It is essential to select materials with excellent mechanical properties to prevent chemical and mechanical damage to the surfaces of materials used in machines and structures and to extend their lifespan. Co-based stellite alloy, which has wear resistance, heat resistance, and corrosion resistance, is essential for products used in harsh environments. However, due to the problem of enormous costs, research on hard facing, which uses a stellite coating layer only on the contact surface, is urgently required. Currently, high-facing research on Stellite coating layers is focused on powder, and GMAW research using wire is relatively lacking. In this study, welding experiments were performed to form stable weld beads using stellite 6 welding wire, and the correlation between parameters and weld beads was analyzed. A CMT welder was used to minimize the heat effect on the base material.

Aluminum material, which has excellent corrosion resistance, durability, and light weight, is widely used in the field of shipbuilding, and welding is an essential technology in shipbuilding. currently, welding is efficiently used to assemble structures of various sizes in the shipbuilding process, but aluminum is a very sensitive material at high temperatures and in a molten state, so appropriate process control is essential. research on aluminum welding has been continuously conducted, but most of the research is on the butt welding method. therefore, in this study fillet welding experiments, which are essentially applied to the internal structure of aluminum ships, were performed and the correlation between welding beads and process variables was identified. for the welding experiment GMA fillet welding was performed on Al5083 material used in the shipbuilding industry, and the influence of the process variable was confirmed by analyzing the correlation through the analysis of the etched fillet weld bead cross section for the test result according to the process variable.

Demand for research on the use of hydrogen, an eco-friendly fuel, is rapidly increasing in accordance with global environmental problems and IMO environmental regulations in the shipbuilding and marine industry. In the case of hydrogen, similar to liquefied natural gas, it has a characteristic that its volume decreases hundreds of times during phase transformation from gas to liquid, so it must be stored in a tank in the form of liquefied hydrogen for transport efficiency. The material of the liquid hydrogen tank is selected in consideration of mechanical properties and hydrogen embrittlement at cryogenic temperatures. In this study, welding research was conducted on STS316L material, which was most commonly used in the space industry. In this study, flux cored arc welding was performed under 4 welding conditions to derive the optimal welding conditions for STS316L material, and then mechanical properties of the welded part were compared and analyzed.

Stainless steel is used in many industrial fields due to its excellent properties such as workability, strength, ductility, and corrosion resistance, and various properties required in the manufacturing field depending on the constituent components. pump impellers used in seawater and underwater require high corrosion resistance and high rigidity to prevent corrosion and damage, so they are a representative part group to which Stainless materials are applied. Through the introduction of the CMT(Cold Metal Transfer) process, a manufacturing method through WAAM(Wire Arc Additive Manufacturing) technology, which has advantages of lower production cost and excellent fatigue strength compared to the existing casting method, is being proposed. Recently, prior research on the WAAM process has been conducted on various materials, but most of the research results published so far are focused on the DED(Direct Energy Deposition) process, and a good WAAM shape design study using austenitic stainless steel is lacking. in this study, using the CMT process, the relationship between the change in bead shape and process parameters was confirmed in the BoP(Bead on Plate) welding experiment using wire made of austenitic stainless steel STS-308.

Welding is a representative processing technology applied in many industrial sites due to its quality and convenience. In particular, fiber laser welding can be welded at a faster speed compared to arc welding, and there is an advantage in welding distortion, which is the most significant disadvantage of welding. In this study, the weldable thickness was predicted, and the optimal welding angle was estimated using simulations during the welding of the T-shape structure. The multi-layer heat source model proposed in the previous author's study was used, and the study was conducted using the proposed welding heat source under specific conditions of 4kw and 1.0m/min. As a result, it was predicted that high-quality welding would be possible when the thickness was 3mm or 4mm, and it was also confirmed that welding should be performed at an angle of 82.5° or more when welding a 3mm thick structure. As a follow-up study, we plan to build a welding heat source model under various conditions and conduct a study to derive welding conditions at various thicknesses.

A5J32-T4 and A5052-H32 dissimilar aluminum alloy plates with thickness of 1.6 and 1.5 mm were welded by friction stir lap welding (FSLW). The FSLW were studied using different probe length tool and various welding conditions which is rotation speed of 1000, 1500 rpm and welding speed of 100 to 600 mm/min and material arrangement, respectively. The effects of plunge depth of tool and welding conditions on tensile properties and weld nugget formation. The results showed that three type nugget shapes such as hooking, void, sound have been observed with revolutionary pitch. This plunge depth and material arrangement were found to effect on the void and hooking for- mation, which in turn significantly influenced the mechanical properties. The maximum joint efficiency of the FSLWed plates was about 90% compared to base metal, A5052-H32 when the A5052-H32 was positioned upper plate and plunge depth was positioned at near interface between upper and lower plates.