The purpose of this study is to understand a compressive strength and propose a dry shrinkage strain equation being able to predict dry shrinkage of alkali-activated materials(AAM) mortar samples manufactured using fly-ash(FA) and ground granulated blast furnace slag(GGBFS). The main parameters investigated were the GGBFS replace ratios(30, 50, 70 and 100%) and sodium silicate modules(Ms[SiO2/Na2O] 1.0, 1.5 and 2.0). The compressive strength of AAM increased with increases GGBFS replace ratios or Ms contents. The dry shrinkage strain of AAM decreased with increases Ms contents. But, the dry shrinkage strain of AAM increased as the GGBFS replace ratio increases. Therefore, the GGBFS replace ratio seems to have very significant and important consequences for the mix design of the AAM mortar. The results indicated the R-square of single regression analysis based on each mix properties was the highest value; 0.7539~0.9786(average 0.9359). And the presumption equation of dry shrinkage strain with all variables(GGBFS, Ms and material age) has higher accuracy and its R-square was 0.8020 at initial curing temperature 23 degrees Celsius and 0.8018 at initial curuing temperature 70 degrees Celsius.

이 연구의 목적은 개착식 전력구 콘크리트에 발생하는 부등건조수축에 의한 균열특성을 파악하고, 그 제어방법을 제시하는데 있 다. 건조수축균열은 콘크리트 내부의 수분확산계수의 영향을 크게 받으며, 수분확산계수는 콘크리트 내부에서의 수분이동속도를 결정하는 주요인자이다. 수분확산계수와 더불어 콘크리트 표면의 표면계수와 외부의 상대습도는 콘크리트 내부에서 외부로의 수분이동에 영향을 미친 다. 따라서 이 연구에서는 전력구 박스형 콘크리트 구조물의 부등건조수축에 의한 균열특성을 파악하기 위하여 세 가지 주요영향인자를 고려 한 수치해석을 수행하였다. 수치해석 결과, 수분확산계수와 표면계수가 증가할수록 상부슬래브의 부등건조수축에 의한 균열발생시점이 빨라 지며, 세 가지 요인 중에 콘크리트의 부등건조수축에 의한 균열발생 특성에 가장 큰 영향을 미치는 것은 외기습도인 것으로 나타났다. 이 연구 결과를 분석한 결과, 개착식 전력구 시공시에 콘크리트 타설 후 표면보습이나 살수양생과 같이 외기습도를 증가시키는 것이 부등건조수축에 의한 균열제어에 가장 효과적인 것으로 판단되며, 콘크리트 재료적 측면의 균열저감방법으로 수분확산계수와 표면계수를 결정하는 콘크리트 의 배합이나 재료특성을 적절히 선정함으로써 균열의 진전속도나 발생시점을 제어할 수 있을 것으로 판단된다.

The purpose of this study was to evaluate the shrinkage of ternary blended concrete based on low-heat cement for reducing the heat of hydration. The main parameters were water-to-binder ratio and curing temperature(5, 20, 40℃). Test results showed that the shrinkage significantly was influenced by water-to-binder ratio than binder type. The shrinkage strain of all of the mixtures was increased with increasing the curing temperature.

본 연구는 MgO를 0~16% 사용한 알칼리 활성화 슬래그 시멘트 (AASC)의 강도와 건조수축 특성에 관안 연구이다. 고로슬래그 미분말 (GGBFS)는 KOH를 활성화제로 사용하였고, 활성화제의 농도는 2M과 4M이다. MgO는 GGBFS의 중량에 대해 치환하였고 물-결합재 비 (w/b)는 0.5이다. 실험결과, 높은 MgO 치환율은 높은 수화반응으로 모든 재령에서 높은 압축강도를 나타내었다. 압축강도와 초음파속도 (UPV)는 MgO의 양이 증가함에 따라 증가되었다. AASC의 건조수축은 MgO의 양이 증가함에 따라 감소하였다. SEM 결과를 통해 높은 양의 MgO 시험체는 치밀한 반응 생성물질이 만들어 진 것을 확인할 수 있다.

Autogenous shrinkage isn't currently defined in Korean Highway Bridge Specifications. Accordingly, the structural analysis was carried out to reflect the contents on the autogenous shrinkage of the Eurocode(fib Bulletin 55 : Model code 2010). As a result, we examined the possible initial crack caused by the autogenous shrinkage.

