Multiwall carbon nanotubes (MWCNT) with two different (L/D) aspect ratios (7±2 μm/140±30 nm and 0.5–2 μm/8–15 nm) were surface treated using nitric acid (HNO3) and polyethyleneimine (PEI) prior to their deposition on carbon fibers (CF). Before the hierarchical reinforcement with CF-MWCNT, the CFs were treated with 3-glycidoxypropyltrimethoxysilane, a coupling agent (Z6040) and with poly(amidoamine) (PAMAM) a dendrimer containing an ethylenediamine core and amine surface groups. The MWCNT were deposited on the CF using two methods, by electrostatic attraction and by chemical reactions. The changes in the CF surface morphology after the MWCNT deposition were analyzed using SEM, which revealed a higher density and uniform coverage for the PAMAM-treated CF and the short MWCNTs. The interfacial adhesion of the composite materials was evaluated using the single fiber fragmentation technique. The results indicated an improvement in the interfacial shear strength with the addition of the short-MWCNTs treated with acid solutions and grafted onto the surface of the CF fiber using electrostatic attraction.

증류에 의한 올레핀/파라핀 분리는 끓는점이 유사하여 에너지 소모가 높기 때문에, 분리막을 이용한 연구가 많이 진행 중이다. 특히 CMS 분리막은 sieving separation에 의한 투과/분리 성능이 우수하다. 따라서 본 연구에서는 중공사형 α-alumina 지지체에 γ-alumina 중간층을 형성한 후 Matrimid로 코팅하여 열분해함으로써 높은 기계적 강도와 충진 밀도를 갖는 중공사형 CMS 복합막을 제조하였다. 제조된 CMS 분리막은 20 - 35 GPU 프로필렌 투과도와 10 이상의 프로필렌/프로판 분리도를 보였다. 이 연구는 2014년 정부(미래창조과학부)의 재원으로 국가과학 기술연구회 융합연구단 사업(No. CRC-14-01-KRICT)의 지원을 받아 수행된 연구입니다.

The aim of the work was to investigate the thermo-electrical properties of low cost and rapidly produced randomly oriented carbon/carbon (C/C) composite. The composite body was fabricated by combining the high-pressure hot-pressing (HP) method with the lowpressure impregnation thermosetting carbonization (ITC) method. After the ITC method step selected samples were graphitized at 3000°C. Detailed characterization of the samples’ physical properties and thermal properties, including thermal diffusivity, thermal conductivity, specific heat and coefficient of thermal expansion, was carried out. Additionally, direct current (DC) electrical conductivity in both the in-plane and through-plane directions was evaluated. The results indicated that after graphitization the specimens had excellent carbon purity (99.9 %) as compared to that after carbonization (98.1). The results further showed an increasing trend in thermal conductivity with temperature for the carbonized samples and a decreasing trend in thermal conductivity with temperature for graphitized samples. The influence of the thickness of the test specimen on the thermal conductivity was found to be negligible. Further, all of the specimens after graphitization displayed an enormous increase in electrical conductivity (from 190 to 565 and 595 to 1180 S/cm in the through-plane and in-plane directions, respectively).

Heavy metals are typical contaminant in water and need to be removed because they are non-biodegradable and can accumulate in human body. To remove metal and other contaminants from water, chemical absorbents are widely used due to their low cost. Herein, hybrid materials comprised of amylose and single wall carbon-nanotube (swCNT) was developed as the absorbent for water purification. A high adsorption properties of carbon-nanotubes have been utilized in designing effective absorbent but its poor dispersity in water is a limiting factor for practical use. Single wall carbon-nanotube was hybridized with amylose chain produced by enzyme reaction of amylosucrase and their tendency to self-assemble in aqueous environment. The amylose-swCNT microparticles were characterized by FE-SEM and turned out to be spherical structure with CNTs embedded throughout the amylose matrix. The ability of amylose-CNT microparticles to remove copper was examined. Concentration of copper was decreased after reaction with amylose-swCNT microparticles. Although amount of decreasing copper was less than swCNT on same total mass, Adsorption efficiency of amylose-swCNT microparticles was good because their swCNT content was only 10% of total mass.

Isroaniso matrix precursor synthesized from commercially available petroleum pitch was stabilized in air. The influence of oxygen mass gain during stabilization on the yield of matrix precursor was studied. Additionally, the influence of pressure on the yield of the stabilized matrix precursor in a real system was studied. The fourier transform infrared spectrometry (FTIR), thermogravimetric analysis (TGA), yield, yield rate, and yield impact were used to check the effect of stabilization and pressure on the yield of the matrix precursor and the end properties of the composite thereafter. The results showed that the yield increased with stabilization duration up to 20 h whereas it decreased for stabilization duration beyond 20 h. Further results showed that the stabilized matrix precursor for a duration of 5 h could withstand almost two-fold greater hot-pressing pressure without resulting in exudation as compared to that of a 1 h stabilized matrix precursor. The enhanced hot-pressing pressure significantly improved the yield of the matrix precursor. As a consequence, the densification and mechanical properties were increased significantly. Further, the matrix precursor stabilized for a duration of 20 h or more failed to provide proper and uniform binding of the reinforcement.

