In this study, the effects of Co content on the microstructure and Charpy impact properties of Fe-Cr-W ferritic/martensitic oxide dispersion strengthened (F/M ODS) steels are investigated. F/M ODS steels with 0–5 wt% Co are fabricated by mechanical alloying, followed by hot isostatic pressing, hot-rolling, and normalizing/tempering heat treatment. All the steels commonly exhibit two-phase microstructures consisting of ferrite and tempered martensite. The volume fraction of ferrite increases with the increase in the Co content, since the Co element considerably lowers the hardenability of the F/M ODS steel. Despite the lowest volume fraction of tempered martensite, the F/M ODS steel with 5 wt% Co shows the highest micro-Vickers hardness, owing to the solid solution-hardening effect of the alloyed Co. The high hardness of the steel improves the resistance to fracture initiation, thereby resulting in the enhanced fracture initiation energy in a Charpy impact test at – 40oC. Furthermore, the addition of Co suppresses the formation of coarse oxide inclusions in the F/M ODS steel, while simultaneously providing a high resistance to fracture propagation. Owing to these combined effects of Co, the Charpy impact energy of the F/M ODS steel increases gradually with the increase in the Co content.

This research is conducted to analyze the compatibility of used monomers and produce the high functional hydrogel ophthalmic polymer containing silane and nanoparticles. VTMS (vinyltrimethoxysilane), TAVS [Triacetoxy(vinyl)silane] and cobalt oxide nanoparticles are used as additives for the basic combination of SilM (silicone monomer), MMA (methyl methacrylate) and MA (methyl acrylate). Also, the materials are copolymerized with EGDMA (ethylene glycol dimethacrylate) as cross-linking agent, AIBN (thermal polymerization initiator) as the initiator. It is judged that the lenses of all combinations are optically excellent and thus have good compatibility. Measurement of the optical and physical characteristics of the manufactured hydrophilic ophthalmic polymer are different in each case. Especially for TAVS, the addition of cobalt oxide nanoparticles increases the oxygen permeability. These materials are considered to create synergy, so they can be used in functional hydrogel ophthalmic lenses.

To meet the current demand in the fields of permanent magnets for achieving a high energy density, it is imperative to prepare nano-to-microscale rare-earth-based magnets with well-defined microstructures, controlled homogeneity, and magnetic characteristics via a bottom-up approach. Here, on the basis of a microstructural study and qualitative magnetic measurements, optimized reduction conditions for the preparation of nanostructured Sm-Co magnets are proposed, and the elucidation of the reduction-diffusion behavior in the binary phase system is clearly manifested. In addition, we have investigated the microstructural, crystallographic, and magnetic properties of the Sm-Co magnets prepared under different reduction conditions, that is, H2 gas, calcium, and calcium hydride. This work provides a potential approach to prepare high-quality Sm-Co-based nanofibers, and moreover, it can be extended to the experimental design of other magnetic alloys.

Cobalt tetraphenylporphyrin-benzylimidazole (CoTpp-BIm)을 산소 운반체로 이용하여 polyethersulfone (PES)와의 혼합물을 기반으로 하는 혼합 구조의 평판형 분리막의 기체 분리 성능을 조사하였다. CoTpp-BIm이 혼합된 PES막은 손가락 구조와 스폰지형 구조가 혼합된 비대칭 구조를 가졌고, 상부표면은 치밀한 형태를 보였다. 기체분리 성능 실험은 94%의 N2 기체에 6%의 O2가 혼합된 기체를 사용하여 평가하였다. 산소 및 질소 투과율은 △P가 15~228 cmHg 범위에서 실험하였고, PES막의 투과면은 진공수준으로 유지되었다. CoTpp-BIm이 혼합된 PES막의 산소 투과율은 공급 압력이 감소함에 따라 증가 하였다. 공급 압력이 15 cmHg일 때 산소 투과율(Po2)는 6676 Barrer이었고, O2/N2 선택도(α)는 6.1, 촉진인자(F)는 2.39까지 증가하였다. 이를 바탕으로 PES막에 CoTpp-BIm을 첨가하면 산소분리 특성이 향상되는 것을 확인하였다.

The manganese-, nickel-, and aluminum-doped cobalt ferrite powders, Mn0.2Co0.8Fe2O4, Ni0.2Co0.8Fe2O4, and Al0.2CoFe1.8O4, are fabricated by the sol-gel method, and the crystallographic and magnetic properties of the powders are studied in comparison with those of CoFe2O4. All the ferrite powders are nano-sized and have a single spinel structure with the lattice constant increasing in Mn0.2Co0.8Fe2O4 but decreasing in Ni0.2Co0.8Fe2O4 and Al0.2CoFe1.8O4. All the Mössbauer spectra are fitted as a superposition of two Zeeman sextets due to the tetrahedral and octahedral sites of the Fe3+ ions. The values of the magnetic hyperfine fields of Ni0.2Co0.8Fe2O4 are somewhat increased in the A and B sites, while those of Mn0.2Co0.8Fe2O4 and Al0.2CoFe1.8O4 are decreased. The variation of Mössbauer parameters is explained using the cation distribution equation, superexchange interaction and particle size. The hysteresis curves of the ferrite powders reveal a typical soft ferrite pattern. The variation in the values of saturation magnetization and coercivity are explained in terms of the site distributions, particle sizes and the spin magnetic moments of the doped ions.