This experimental study investigates the influence on the tensile behavior of strain-hardening cement composite (SHCC) with HR and SWP Shrinkage Reducing Admixture (SRA). SRA can also improve the tensile strength and multiple cracks of SHCC material used in this study.

This experimental study investigates the influence on the flexural behavior of strain-hardening cement composite (SHCC) with HR and SWP Shrinkage Reducing Admixture (SRA). SRA can also improve flexural strengths and flexural toughness.

Recently, field applications and researches for concrete using by-products, fly-ash, GGBS, etc, have been conducted. In case of GGBS, however, quality control and replacement amount is limited because of some disadvantages. In this study, high early strength concrete using GGBS was evaluated applicability for concrete structural material. In order to evaluate, compressive strength and shrinkage test were conducted.

This experimental study examines the test results on the flexural behavior of strain-hardening cement composite (SHCC) with two types of Shrinkage Reducing Admixture (SRA). An influence of SRA on the flexural behaviors of SHCC mixes was observed.

In this study, it evaluates autogenous Shrinkage of high strength concrete with polymix fiber and type of aggregate. Consequently, When concrete is mixed with limestone aggregate and spalling prevention fiber, Compressive strength, modulus of elasticity and autogenous shrinkage was better.

콘크리트는 초기재령에 있어서 수분의 증발 및 이동으로 소성 및 건조수축 등의 수축현상이 발생한다. 국내에서는 아령형 구속건조수축몰드를 활용한 콘크리트의 건조수축 균열 평가방법을 KS에서 규격화하여 활용하고 있으나 이는 균열발생시점 및 구속수축응력을 평가하는 방법으로 균열발생량에 관한 정량적 평가는 어려운 실정이다. 이에 본 연구에서는 콘크리트의 수축변형거동 및 균열발생량에 대한 정량적 데이터를 확보하기 위하여 판상-링형 구속시험방법을 개발하고 시험체 치수가 콘크리트의 수축균열에 미치는 영향을 검토하여 판상-링형 구속시험방법의 최적 시험체 치수 도출 및 수축균열특성에 관한 정량적 평가방법을 제안하고 그 적용성을 검증하고자 한다.

본 연구는 대형․대단면 지하공간에 적용하기 위한 고강도 콘크리트의 개발 및 적용을 위한 연구의 일환으로 50MPa급의 고강도 콘크리트의 제조를 위해 플라이애쉬와 고로슬래그미분말의 치환에 따른 최적 배합을 선정하고, 비구속 수축 실험과 수축균열 실험을 통해 정량적으로 평가하였다. 콘크리트의 압축강도는 전 배합이 7일 재령에서 30MPa을 넘었고, 28일 재령에서는 설계강도를 모두 안정적으로 획득하였다. 고강도 콘크리트에 고로슬래그를 사용할 경우 자기수축량이 커지고, 다량 치환할 경우 수축변형이 증가하고 강도발현이 지연되어 수축에 의한 균열 발생의 우려가 있다. 혼화재를 다량 치환한 고강도 콘크리트 배합은 수화반응과 건조 효과에 영향을 주는 초기 재령의 양생 조건에 대한 검토가 필요하다.

본 연구는 개발된 저수축 고성능 콘크리트를 대상으로 모의부재 시험체에 있어서 콘크리트의 기초적 물성과 수축특성에 대하여 검토한 것이다. 실험연구 결과, 콘크리트의 배합특성으로 제안 배합은 목표 슬럼프플로우 및 목표 공기량을 만족하기 위해 SP제량 증가, AE제량 감소의 배합보정이 필요하였다. 응결시간은 제안 배합이 8시간 정도 빠르게 나타났으며, 굳은 콘크리트의 압축강도는 60MPa 이상의 고강도로 나타냈다. 수축특성으로 제안 배합 자기수축의 경우 플레인 배합 자기수축에 비해 50% 정도 저감되었고, 제안 배합의 중심부 건조수축은 수분발산이 없는 것에 기인하여 자기수축과 유사한 경향이었으나, 표면부는 크게 수축하였다. 단, 철근배근 시험체인 경우는 철근구속에 의해 내부 및 표면의 수축량이 작게 나타났다.