본 연구에서는 유연성을 갖는 전극 제조를 위해 환원된 그래핀 옥사이드/단일벽 탄소나노튜 브 복합체를 금이 코팅된 PET 기판 위에 스프레이 코팅하였다. 제조된 플렉시블한 전극의 전기 용량 값 은 1 M의 황산 전해질과 100 mV s-1 의 주사속도에서 82 F g-1 으로 측정 되었으며, 이 용량 값은 500 번의 굽힘 시험 후에 38 F g-1 로 감소되는 현상을 확인 하였다. 또한, 이러한 결과는 정전류 충 방전과 전기화학 임피던스법을 포함한 전기화학적 분석 결과와도 부합하는 결과를 나타내었다. 유연성을 갖는 환원된 그래핀 옥사이드/단일벽 탄소나노튜브 복합체 전극은 500회의 반복적인 굽힘 시험 후에도 대략 50%의 초기 전기 용량 값을 유지 할 수 있었으며, 이러한 여러 가지 전기화학적 특성을 고려하여 볼 때 미래 개발 가능한 플렉시블한 에너지 저장 매체로써의 적용이 가능 하다는 점을 확인 할 수 있었 다.

Fabrication of iron oxide/carbon nanotube composite structures for detection of ammonia gas at room temperature is reported. The iron oxide/carbon nanotube composite structures are fabricated by in situ co-arc-discharge method using a graphite source with varying numbers of iron wires inserted. The composite structures reveal higher response signals at room temperature than at high temperatures. As the number of iron wires inserted increased, the volume of carbon nanotubes and iron nanoparticles produced increased. The oxidation condition of the composite structures varied the carbon nanotube/iron oxide ratio in the structure and, consequently, the resistance of the structures and, finally, the ammonia gas sensing performance. The highest sensor performance was realized with 500 oC/2 h oxidation heat-treatment condition, in which most of the carbon nanotubes were removed from the composite and iron oxide played the main role of ammonia sensing. The response signal level was 62% at room temperature. We also found that UV irradiation enhances the sensing response with reduced recovery time.

This study fabricated low thermal conductive polyacrylonitrile (PAN)-based carbon fibers containing cellulose particles while maintaining their mechanical properties. The high thermal conductivity of carbon fibers limits their application as a high temperature insulator in various systems such as an insulator for propulsion parts in aerospace or missile systems. By controlling process parameters such as the heat treatment temperature of the cellulose particles and the amount of cellulose added, the thermal and mechanical properties of the PANbased carbon fibers were investigated. The results show that it is possible to manufacture composite carbon fibers with low thermal conductivity. That is, thermal conductivities were reduced by the cellulose particles in the PAN based carbon fibers while at the same time, the tensile strength loss was minimized, and the tensile modulus increased.

Impact damages induced by a low-velocity impact load on carbon fiber reinforced polymer (CFRP) composite plates fabricated with various stacking sequences were studied experimentally. The impact responses of the CFRP composite plates were significantly affected by the laminate stacking sequences. Three types of specimens, specifically quasi-isotropic, unidirectional, and cross-ply, were tested by a constant impact carrying the same impact energy level. An impact load of 3.44 kg, corresponding to 23.62 J, was applied to the center of each plate supported at the boundaries. The unidirectional composite plate showed the worst impact resistance and broke completely into two parts; this was followed by the quasi-isotropic lay-up plate that was perforated by the impact. The cross-ply composite plate exhibited the best resistance to the low-velocity impact load; in this case, the impactor bounced back. Impact parameters such as the peak impact force and absorbed energy were evaluated and compared for the impact resistant characterization of the composites made by different stacking sequences.

Single-walled carbon nanotubes (SWNTs) was modified with various length of linear alkyl chains and passivated to form dielectric filler. The modified SWNTs embedded into epoxy matrix to fabricate a flexible composite with high dielectric constant. The dielectric behavior of the composite was significantly changed with various alkyl chain length(n) of pyrene. The dielectric constant of the epoxy/SWNTs composite significantly increased with respect to increase in length of alkyl chain at the frequency range from 10 to 105 Hz (n=12and18). We also found that the passivated epoxy/SWNTs composite with high dielectric constant presented low dielectric loss. The resulted dielectric performances corresponded to de-bundling of nanotubes and their distribution behavior in the matrix in terms of tail length of alkyl pyrene in the passivation layer.

The composite of porous silicon (Si) and amorphous carbon (C) is prepared by pyrolysis of a nano-porous Si + pitch mixture. The nano-porous Si is prepared by mechanical milling of magnesium powder with silicon monoxide (SiO) followed by removal of MgO with hydrochloric acid (etching process). The Brunauer-Emmett-Teller (BET) surface area of porous Si (64.52 m2g−1) is much higher than that before etching Si/MgO (4.28 m2g−1) which indicates pores are formed in Si after the etching process. Cycling stability is examined for the nano-porous Si + C composite and the result is compared with the composite of nonporous Si + C. The capacity retention of the former composite is 59.6% after 50 charge/discharge cycles while the latter shows only 28.0%. The pores of Si formed after the etching process is believed to accommodate large volumetric change of Si during charging and discharging process.