오염수로부터 자성분리가 가능하며, 방사성 세슘을 효율적으로 제거하기 위한 코발트 페로시아나이드(cobalt ferrocyanide, CoFC) 혹은 니켈 페로시아나이드(nickel ferrocyanide, NiFC)가 도입된 자성입자 흡착제를 제조하였다. Fe3O4 나노 입자는 공침법을 이용해 제조하였고, Co2+와 Ni2+ 이온을 입자 표면에 도입시키기 위해 금속이온과 금속 배위결합(metalcoordination) 을 하는 카르복실기를 포함한 숙신산(succinic acid, SA)을 자성나노입자(magnetic nanoparticles, MNPs) 표 면에 코팅하였다. CoFC와 NiFC는 자성나노입자 표면에 도입된 Co2+ 혹은 Ni2+ 이온이 hexacynoferrate와 결합하여 형성된 다. 제조된 CoFC-MNPs 그리고 NiFC-MNPs는 각각 43.2 emu·g-1, 47.7 emu·g-1의 우수한 포화자화 값을 보여주었다. X- 선 회절분석(XRD), 퓨리에 변환 적외선 분광분석(FT-IR), 나노입자 입도 분석기(DLS), 투과전자현미경(TEM) 등의 분석을 통해 흡착제의 물성을 파악하고, 세슘에 대한 흡착 성능을 알아보았다. 흡착실험을 평가하기 위해 Langmuir/Freundlich 등 온흡착식을 이용해 실험 결과 값을 곡선맞춤 하였고, CoFC-MNPs와 NiFC-MNPs의 최대흡착량(qm)은 각각 15.63 mg·g-1, 12.11 mg·g-1이다. CoFC-MNPs와 NiFC-MNPs는 방사성 세슘에 대해서도 최저 99.09%의 제거율을 가지며, 경쟁이온의 존재에도 방사성 세슘만을 선택적으로 흡착한다.

Cobalt was electrodeposited onto chemical vapor deposition (CVD) graphene/Si/SiO2 substrates, during different time intervals, using an electrolyte solution containing a low concentration of cobalt sulfate. The intention was to investigate the details of the deposition process (and the dissolution process) and the resulting magnetic properties of the Co deposits on graphene. During and after electrodeposition, in-situ magnetic measurements were performed using an (AGFM). These were followed by ex situ morphological analysis of the samples with ΔtDEP 30 and 100 s by atomic force microscopy in the non-contact mode on pristine CVD graphene/SiO2/Si. We demonstrate that it is possible to electrodeposit Co onto graphene, and that in-situ magnetic measurements can also help in understanding details of the deposition process itself. The results show that the Co deposits are ferromagnetic with decreasing coercivity (HC) and demonstrate increasing magnetization on saturation (MSAT) and electric signal proportional to remanence (Mr), as a function of the amount of the electrodeposited Co. It was also found that, after the end of the dissolution process, a certain amount of cobalt remains on the graphene in oxide form (this was confirmed by X-ray photoelectron spectroscopy), as suggested by the magnetic measurements. This oxide tends to exhibit a limited asymptotic amount when cycling through the deposition/dissolution process for increasing deposition times, possibly indicating that the oxidation process is similar to the graphene surface chemistry.

In order to identify changes in the nature of the particles due to changes in the inflow rate of the raw material solution, the present study was intended to prepare nano-sized cobalt oxide (Co3O4) powder with an average particle size of 50 nm or less by spray pyrolysis reaction using raw cobalt chloride solution. As the inflow rate of the raw material solution increased, droplets formed by the pyrolysis reaction showed more divided form and the particle size distribution was more uneven. As the inflow rate of the solution increased from 2 to 10 ml/min, the average particle size of the formed particles increased from about 25 nm to 40 nm, while the average particle size did not show significant changes when the inflow rate increased from 10 to 50 ml/min. XRD analysis showed that the intensity of the XRD peaks increased remarkably when the inflow rate of the solution increased from 2 to 10 ml/min. On the other hand, the peak intensity stayed almost constant when the inflow rate increased from 10 to 50 ml/min. With the increase in the inflow rate from 2 to 10 ml/min, the specific surface area of the particles decreased by approximately 20 %. On the contrary, the specific surface area stayed constant when the inflow rate increased from 10 to 50 ml/min.

