Dry sliding wear behavior of electro-pressure sintered Co-Fe, Co-Ni and Co-Fe-Ni compacts was investigated. Pin-on-disk wear tests were performed on the sintered compacts disk specimens against alumina and silica ball counterparts at various loads ranging from 3N to 12N. Two sliding speeds of 0.1m/sec and 0.2m/sec and a fixed sliding distance of 1,000m were employed. Worn surfaces and cross sections of them were examined by a scanning electron microscopy, and wear mechanism of the compacts was investigated. Effects of the oxide layer that was formed on wearing surface of the compacts on the wear were also studied.

Effect of phase transformation and grain-size variation of hot-pressed cobalt on its dry sliding wear was investigated. The sliding wear test was carried out against glass (83% SiO2) beads at 100N load using a pin-on-disk wear tester. Worn surfaces, cross sections, and wear debris were examined by an SEM. Phases of the specimen and wear debris were identified by an XRD. Thermal transformation of the cobalt from the hcp ε phase to the γ (fcc) phase during the wear was detected, which was deduced as the wear mechanism of the sintered cobalt.