The prime objective of this research was to study the influence of hot-pressing pressure and matrix-to-reinforcement ratio on the densification of short-carbon-fiber-reinforced, randomly oriented carbon/carbon-composite. Secondary objectives included determination of the physical and mechanical properties of the resulting composite. The ‘hybrid carbon-fiberreinforced mesophase-pitch-derived carbon-matrix’ composite was fabricated by hot pressing. During hot pressing, pressure was varied from 5 to 20 MPa, and reinforcement wt% from 30 to 70. Densification of all the compacts was carried at low impregnation pressure with phenolic resin. The effect of the impregnation cycles was determined using measurements of microstructure and density. The results showed that effective densification strongly depended on the hot-pressing pressure and reinforcement wt%. Furthermore, results showed that compacts processed at lower hot-pressing pressure, and at higher reinforcement wt%, gained density gradually during three densification cycles and showed the symptoms of further gains with additional densification cycles. In contrast, samples that were hot-pressed at moderate pressure and at moderate reinforcement wt%, achieved maximum density within three densification cycles. Furthermore, examination of microstructure revealed the formation of cracks in samples processed at lower pressure and with low reinforcement wt%.

본 연구에서는, 유기용매를 사용하지 않는 친 환경적인 건식 공정과 초임계 공정을 이용한 Thin-multiwalled carbon nanotube (TWNTs)/아민계 에폭시 첨가제의 복합체 제조에 관하여 연구를 하였다. 제조된 TWNTs/아민계 에폭시 첨가제의 복합체는 우레탄기반의 비스페놀 A 타입의 에폭시 레 진의 경화제로 사용하였다. TWNTs/아민계 에폭시 첨가제의 복합체를 경화제로 사용하여 제조된 에폭 시 레진의 열적 성질을 Dynamic mechanical analysis (DMA)를 이용하여 분석 하였으며, 메트릭스상의 carbon nanotube 의 높은 분산성은 SEM을 통하여 확인 하였다. 그 결과, 초임계 공정을 이용하여 제 조된 에폭시 레진의 열적 성질과 매트릭스내의 carbon nanotube 분산성이 건식 공정을 사용 하였을 때 보다 더욱 증가된 결과를 확인 할 수 있었다

Silicon-carbon composite was prepared by the magnesiothermic reduction of mesoporous silica and subsequent impregnation with a carbon precursor. This was applied for use as an anode material for high-performance lithium-ion batteries. Well-ordered mesoporous silica(SBA-15) was employed as a starting material for the mesoporous silicon, and sucrose was used as a carbon source. It was found that complete removal of by-products (Mg2Si and Mg2SiO4) formed by side reactions of silica and magnesium during the magnesiothermic reduction, was a crucial factor for successful formation of mesoporous silicon. Successful formation of the silicon-carbon composite was well confirmed by appropriate characterization tools (e.g., N2 adsorption-desorption, small-angle X-ray scattering, X-ray diffraction, and thermogravimetric analyses). A lithium-ion battery was fabricated using the prepared silicon-carbon composite as the anode, and lithium foil as the counter-electrode. Electrochemical analysis revealed that the silicon-carbon composite showed better cycling stability than graphite, when used as the anode in the lithium-ion battery. This improvement could be due to the fact that carbon efficiently suppressed the change in volume of the silicon material caused by the charge-discharge cycle. This indicates that silicon-carbon composite, prepared via the magnesiothermic reduction and impregnation methods, could be an efficient anode material for lithium ion batteries.

In this study, carbon fiber reinforced plastic and aluminum foam used in impact absorber are assembled and modelled. These models are investigated by impact simulation and verified by experimental data. Impact energies of 30 J, 60 J and 100 J are applied on these specimens by striker. For example the experiment for impact energy of 30 J is done and verified by referring to analysis result. As the structural safeties of these assembled composite materials can be anticipated through this study result, these simulation analysis results can be applied into real field.

A powder-in-sheath rolling method was applied to a fabrication of a carbon nano tube (CNT) reinforcedaluminum composite. A STS304 tube with an outer diameter of 34 mm and a wall thickness of 2 mm was used as asheath material. A mixture of pure aluminum powders and CNTs with the volume contents of 1, 3, 5 vol was filled inthe tube by tap filling and then processed to 73.5% height reduction by a rolling mill. The relative density of the CNT/Al composite fabricated by the powder-in-sheath rolling decreased slightly with increasing of CNTs content, but exhib-ited high value more than 98. The grain size of the aluminum matrix was largely decreased with addition of CNTs; itdecreased from 24 µm to 0.9 µm by the addition of only 1 volCNT. The average hardness of the composites increasedby approximately 3 times with the addition of CNTs, comparing to that of unreinforced pure aluminum. It is concludedthat the powder-in-sheath rolling method is an effective process for fabrication of CNT reinforced Al matrix composites.