The cobalt silicides were investigated for employment as a catalytic layer for a DSSC. Using an E-gun evaporation process, we prepared a sample of 100 nm-thick cobalt on a p-type Si (100) wafer. To form cobalt silicides, the samples were annealed at temperatures of 300 oC, 500 oC, and 700 oC for 30 minutes in a vacuum. Four-point probe, XRD, FE-SEM, and CV analyses were used to determine the sheet resistance, phase, microstructure, and catalytic activity of the cobalt silicides. To confirm the corrosion stability, we also checked the microstructure change of the cobalt silicides after dipping into iodide electrolyte. Through the sheet resistance and XRD results, we determined that Co2Si, CoSi, and CoSi2 were formed successfully by annealing at 300 oC, 500 oC, and 700 oC, respectively. The microstructure analysis results showed that all the cobalt silicides were formed uniformly, and CoSi and CoSi2 layers were very stable even after dipping in the iodide electrolyte. The CV result showed that CoSi and CoSi2 exhibit catalytic activities 67 % and 54 % that of Pt. Our results for Co2Si, CoSi, and CoSi2 revealed that CoSi and CoSi2 could be employed as catalyst for a DSSC.

전 세계적으로 원자력 발전소는 442기가 가동 중이며, 62기가 충원될 예정이다. 원자력 발전소의 증가에 따라 방사성 폐기물 유출에 대한 위험성도 증가하였다. 이러한 이유 때문 에, 방사성 폐기물의 처리는 인간, 동물, 식물을 포함하는 자 연 생태계를 보전하는 관점에서 중요하다. 또한, 방사성 폐 기물 유출은 그 지역뿐만 아니라 전 세계적으로 심각한 문 제를 야기한다. 본 연구는 입체 배양세포에 방사성 핵종원 소 (세슘, 스트론튬, 코발트)를 처리하였고 이에 대한 영향력 을 확인하였다. 입체 배양 구조체는 아가로오스 하이드로겔 을 이용하여 제작했으며 암세포 및 정상세포 (HeLa, HepG2, COS-7)를 사용하여 입체 배양을 실시 하였다. 입체 형태로 세포를 배양한 후 세슘, 스트론튬, 코발트 농도 변화에 따라 세포 생존능력을 분석하였다. 이때 입체 배양세포에서 생존 능력이 단층 배양세포 보다 최대 42% 우수한 것을 확인하였 다. 입체 배양구조체는 세포가 형태 및 생리학적으로 in vivo 환경인 조직과 비슷하게 배양을 가능하게 하였다. 따라서, 입체 배양구조체는 기존의 단층 배양 한계점인 in vivo 환경 에 적용시킬 수 없다는 한계를 극복하였다. 본 입체 배양 기 술이 중금속 독성평가 및 단시간 내에 다수의 물질 분석을 수행하는 고속 대량 스크리닝 기술에 활용될 것으로 기대한 다.

Perforated polygonal cobalt oxide (Co3O4) is synthesized using electrospinning and a hydrothermal methodfollowed by the removal of a carbon nanofiber (CNF) template. To investigate their formation mechanism, thermogravi-metric analysis, field-emission scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy are examined. To obtain the optimum condition of perforated polygonal Co3O4, we pre-pare three different weight ratios of the Co precursor and the CNF template: sample A (Co precursor:CNF template-10:1), sample B (Co precursor:CNF template-3.2:1), and sample C (Co precursor:CNF template-2:1). Among them, sam-ple A exhibits the perforated polygonal Co3O4 with a thin carbon layer (5.7-6.2 nm) owing to the removal of CNF tem-plate. However, sample B and sample C synthesized perforated round Co3O4 and destroyed Co3O4 powders, respectively,due to a decreased amount of Co precursor. The increased amount of the CNF template prevents the formation of polygonalCo3O4. For sample A, the optimized weight ratio of the Co precursor and CNF template may be related to the suc-cessful formation of perforated polygonal Co3O4. Thus, perforated polygonal Co3O4 can be applied to electrode materialsof energy storage devices such as lithium ion batteries, supercapacitors, and fuel cells.

Spherical fine cobalt powders were fabricated by new liquid reduction method. Commercial cobalt sufate heptahydrate was used as raw material. Also ethylene glycol was used as solvent and hydrazine-sodium hypophosphite mixture was used as reduction agent for the new liquid reduction method. A plate shaped cobalt powders with an approximately 300 nm were prepared by a traditional wet ruduction method using distilled water as solvent and hydrazine. Spherical fine cobalt powders with an average size of 1-3 μm were synthesized by a new liquid reduction method in 0.3M cobalt sulfate and 1.5M hydrazine-0.6M sodium hypophosphite mixture at 333K.

In this study, cobalt nanopowder is fabricated by sonochemical polyol synthesis and magnetic separation method. First, sonochemical polyol synthesis is carried out at 220oC for up to 120 minutes in diethylene glycol (C4H10O3). As a result, when sonochemical polyol synthesis is performed for 50 minutes, most of the cobalt precursor (Co(OH)2) is reduced to spherical cobalt nanopowder of approximately 100 nm. In particular, aggregation and growth of cobalt particles are effectively suppressed as compared to common polyol synthesis. Furthermore, in order to obtain finer cobalt nanopowder, magnetic separation method using magnetic property of cobalt is introduced at an early reduction stage of sonochemical polyol synthesis when cobalt and cobalt precursor coexist. Finally, spherical cobalt nanopowder having an average particle size of 22 nm is successfully separated.