 의하면, 실리카 퓸을 혼합한 시멘트 경화체의 황산마그네슘 침식은 주로 gypsum, thaumasite 및 brucite 등의 반응생성물과 깊은 관련이 있는 것으로 나타났다.

본 연구는 실리카 퓸을 사용한 시멘트 경화체의 황산염침식 저항성을 평가하기 위하여 수행되었다. 실리카 퓸을 시멘트 중량에 대하여 0, 5, 10 및 15%의 4단계로 대체한 모르타르 및 0 및 10%의 2단계로 대체한 페이스트를 제조하여 침지실험을 실시하였다. 황산나트륨용액에 510일 동안 모르타르 및 페이스트를 침지한 후 재령별 외관조사, 팽창, 압축강도 감소율 및 공극특성을 조사한 결과, 실리카 퓸 대체율에 관계없이 실리카 퓸을 대체한 시멘트 경화체는 황산염침식에 대하여 저항성이 매우 우수하였으나, 보통포틀랜드시멘트 모르타르 및 페이스트는 황산염침식에 의한 극심한 성능저하 현상이 관찰되었다.