Various carbon aerogels (CAs) were prepared from polymerization of resorcinol and formaldehyde and applied as the electrode materials of an electric double layer capacitor (EDLC) with the aim of controlling the textural and electrochemical properties of CAs by the type of base catalyst and the ratio of resorcinol to catalyst (R/C). The CAs from NaHCO3 and KHCO3 with H+ ions had higher specific surface areas but exhibited lower electrochemical properties than those from K2CO3 and Na2CO3, which had more uniform pore size distributions. The electrochemical properties of Na2CO3 were superior to those of K2CO3 probably because the polarizing power of Na+ ions was higher than K+ ions. With an increasing R/C ratio, the pore sizes of CA showed a tendency to increase but the uniformity of the pore size distribution got worse. For the four base catalysts, the highest electrochemical property was obtained at the R/C ratio of 500.

Two sorghum(Sorghum bicolor L. Moench cv. Hwanggeumchal-susu and Miryang 3) samples were milled using different milling methods, and their physicochemical properties were tested. Particle size was classified into five groups such as pin mill and low temperature-microparticulation(LTM; 10, 000, 20, 000, 30, 000, and 40, 000 rpm). The water absorption index (WAI), water solubility index(WSI), and a rapid Visco analyzer(RVA) were used to examine particle size distribution and color differences. Particle size of sorghum flour prepared using LTM was lower than that prepared using a pin mill. Particle size was further reduced by successive dry milling of the LTM flour. Lightness of colored pigments increased when particle size decreased. The WAI of Miryang 3 pin milling(M1) flour was the lowest after LTM, and WSI was higher in the order of M2, M3, M4, and M5. LTM sorghum flour had significantly higher pasting viscosity, as determined using a rapid Visco analyzer. LTM Miryang 3 sorghum flour(M2～M5) flour showed lower breakdown viscosity and higher final viscosity compared to those of M1 flour, resulting in an increased setback value.

The purpose of this study was to evaluate the appearance, sensory and physicochemical characteristics of muffin added glutinous(GSP) and non-glutinous sorghum powder(NGSP). As increasing the amounts of sorghum powder, proximate (moisture, ash and protein) and minerals composition(K, Ca, Mg and Na) of muffin were significant difference. The weight, volume, height, lightness(L-value) and yellowness(b-value) were decreased as increasing the amounts of sorghum powder. In the results of sensory evaluation, appearance, color, flavor, taste, texture and overall quality of untreated muffin were 1.4, 1.6, 1.4, 1.0, 1.1 and 0.9, and muffin added 10% GSP and NGSP were scored relatively high. Antioxidant compounds contents of muffin added sorghum powder were increased as increasing the amounts of sorghum powder. DPPH and ABTS free radical scavenging activities on methanolic extracts of untreated muffin were 0.74 and 1.31 ㎎ TE/g ER, respectively. DPPH and ABTS free radical scavenging activities of 100% GSP muffin were 9.40 and 19.14 ㎎ TE/g ER, and 100% NGSP muffin were 10.59 and 18.78 ㎎ TE/g ER, respectively. The results of this study show that notable antioxidant compounds and antioxidant activity on muffin added sorghum powder are considered to have significant health benefits.