PURPOSES:The objective of this study is to ascertain the curing period of cementless cold central plant recycled asphalt base-layer, using mechanical analyses and specimen quality tests on the field.METHODS :Cold central plant recycled asphalt base-layer mixture was produced in the plant from reclaimed asphalt, natural aggregate, filler for the cold mix, and the modified emulsion AP using asphalt mix design and plant mix design. In order to examine the applicability of the curing period during the field test, the international standards for the possibility of core extraction and the degree of compaction and LFWD deflection were analyzed. Moreover, Marshall stability test, porosity test, and indirect tensile strength test were performed on the specimens of asphalt mix and plant mix design.RESULTS :The plant production process and compaction method of cementless cold central plant recycled asphalt base-layer were established, and the applicability of the optical moisture content for producing the mixture was verified through the field test. In addition, it was determined that the core extraction method of the conventional international curing standard was insufficient to ensure performance, and the LFWD test demonstrated that the deflection converges after a two-day curing. However, the back-calculation analysis reveals that a three-day curing is satisfactory, resulting in a general level of performance of dense asphalt base-layer. Moreover, from the result of the specimen quality test of the asphalt mix design and plant mix design according to the curing period, it was determined that the qualities satisfied both domestic and international standards, after a two-day curing. However, it was determined that the strength and stiffness after three-day curing are higher than those after a two-day curing by approximately 3.5 % and 20 %, respectively.CONCLUSIONS:A three-day curing period is proposed for the cementless cold central plant recycled asphalt base-layer; this curing period can be demonstrated to retain the modulus of asphalt-base layer in the field and ensure stable quality characteristics.

본 연구는 여성의 요가참여가 신체상과 신체적 자기개념에 어떤 영향을 미치는지를 알아보기 위한 것이다. 이와 같은 연구목적을 달성하기 위해 G광역시, C도 및 J도에 거주하고 있는 만20세 이상의 여성요가참여자 274명과 비 참여여성 212명 총486명을 대상으로 SMT와 PSDQ를 사용하여 분석한 결과 첫째, 여성요가참여자의 연령에 따른 신체상과 신체적 자기개념을 비교한 결과 신체상의 경우 60대에 비만형의 비율이 증가하는 것으로 나타났다. 신체적 자기개념의 경우 체지방은 연령이 증가할수록 증가하고, 신체활동은 50대에 가장 왕성한 것으로 나타났으며, 유연성의 경우 연령이 증가할수록 낮아지는 것으로 나타났다. 둘째, 여성의 요가참여 변인이 신체적 자기개념에 미치는 영향을 중다회귀분석으로 분석한 결과 요가참여 빈도는 외모와 지구력에 유의한 영향을 미치는 것으로 나타났고, 참여 시간은 체지방에, 참여기간은 건강을 제외한 전체 영역에 유의한 영향을 미치는 것으로 나타났으며, 요가참여시간은 현재의 신체상에 영향을 미치는 것으로 나타났다. 셋째, 신체상이 신체적 자기개념에 미치는 영향 중 건강과 자기존중감을 제외한 8개 하위영역에서 신체상에 유의하게(p <.05) 영향을 미치는 것으로 나타났다.