Hexagonal barium ferrite () nano-particles have been successfully fabricated by spraypylorysis process. precursor solutions were synthesized by self-assembly method. Diethyleneamine (DEA) surfactant was used to fabricate the micelle structure of Ba-DEA complex under various DEA concentrations. powders were synthesized with addition of Fe ions to Ba-DEA complex and then fabricated powders by spray-pyrolysis process at the temperature range of . The molar ratio of Ba/DEA and heat-treatment temperatures significantly affected the magnetic properties and morphology of powders. powders synthesized with Ba/DEA molar ratio of 1 and heat-treated at showed the coercive forces (iHc) of 4.2 kOe with average crystal size of about 100 nm.

Green-emitting Ba1.468Sr0.5SiO4 : Eu0.012, Y0.02 phosphor powders under long-wavelength ultraviolet light were prepared via high-temperature flame spray pyrolysis from spray solutions with and without NH4Cl flux. The effects of the temperature of the diffusion flame and the NH4Cl flux on the morphologies, crystal structures and photoluminescence intensities of the Ba1.468Sr0.5SiO4 : Eu0.012, Y0.02 phosphor powders were investigated. The phosphor powders obtained from the spray solution with the NH4Cl flux had higher photoluminescence intensities compared to phosphor powders obtained from the spray solution without the flux. The photoluminescence intensity of the phosphor powders obtained from the spray solution without the flux decreased as the flow rate of the fuel gas increased. On the other hand, the photoluminescence intensity of the phosphor powders obtained from the spray solution with the flux increased as the flow rate of the fuel gas increased. The difference of in the phase purity and morphology of the powders affected the photoluminescence intensities of the phosphor powders.

표면 개질한 다공성 금속 지지체에 초음파 분무 열분해법을 이용하여 silica막을 합성하고, 고온 기체 선택 투과 분리 특성을 조사하였다. Tetraethyl orthosilicate (TEOS)를 전구체로 하여 지지체 세공을 통한 감압 진공을 하면서 873K에서 표면에 defect 없이 균일한 양질의 silica막이 형성되었다. 투과 온도 523 K에서 silica막의 수th/질소 및 수증기/메탄을 분리 계수가 각각 17 및 16 정도의 우수한 선택 투과 성능을 나타냈다. 다공성 금속 지지체의 불균일한 기공에 silica 분체 및 γ-alumina층을 중간층으로 도입하고, 그 위에 열분해법에 의한 silica를 합성한 결과, Knudsen 확산에 의한 투과 영역의 세공이 완전히 제거되어 높은 수소 및 수증기 선택성을 가지는 복합 막이 형성되었다.

초음파 분무 열분해법에 의해 합성된 Pb(Zr, Ti)O3미분말의 원료염의 종류에 따른 상과 모양의 변화에 대해 조사했다. 질산염, 초산염, 알콕사이드등의 조합으로 만들어진 원료용액으로부터 합성된 미분말은 약간의 PbTiO3를 포함하거나 포함하지 않는 Pb(Zr, Ti)O3, 상을 나타내었다. 구형 이차입자의 표면에서 발견되는 표면 기공은 질산염의 함량증가에 따라 증가되며, 그 생성은 질산염의 열분해 특성에 기인되는 것으로 해석된다. 본 연구에서 초음파 분무 열분해법으로 합성된 미분말의상, 모양등의 분말특성을 고려할 때, Pb의 원료로서는 acetate, Zr의 원료로서는 oxyacetate, Ti의 원료로서는 oxynitrate 혹은 (iso-propoxide +acetylacetonate)가 적합한 것으로 판단된다.