The synthesis of silver coated iron base alloy (Sendust : Fe-Si-Al) powder having the both effects of shielding and suppressing of electromagnetic wave was studied. Depending on thickness of silver coating layer, the electromagnetic properties of the dispersed particles complexed with organic binder were examined. It is proposed that the silver coated sendust flake powders with controlled electrical properties and thickness can be used as thin microwave absorbers in quasi-microwave frequency band.

Type I clathrate was produced by arc melting and hot pressing and thermoelectric properties were investigated. Negative Seebeck coefficient at all temperatures measured, which means that the majority carriers are electrons. Electrical conductivity decreased by increasing temperature and thermal conductivity was 0.012 W/cmK at room temperature and dimensionless thermoelectric figure of merit (ZT) was 0.01 at 873K.

This paper presents hull stress monitoring system installed in LNGC damaged by a Typhoon Elongation/contraction of removed areas has been assessed in terms of possible residual stress that will take place in replaced blocks when the applied load is removed. The bending moment of a vessel changes actually in terms of loss of longitudinal members and the change of weight distribution in repair procedure. The change of bending moment affects mainly in hull stress of longitudinal members. Hull stress monitoring system was installed on upper deck to prove LNGC stable in the criteria to be less than 40MPa during the period of repair procedure. A temperature measuring system was also installed to exclude the additional stress due to thermal effect from the measured hull stress. As a result, the hull stress was modified with the data measured by the temperature measuring system. This hull stress considering thermal effect was used as a guide stress to check the safety of LNGC during the period of repair procedure.